Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14398_dAYhqD.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.55 T-atoms per nm^3
Material density = 2.250 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6231 Angstrom
T1  -- O2  = 1.6185 Angstrom
T1  -- O4  = 1.6212 Angstrom
T1  -- O3  = 1.6227 Angstrom
      mean = 1.6214 Angstrom
        t1 = 0.014832  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008288  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6290 Angstrom
T2  -- O6  = 1.6240 Angstrom
T2  -- O5  = 1.6342 Angstrom
T2  -- O4  = 1.6532 Angstrom
      mean = 1.6351 Angstrom
        t1 = 0.023901  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015748  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6185 A <--> 1.6532 A
          Mean   = 1.6282 A
          StdDev = 0.0106 A

       t1 Range  = 0.0148 <-- 0.0194 --> 0.0239
       t2 Range  = 0.0083 <-- 0.0120 --> 0.0157

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.046 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.226 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 113.379 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.477 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.453 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 106.181 deg; O4  -- O3  = 3 A
       106.181 deg <-- 109.461 deg --> 113.379 deg

O3  -- T2  -- O6  = 108.581 deg; O3  -- O6  = 3 A
O3  -- T2  -- O5  = 107.028 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 108.438 deg; O3  -- O4  = 3 A
O6  -- T2  -- O5  = 108.980 deg; O6  -- O5  = 3 A
O6  -- T2  -- O4  = 108.599 deg; O6  -- O4  = 3 A
O5  -- T2  -- O4  = 115.049 deg; O5  -- O4  = 3 A
       107.028 deg <-- 109.446 deg --> 115.049 deg

        O-T-O SUMMARY
          Range  = 106.1806 deg <--> 115.0494 deg
          Mean   = 109.4931 deg
          StdDev = 2.4792 deg

        O--O SUMMARY
          Range  = 2.5937 A <--> 2.7734 A
          Mean   = 2.6592 A
          StdDev = 0.0458 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 131.348 deg; T1  -- T1  = 5.6875 A
T1  - O1  - T1  - O4  - T2  =  90.170 deg; T1  -- T2  = 4.1322 A
T1  - O1  - T1  - O3  - T2  =  90.169 deg; T1  -- T2  = 4.1506 A
T1  - O2  - T1  - O4  - T2  =  94.222 deg; T1  -- T2  = 4.4669 A
T1  - O2  - T1  - O3  - T2  = 132.985 deg; T1  -- T2  = 5.6066 A
T2  - O4  - T1  - O3  - T2  = 108.603 deg; T2  -- T2  = 4.6324 A

T2  - O3  - T2  - O6  - T2  = 130.615 deg; T2  -- T2  = 5.7065 A
T2  - O3  - T2  - O5  - T1  =  89.831 deg; T2  -- T1  = 4.1506 A
T2  - O3  - T2  - O4  - T1  =  89.830 deg; T2  -- T1  = 4.1322 A
T2  - O6  - T2  - O5  - T1  =  89.973 deg; T2  -- T1  = 4.3457 A
T2  - O6  - T2  - O4  - T1  = 136.230 deg; T2  -- T1  = 5.6693 A
T1  - O5  - T2  - O4  - T1  = 108.603 deg; T1  -- T1  = 4.6324 A

        T-T-T SUMMARY
          Range  = 89.8299 deg <--> 136.2298 deg
          Mean   = 107.4471 deg
          StdDev = 18.9270 deg

        T--T SUMMARY
          Range  = 4.1322 A <--> 5.7065 A
          Mean   = 4.7542 A
          StdDev = 0.6545 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2462 A

T1  -- O2  -- T1  = 135.347 deg ; T1  -- T1   2.9943 A

T1  -- O3  -- T2  = 123.586 deg ; T1  -- T2   2.8655 A

T1  -- O4  -- T2  = 120.210 deg ; T1  -- T2   2.8387 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2685 A

T2  -- O6  -- T2  = 135.969 deg ; T2  -- T2   3.0112 A


        T-O-T SUMMARY
          Range  = 120.2100° <--> 180.0000 deg
          Mean   = 145.8521 deg
          StdDev = 25.3445 deg

        T--T SUMMARY
          Range  = 2.8387 A <--> 3.2685 A
          Mean   = 3.0374 A
          StdDev = 0.1712 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000