Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14162_vUYMrd.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 18.00 T-atoms per nm^3
Material density = 1.796 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O2  = 1.6197 Angstrom
T1  -- O3  = 1.6100 Angstrom
T1  -- O4  = 1.6206 Angstrom
      mean = 1.6165 Angstrom
        t1 = 0.004329  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001851  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6098 Angstrom
T2  -- O6  = 1.6202 Angstrom
T2  -- O4  = 1.6210 Angstrom
T2  -- O5  = 1.6154 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.004451  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001219  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6098 A <--> 1.6210 A
          Mean   = 1.6166 A
          StdDev = 0.0044 A

       t1 Range  = 0.0043 <-- 0.0044 --> 0.0045
       t2 Range  = 0.0012 <-- 0.0015 --> 0.0019

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.329 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.427 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.361 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.679 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.517 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.512 deg; O3  -- O4  = 3 A
       109.329 deg <-- 109.471 deg --> 109.679 deg

O3  -- T2  -- O6  = 109.692 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.440 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.427 deg; O3  -- O5  = 3 A
O6  -- T2  -- O4  = 109.536 deg; O6  -- O4  = 3 A
O6  -- T2  -- O5  = 109.308 deg; O6  -- O5  = 3 A
O4  -- T2  -- O5  = 109.424 deg; O4  -- O5  = 3 A
       109.308 deg <-- 109.471 deg --> 109.692 deg

        O-T-O SUMMARY
          Range  = 109.3076 deg <--> 109.6919 deg
          Mean   = 109.4850 deg
          StdDev = 0.1143 deg

        O--O SUMMARY
          Range  = 2.6327 A <--> 2.6475 A
          Mean   = 2.6399 A
          StdDev = 0.0044 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.003 deg; T1  -- T2  = 4.4488 A
T1  - O1  - T1  - O3  - T1  = 123.482 deg; T1  -- T1  = 5.5541 A
T1  - O1  - T1  - O4  - T2  =  90.004 deg; T1  -- T2  = 4.3163 A
T2  - O2  - T1  - O3  - T1  = 111.459 deg; T2  -- T1  = 5.3286 A
T2  - O2  - T1  - O4  - T2  = 111.975 deg; T2  -- T2  = 5.1790 A
T1  - O3  - T1  - O4  - T2  = 123.927 deg; T1  -- T2  = 5.5280 A

T1  - O3  - T2  - O6  - T2  =  89.997 deg; T1  -- T2  = 4.4488 A
T1  - O3  - T2  - O4  - T2  = 110.483 deg; T1  -- T2  = 5.2968 A
T1  - O3  - T2  - O5  - T1  = 111.975 deg; T1  -- T1  = 5.1790 A
T2  - O6  - T2  - O4  - T2  = 123.483 deg; T2  -- T2  = 5.5538 A
T2  - O6  - T2  - O5  - T1  =  89.996 deg; T2  -- T1  = 4.3163 A
T2  - O4  - T2  - O5  - T1  = 124.834 deg; T2  -- T1  = 5.5503 A

        T-T-T SUMMARY
          Range  = 89.9963 deg <--> 124.8344 deg
          Mean   = 110.1471 deg
          StdDev = 13.5972 deg

        T--T SUMMARY
          Range  = 4.3163 A <--> 5.5541 A
          Mean   = 5.1197 A
          StdDev = 0.4779 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2317 A

T1  -- O2  -- T1  = 143.152 deg ; T1  -- T1   3.0734 A

T1  -- O3  -- T2  = 174.681 deg ; T1  -- T2   3.2163 A

T1  -- O4  -- T2  = 138.393 deg ; T1  -- T2   3.0303 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2309 A

T2  -- O6  -- T2  = 143.104 deg ; T2  -- T2   3.0738 A


        T-O-T SUMMARY
          Range  = 138.3933° <--> 180.0000 deg
          Mean   = 159.8883 deg
          StdDev = 18.8894 deg

        T--T SUMMARY
          Range  = 3.0303 A <--> 3.2317 A
          Mean   = 3.1427 A
          StdDev = 0.0868 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000