Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14168_NQjPS2.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 20.86 T-atoms per nm^3
Material density = 2.081 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6204 Angstrom
T1  -- O2  = 1.6203 Angstrom
T1  -- O3  = 1.6344 Angstrom
T1  -- O4  = 1.6249 Angstrom
      mean = 1.6250 Angstrom
        t1 = 0.009883  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002188  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6279 Angstrom
T2  -- O5  = 1.6146 Angstrom
T2  -- O6  = 1.6219 Angstrom
T2  -- O4  = 1.6236 Angstrom
      mean = 1.6220 Angstrom
        t1 = 0.011892  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006393  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6146 A <--> 1.6344 A
          Mean   = 1.6235 A
          StdDev = 0.0056 A

       t1 Range  = 0.0099 <-- 0.0109 --> 0.0119
       t2 Range  = 0.0022 <-- 0.0043 --> 0.0064

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.298 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.388 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.415 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.026 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.081 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.610 deg; O3  -- O4  = 3 A
       109.026 deg <-- 109.470 deg --> 110.415 deg

O3  -- T2  -- O5  = 111.936 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.799 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 107.903 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.952 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 107.331 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.854 deg; O6  -- O4  = 3 A
       107.331 deg <-- 109.463 deg --> 111.936 deg

        O-T-O SUMMARY
          Range  = 107.3312 deg <--> 111.9365 deg
          Mean   = 109.4518 deg
          StdDev = 1.1719 deg

        O--O SUMMARY
          Range  = 2.6086 A <--> 2.6872 A
          Mean   = 2.6513 A
          StdDev = 0.0197 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.900 deg; T1  -- T2  = 4.1656 A
T1  - O1  - T1  - O3  - T1  = 125.882 deg; T1  -- T1  = 5.5827 A
T1  - O1  - T1  - O4  - T2  =  89.904 deg; T1  -- T2  = 4.2678 A
T2  - O2  - T1  - O3  - T1  = 108.306 deg; T2  -- T1  = 4.9557 A
T2  - O2  - T1  - O4  - T2  = 109.916 deg; T2  -- T2  = 4.8153 A
T1  - O3  - T1  - O4  - T2  = 126.651 deg; T1  -- T2  = 5.5896 A

T1  - O3  - T2  - O5  - T2  =  90.100 deg; T1  -- T2  = 4.1656 A
T1  - O3  - T2  - O6  - T1  = 109.916 deg; T1  -- T1  = 4.8153 A
T1  - O3  - T2  - O4  - T2  = 139.288 deg; T1  -- T2  = 5.7169 A
T2  - O5  - T2  - O6  - T1  =  90.096 deg; T2  -- T1  = 4.2678 A
T2  - O5  - T2  - O4  - T2  = 126.251 deg; T2  -- T2  = 5.5725 A
T1  - O6  - T2  - O4  - T2  =  89.803 deg; T1  -- T2  = 4.4094 A

        T-T-T SUMMARY
          Range  = 89.8026 deg <--> 139.2882 deg
          Mean   = 109.6377 deg
          StdDev = 17.4161 deg

        T--T SUMMARY
          Range  = 4.1656 A <--> 5.7169 A
          Mean   = 4.9189 A
          StdDev = 0.5886 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2408 A

T1  -- O2  -- T1  = 138.172 deg ; T1  -- T1   3.0271 A

T1  -- O3  -- T2  = 122.995 deg ; T1  -- T2   2.8670 A

T1  -- O4  -- T2  = 136.153 deg ; T1  -- T2   3.0135 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2293 A

T2  -- O6  -- T2  = 136.900 deg ; T2  -- T2   3.0171 A


        T-O-T SUMMARY
          Range  = 122.9950° <--> 180.0000 deg
          Mean   = 149.0365 deg
          StdDev = 22.9441 deg

        T--T SUMMARY
          Range  = 2.8670 A <--> 3.2408 A
          Mean   = 3.0658 A
          StdDev = 0.1342 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 541
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 539
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000