Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14145_hYi5V_.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 20.99 T-atoms per nm^3
Material density = 2.094 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6181 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6303 Angstrom
T1  -- O4  = 1.6220 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.008460  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001868  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6267 Angstrom
T2  -- O5  = 1.6161 Angstrom
T2  -- O6  = 1.6216 Angstrom
T2  -- O4  = 1.6236 Angstrom
      mean = 1.6220 Angstrom
        t1 = 0.011558  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005933  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6161 A <--> 1.6303 A
          Mean   = 1.6224 A
          StdDev = 0.0043 A

       t1 Range  = 0.0085 <-- 0.0100 --> 0.0116
       t2 Range  = 0.0019 <-- 0.0039 --> 0.0059

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.412 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.418 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.313 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.338 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.801 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.541 deg; O3  -- O4  = 3 A
       108.801 deg <-- 109.470 deg --> 110.313 deg

O3  -- T2  -- O5  = 111.841 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.728 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 108.546 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 110.079 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 107.156 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.422 deg; O6  -- O4  = 3 A
       107.156 deg <-- 109.462 deg --> 111.841 deg

        O-T-O SUMMARY
          Range  = 107.1564 deg <--> 111.8409 deg
          Mean   = 109.4408 deg
          StdDev = 1.1105 deg

        O--O SUMMARY
          Range  = 2.6069 A <--> 2.6859 A
          Mean   = 2.6492 A
          StdDev = 0.0184 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.918 deg; T1  -- T2  = 4.1584 A
T1  - O1  - T1  - O3  - T1  = 128.863 deg; T1  -- T1  = 5.6244 A
T1  - O1  - T1  - O4  - T2  =  89.921 deg; T1  -- T2  = 4.2340 A
T2  - O2  - T1  - O3  - T1  = 106.485 deg; T2  -- T1  = 4.9097 A
T2  - O2  - T1  - O4  - T2  = 109.801 deg; T2  -- T2  = 4.8116 A
T1  - O3  - T1  - O4  - T2  = 125.987 deg; T1  -- T2  = 5.5522 A

T1  - O3  - T2  - O5  - T2  =  90.082 deg; T1  -- T2  = 4.1584 A
T1  - O3  - T2  - O6  - T2  = 137.007 deg; T1  -- T2  = 5.6944 A
T1  - O3  - T2  - O4  - T1  = 109.801 deg; T1  -- T1  = 4.8116 A
T2  - O5  - T2  - O6  - T2  = 129.109 deg; T2  -- T2  = 5.6191 A
T2  - O5  - T2  - O4  - T1  =  90.079 deg; T2  -- T1  = 4.2340 A
T2  - O6  - T2  - O4  - T1  =  89.563 deg; T2  -- T1  = 4.3892 A

        T-T-T SUMMARY
          Range  = 89.5626 deg <--> 137.0067 deg
          Mean   = 107.9183 deg
          StdDev = 17.5319 deg

        T--T SUMMARY
          Range  = 4.1584 A <--> 5.6944 A
          Mean   = 4.8462 A
          StdDev = 0.5943 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2362 A

T1  -- O2  -- T1  = 135.268 deg ; T1  -- T1   2.9977 A

T1  -- O3  -- T2  = 124.796 deg ; T1  -- T2   2.8863 A

T1  -- O4  -- T2  = 134.599 deg ; T1  -- T2   2.9942 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2322 A

T2  -- O6  -- T2  = 134.369 deg ; T2  -- T2   2.9894 A


        T-O-T SUMMARY
          Range  = 124.7959° <--> 180.0000 deg
          Mean   = 148.1720 deg
          StdDev = 23.2706 deg

        T--T SUMMARY
          Range  = 2.8863 A <--> 3.2362 A
          Mean   = 3.0560 A
          StdDev = 0.1345 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000