Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14192_RMK6ll.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 20.81 T-atoms per nm^3
Material density = 2.076 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6162 Angstrom
T1  -- O2  = 1.6290 Angstrom
T1  -- O3  = 1.6101 Angstrom
T1  -- O4  = 1.6218 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.016863  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012764  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6294 Angstrom
T2  -- O4  = 1.6247 Angstrom
T2  -- O5  = 1.6154 Angstrom
T2  -- O6  = 1.6364 Angstrom
      mean = 1.6265 Angstrom
        t1 = 0.012480  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004541  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6101 A <--> 1.6364 A
          Mean   = 1.6229 A
          StdDev = 0.0083 A

       t1 Range  = 0.0125 <-- 0.0147 --> 0.0169
       t2 Range  = 0.0045 <-- 0.0087 --> 0.0128

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.756 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.062 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.963 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.712 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.643 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.438 deg; O3  -- O4  = 3 A
       104.963 deg <-- 109.429 deg --> 112.062 deg

O3  -- T2  -- O4  = 108.966 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.751 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.974 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 107.853 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.875 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 110.380 deg; O5  -- O6  = 3 A
       107.853 deg <-- 109.467 deg --> 110.380 deg

        O-T-O SUMMARY
          Range  = 104.9627 deg <--> 112.0619 deg
          Mean   = 109.3005 deg
          StdDev = 1.9001 deg

        O--O SUMMARY
          Range  = 2.5683 A <--> 2.6866 A
          Mean   = 2.6468 A
          StdDev = 0.0339 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.022 deg; T1  -- T2  = 4.1382 A
T1  - O1  - T1  - O3  - T2  =  90.021 deg; T1  -- T2  = 4.2190 A
T1  - O1  - T1  - O4  - T1  = 133.389 deg; T1  -- T1  = 5.6432 A
T2  - O2  - T1  - O3  - T2  = 107.915 deg; T2  -- T2  = 4.8468 A
T2  - O2  - T1  - O4  - T1  = 134.322 deg; T2  -- T1  = 5.6901 A
T2  - O3  - T1  - O4  - T1  =  88.509 deg; T2  -- T1  = 4.3882 A

T1  - O3  - T2  - O4  - T2  =  89.978 deg; T1  -- T2  = 4.1382 A
T1  - O3  - T2  - O5  - T2  = 111.917 deg; T1  -- T2  = 5.1163 A
T1  - O3  - T2  - O6  - T1  = 107.915 deg; T1  -- T1  = 4.8468 A
T2  - O4  - T2  - O5  - T2  = 133.363 deg; T2  -- T2  = 5.6432 A
T2  - O4  - T2  - O6  - T1  =  89.979 deg; T2  -- T1  = 4.2190 A
T2  - O5  - T2  - O6  - T1  = 118.640 deg; T2  -- T1  = 5.4051 A

        T-T-T SUMMARY
          Range  = 88.5087 deg <--> 134.3225 deg
          Mean   = 108.3308 deg
          StdDev = 18.2128 deg

        T--T SUMMARY
          Range  = 4.1382 A <--> 5.6901 A
          Mean   = 4.8657 A
          StdDev = 0.6066 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2324 A

T1  -- O2  -- T1  = 126.596 deg ; T1  -- T1   2.9106 A

T1  -- O3  -- T2  = 130.379 deg ; T1  -- T2   2.9405 A

T1  -- O4  -- T2  = 140.251 deg ; T1  -- T2   3.0532 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2308 A

T2  -- O6  -- T2  = 125.755 deg ; T2  -- T2   2.9128 A


        T-O-T SUMMARY
          Range  = 125.7548° <--> 180.0000 deg
          Mean   = 147.1634 deg
          StdDev = 24.1997 deg

        T--T SUMMARY
          Range  = 2.9106 A <--> 3.2324 A
          Mean   = 3.0467 A
          StdDev = 0.1421 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000