Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14160_p8bEo8.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.90 T-atoms per nm^3
Material density = 1.786 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6162 Angstrom
T1  -- O2  = 1.6166 Angstrom
T1  -- O3  = 1.6161 Angstrom
T1  -- O4  = 1.6167 Angstrom
      mean = 1.6164 Angstrom
        t1 = 0.004691  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001821  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6153 Angstrom
T2  -- O4  = 1.6164 Angstrom
T2  -- O5  = 1.6153 Angstrom
T2  -- O6  = 1.6176 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.004463  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001941  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6153 A <--> 1.6176 A
          Mean   = 1.6163 A
          StdDev = 0.0007 A

       t1 Range  = 0.0045 <-- 0.0046 --> 0.0047
       t2 Range  = 0.0018 <-- 0.0019 --> 0.0019

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.392 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.264 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.112 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.508 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.313 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.233 deg; O3  -- O4  = 3 A
       109.112 deg <-- 109.470 deg --> 110.313 deg

O3  -- T2  -- O4  = 109.255 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.232 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.898 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.168 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.970 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.299 deg; O5  -- O6  = 3 A
       109.168 deg <-- 109.470 deg --> 109.970 deg

        O-T-O SUMMARY
          Range  = 109.1124 deg <--> 110.3129 deg
          Mean   = 109.4818 deg
          StdDev = 0.3835 deg

        O--O SUMMARY
          Range  = 2.6337 A <--> 2.6536 A
          Mean   = 2.6395 A
          StdDev = 0.0067 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.012 deg; T1  -- T2  = 4.4683 A
T1  - O1  - T1  - O3  - T1  = 117.395 deg; T1  -- T1  = 5.4976 A
T1  - O1  - T1  - O4  - T2  =  90.012 deg; T1  -- T2  = 4.4601 A
T2  - O2  - T1  - O3  - T1  = 118.188 deg; T2  -- T1  = 5.4476 A
T2  - O2  - T1  - O4  - T2  = 115.828 deg; T2  -- T2  = 5.2705 A
T1  - O3  - T1  - O4  - T2  = 118.078 deg; T1  -- T2  = 5.4344 A

T1  - O3  - T2  - O4  - T2  =  89.988 deg; T1  -- T2  = 4.4683 A
T1  - O3  - T2  - O5  - T2  = 117.621 deg; T1  -- T2  = 5.4297 A
T1  - O3  - T2  - O6  - T1  = 115.828 deg; T1  -- T1  = 5.2705 A
T2  - O4  - T2  - O5  - T2  = 117.387 deg; T2  -- T2  = 5.4968 A
T2  - O4  - T2  - O6  - T1  =  89.988 deg; T2  -- T1  = 4.4601 A
T2  - O5  - T2  - O6  - T1  = 118.674 deg; T2  -- T1  = 5.4496 A

        T-T-T SUMMARY
          Range  = 89.9879 deg <--> 118.6743 deg
          Mean   = 108.6052 deg
          StdDev = 12.8824 deg

        T--T SUMMARY
          Range  = 4.4601 A <--> 5.4976 A
          Mean   = 5.1086 A
          StdDev = 0.4516 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2325 A

T1  -- O2  -- T1  = 163.993 deg ; T1  -- T1   3.2016 A

T1  -- O3  -- T2  = 149.322 deg ; T1  -- T2   3.1162 A

T1  -- O4  -- T2  = 147.564 deg ; T1  -- T2   3.1045 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2305 A

T2  -- O6  -- T2  = 163.794 deg ; T2  -- T2   3.2030 A


        T-O-T SUMMARY
          Range  = 147.5641° <--> 180.0000 deg
          Mean   = 164.1121 deg
          StdDev = 13.1714 deg

        T--T SUMMARY
          Range  = 3.1045 A <--> 3.2325 A
          Mean   = 3.1814 A
          StdDev = 0.0529 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000