Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14373_APY2TE.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 20.61 T-atoms per nm^3
Material density = 2.056 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6301 Angstrom
T1  -- O2  = 1.6301 Angstrom
T1  -- O4  = 1.6102 Angstrom
T1  -- O3  = 1.6153 Angstrom
      mean = 1.6214 Angstrom
        t1 = 0.020904  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018755  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6155 Angstrom
T2  -- O5  = 1.5896 Angstrom
T2  -- O6  = 1.6486 Angstrom
T2  -- O4  = 1.6055 Angstrom
      mean = 1.6148 Angstrom
        t1 = 0.076261  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058841  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5896 A <--> 1.6486 A
          Mean   = 1.6181 A
          StdDev = 0.0171 A

       t1 Range  = 0.0209 <-- 0.0486 --> 0.0763
       t2 Range  = 0.0188 <-- 0.0388 --> 0.0588

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.523 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 113.247 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 106.200 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 105.239 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 110.499 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.160 deg; O4  -- O3  = 3 A
       105.239 deg <-- 109.478 deg --> 113.247 deg

O3  -- T2  -- O5  = 117.435 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 114.618 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  =  99.348 deg; O3  -- O4  = 2 A
O5  -- T2  -- O6  = 119.911 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  =  88.918 deg; O5  -- O4  = 2 A
O6  -- T2  -- O4  = 110.258 deg; O6  -- O4  = 3 A
       88.918 deg <-- 108.415 deg --> 119.911 deg

        O-T-O SUMMARY
          Range  = 88.9175 deg <--> 119.9111 deg
          Mean   = 108.2853 deg
          StdDev = 8.0878 deg

        O--O SUMMARY
          Range  = 2.2379 A <--> 2.8033 A
          Mean   = 2.6162 A
          StdDev = 0.1491 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 144.442 deg; T1  -- T1  = 5.7416 A
T1  - O1  - T1  - O4  - T2  =  89.515 deg; T1  -- T2  = 4.2131 A
T1  - O1  - T1  - O3  - T2  =  89.516 deg; T1  -- T2  = 4.2204 A
T1  - O2  - T1  - O4  - T2  = 112.811 deg; T1  -- T2  = 5.3816 A
T1  - O2  - T1  - O3  - T2  = 109.884 deg; T1  -- T2  = 5.2965 A
T2  - O4  - T1  - O3  - T2  = 104.121 deg; T2  -- T2  = 5.0557 A

T2  - O3  - T2  - O5  - T2  = 148.352 deg; T2  -- T2  = 5.6704 A
T2  - O3  - T2  - O6  - T1  =  90.484 deg; T2  -- T1  = 4.2204 A
T2  - O3  - T2  - O4  - T1  =  90.485 deg; T2  -- T1  = 4.2131 A
T2  - O5  - T2  - O6  - T1  =  87.696 deg; T2  -- T1  = 4.4262 A
T2  - O5  - T2  - O4  - T1  = 120.574 deg; T2  -- T1  = 5.5409 A
T1  - O6  - T2  - O4  - T1  = 104.121 deg; T1  -- T1  = 5.0557 A

        T-T-T SUMMARY
          Range  = 87.6957 deg <--> 148.3525 deg
          Mean   = 106.9029 deg
          StdDev = 19.2826 deg

        T--T SUMMARY
          Range  = 4.2131 A <--> 5.7416 A
          Mean   = 4.9047 A
          StdDev = 0.5926 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2602 A

T1  -- O2  -- T1  = 116.155 deg ; T1  -- T1   2.7672 A

T1  -- O3  -- T2  = 164.257 deg ; T1  -- T2   3.2004 A

T1  -- O4  -- T2  = 173.212 deg ; T1  -- T2   3.2101 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.1793 A

T2  -- O6  -- T2  = 110.734 deg ; T2  -- T2   2.7130 A


        T-O-T SUMMARY
          Range  = 110.7335° <--> 180.0000 deg
          Mean   = 154.0595 deg
          StdDev = 29.8708 deg

        T--T SUMMARY
          Range  = 2.7130 A <--> 3.2602 A
          Mean   = 3.0550 A
          StdDev = 0.2294 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O5  = 2.2379 A
T1  -- T1  = 2.7672 Angstrom
T2  -- T2  = 2.7130 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 170 202 228 253 277 299 325 351
TD10 = 818
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 170 202 228 253 277 299 325 351
TD10 = 818
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 818.000
Average ring size = 5.6000