Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14343_AN4MQg.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.48 T-atoms per nm^3
Material density = 1.744 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6143 Angstrom
T1  -- O2  = 1.6142 Angstrom
T1  -- O3  = 1.6164 Angstrom
T1  -- O4  = 1.6134 Angstrom
      mean = 1.6146 Angstrom
        t1 = 0.004139  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001912  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6156 Angstrom
T2  -- O6  = 1.6183 Angstrom
T2  -- O4  = 1.6138 Angstrom
T2  -- O3  = 1.6177 Angstrom
      mean = 1.6164 Angstrom
        t1 = 0.005134  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003749  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6134 A <--> 1.6183 A
          Mean   = 1.6155 A
          StdDev = 0.0018 A

       t1 Range  = 0.0041 <-- 0.0046 --> 0.0051
       t2 Range  = 0.0019 <-- 0.0028 --> 0.0037

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.711 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.345 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.325 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.221 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.514 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.704 deg; O3  -- O4  = 3 A
       108.711 deg <-- 109.470 deg --> 110.221 deg

O5  -- T2  -- O6  = 109.711 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 108.838 deg; O5  -- O4  = 3 A
O5  -- T2  -- O3  = 108.819 deg; O5  -- O3  = 3 A
O6  -- T2  -- O4  = 109.637 deg; O6  -- O4  = 3 A
O6  -- T2  -- O3  = 110.003 deg; O6  -- O3  = 3 A
O4  -- T2  -- O3  = 109.810 deg; O4  -- O3  = 3 A
       108.819 deg <-- 109.470 deg --> 110.003 deg

        O-T-O SUMMARY
          Range  = 108.7109 deg <--> 110.2212 deg
          Mean   = 109.4934 deg
          StdDev = 0.4543 deg

        O--O SUMMARY
          Range  = 2.6236 A <--> 2.6509 A
          Mean   = 2.6384 A
          StdDev = 0.0082 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 113.267 deg; T1  -- T1  = 5.3672 A
T1  - O1  - T1  - O3  - T2  = 114.043 deg; T1  -- T2  = 5.2995 A
T1  - O1  - T1  - O4  - T2  =  90.083 deg; T1  -- T2  = 4.4518 A
T1  - O2  - T1  - O3  - T2  = 119.267 deg; T1  -- T2  = 5.4775 A
T1  - O2  - T1  - O4  - T2  = 125.696 deg; T1  -- T2  = 5.6250 A
T2  - O3  - T1  - O4  - T2  =  89.747 deg; T2  -- T2  = 4.3829 A

T2  - O5  - T2  - O6  - T1  = 114.043 deg; T2  -- T1  = 5.3071 A
T2  - O5  - T2  - O4  - T2  = 113.075 deg; T2  -- T2  = 5.3709 A
T2  - O5  - T2  - O3  - T1  =  89.917 deg; T2  -- T1  = 4.4518 A
T1  - O6  - T2  - O4  - T2  = 119.624 deg; T1  -- T2  = 5.4897 A
T1  - O6  - T2  - O3  - T1  =  90.253 deg; T1  -- T1  = 4.4023 A
T2  - O4  - T2  - O3  - T1  = 125.108 deg; T2  -- T1  = 5.6124 A

        T-T-T SUMMARY
          Range  = 89.7467 deg <--> 125.6963 deg
          Mean   = 108.2243 deg
          StdDev = 14.4926 deg

        T--T SUMMARY
          Range  = 4.3829 A <--> 5.6250 A
          Mean   = 5.0819 A
          StdDev = 0.5140 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2287 A

T1  -- O2  -- T1  = 164.218 deg ; T1  -- T1   3.1978 A

T1  -- O3  -- T2  = 145.973 deg ; T1  -- T2   3.0926 A

T1  -- O4  -- T2  = 150.312 deg ; T1  -- T2   3.1194 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2312 A

T2  -- O6  -- T2  = 164.394 deg ; T2  -- T2   3.2067 A


        T-O-T SUMMARY
          Range  = 145.9730° <--> 180.0000 deg
          Mean   = 164.1496 deg
          StdDev = 13.3475 deg

        T--T SUMMARY
          Range  = 3.0926 A <--> 3.2312 A
          Mean   = 3.1794 A
          StdDev = 0.0549 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 313 352 387 420 452
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 267 311 351 388 422 452
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182