Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14173_S9JHSK.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 18.05 T-atoms per nm^3
Material density = 1.801 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6167 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6099 Angstrom
T1  -- O4  = 1.6208 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.004811  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002472  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6101 Angstrom
T2  -- O6  = 1.6204 Angstrom
T2  -- O4  = 1.6209 Angstrom
T2  -- O5  = 1.6140 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.004379  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001287  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6099 A <--> 1.6209 A
          Mean   = 1.6167 A
          StdDev = 0.0046 A

       t1 Range  = 0.0044 <-- 0.0046 --> 0.0048
       t2 Range  = 0.0013 <-- 0.0019 --> 0.0025

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.376 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.296 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.536 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.585 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.543 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.491 deg; O3  -- O4  = 3 A
       109.296 deg <-- 109.471 deg --> 109.585 deg

O3  -- T2  -- O6  = 109.703 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.445 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.480 deg; O3  -- O5  = 3 A
O6  -- T2  -- O4  = 109.635 deg; O6  -- O4  = 3 A
O6  -- T2  -- O5  = 109.328 deg; O6  -- O5  = 3 A
O4  -- T2  -- O5  = 109.235 deg; O4  -- O5  = 3 A
       109.235 deg <-- 109.471 deg --> 109.703 deg

        O-T-O SUMMARY
          Range  = 109.2347 deg <--> 109.7035 deg
          Mean   = 109.4819 deg
          StdDev = 0.1380 deg

        O--O SUMMARY
          Range  = 2.6317 A <--> 2.6492 A
          Mean   = 2.6401 A
          StdDev = 0.0054 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.976 deg; T1  -- T2  = 4.4365 A
T1  - O1  - T1  - O3  - T1  = 124.355 deg; T1  -- T1  = 5.5665 A
T1  - O1  - T1  - O4  - T2  =  89.974 deg; T1  -- T2  = 4.3072 A
T2  - O2  - T1  - O3  - T1  = 112.859 deg; T2  -- T1  = 5.3718 A
T2  - O2  - T1  - O4  - T2  = 111.598 deg; T2  -- T2  = 5.1672 A
T1  - O3  - T1  - O4  - T2  = 122.329 deg; T1  -- T2  = 5.4901 A

T1  - O3  - T2  - O6  - T2  =  90.024 deg; T1  -- T2  = 4.4365 A
T1  - O3  - T2  - O4  - T1  = 111.598 deg; T1  -- T1  = 5.1672 A
T1  - O3  - T2  - O5  - T2  = 108.170 deg; T1  -- T2  = 5.2171 A
T2  - O6  - T2  - O4  - T1  =  90.026 deg; T2  -- T1  = 4.3072 A
T2  - O6  - T2  - O5  - T2  = 124.481 deg; T2  -- T2  = 5.5624 A
T1  - O4  - T2  - O5  - T2  = 126.461 deg; T1  -- T2  = 5.5904 A

        T-T-T SUMMARY
          Range  = 89.9742 deg <--> 126.4606 deg
          Mean   = 108.6019 deg
          StdDev = 14.0713 deg

        T--T SUMMARY
          Range  = 4.3072 A <--> 5.5904 A
          Mean   = 5.0564 A
          StdDev = 0.5021 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2335 A

T1  -- O2  -- T1  = 141.445 deg ; T1  -- T1   3.0599 A

T1  -- O3  -- T2  = 172.832 deg ; T1  -- T2   3.2137 A

T1  -- O4  -- T2  = 138.629 deg ; T1  -- T2   3.0327 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2280 A

T2  -- O6  -- T2  = 141.248 deg ; T2  -- T2   3.0572 A


        T-O-T SUMMARY
          Range  = 138.6292° <--> 180.0000 deg
          Mean   = 159.0258 deg
          StdDev = 19.1634 deg

        T--T SUMMARY
          Range  = 3.0327 A <--> 3.2335 A
          Mean   = 3.1375 A
          StdDev = 0.0901 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 304 350 388 427 462
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 304 350 388 427 462
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000