Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_5_70357287_AGc8aG.cif"

There are 72 T-atoms per unit cell
There are 144 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5315 Angstrom
T1  -- O2  = 1.5748 Angstrom
T1  -- O3  = 1.6401 Angstrom
T1  -- O4  = 1.5035 Angstrom
      mean = 1.5625 Angstrom
        t1 = 0.074176  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048415  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5258 Angstrom
T2  -- O5  = 1.7123 Angstrom
T2  -- O6  = 1.7113 Angstrom
T2  -- O7  = 1.5087 Angstrom
      mean = 1.6145 Angstrom
        t1 = 0.108513  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.070017  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.7518 Angstrom
T3  -- O8  = 1.6549 Angstrom
T3  -- O9  = 1.7998 Angstrom
T3  -- O10 = 1.7666 Angstrom
      mean = 1.7433 Angstrom
        t1 = 0.117388  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.068221  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.7593 Angstrom
T4  -- O12 = 1.7475 Angstrom
T4  -- O13 = 1.8518 Angstrom
T4  -- O7  = 1.5192 Angstrom
      mean = 1.7195 Angstrom
        t1 = 0.144842  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.132011  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6750 Angstrom
T5  -- O10 = 1.6750 Angstrom
T5  -- O14 = 1.6027 Angstrom
T5  -- O14 = 1.6027 Angstrom
      mean = 1.6388 Angstrom
        t1 = 0.058692  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036508  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5035 A <--> 1.8518 A
          Mean   = 1.6576 A
          StdDev = 0.1087 A

       t1 Range  = 0.0587 <-- 0.1007 --> 0.1448
       t2 Range  = 0.0365 <-- 0.0710 --> 0.1320

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 102.230 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 111.842 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  94.320 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 113.877 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.353 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 120.043 deg; O3  -- O4  = 3 A
       94.320 deg <-- 108.944 deg --> 120.043 deg

O4  -- T2  -- O5  = 114.902 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.043 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 105.345 deg; O4  -- O7  = 2 A
O5  -- T2  -- O6  = 135.409 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  97.538 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  =  92.076 deg; O6  -- O7  = 2 A
       92.076 deg <-- 108.219 deg --> 135.409 deg

O6  -- T3  -- O8  = 115.026 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 117.084 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 =  91.538 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 103.817 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 101.014 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 127.914 deg; O9  -- O10 = 3 A
       91.538 deg <-- 109.399 deg --> 127.914 deg

O11 -- T4  -- O12 = 112.078 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 124.252 deg; O11 -- O13 = 3 A
O11 -- T4  -- O7  =  89.834 deg; O11 -- O7  = 2 A
O12 -- T4  -- O13 = 122.528 deg; O12 -- O13 = 3 A
O12 -- T4  -- O7  =  89.831 deg; O12 -- O7  = 2 A
O13 -- T4  -- O7  = 100.181 deg; O13 -- O7  = 3 A
       89.831 deg <-- 106.451 deg --> 124.252 deg

O10 -- T5  -- O10 = 123.996 deg; O10 -- O10 = 3 A
O10 -- T5  -- O14 = 106.768 deg; O10 -- O14 = 3 A
O10 -- T5  -- O14 = 108.523 deg; O10 -- O14 = 3 A
O10 -- T5  -- O14 = 108.523 deg; O10 -- O14 = 3 A
O10 -- T5  -- O14 = 106.768 deg; O10 -- O14 = 3 A
O14 -- T5  -- O14 =  99.584 deg; O14 -- O14 = 2 A
       99.584 deg <-- 109.027 deg --> 123.996 deg

        O-T-O SUMMARY
          Range  = 89.8312 deg <--> 135.4087 deg
          Mean   = 107.9666 deg
          StdDev = 11.9248 deg

        O--O SUMMARY
          Range  = 2.2255 A <--> 3.2043 A
          Mean   = 2.6627 A
          StdDev = 0.2699 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 126.631 deg ; T1  -- T1   2.7368 A

T1  -- O2  -- T1  = 107.732 deg ; T1  -- T1   2.5438 A

T1  -- O3  -- T1  = 171.175 deg ; T1  -- T1   3.2705 A

T1  -- O4  -- T2  = 145.671 deg ; T1  -- T2   2.8944 A

T2  -- O5  -- T2  = 128.945 deg ; T2  -- T2   3.0903 A

T2  -- O6  -- T3  = 123.734 deg ; T2  -- T3   3.0540 A

T2  -- O7  -- T4  = 138.312 deg ; T2  -- T4   2.8297 A

T3  -- O8  -- T3  = 124.578 deg ; T3  -- T3   2.9302 A

T3  -- O9  -- T3  = 159.004 deg ; T3  -- T3   3.5393 A

T3  -- O10 -- T5  = 152.708 deg ; T3  -- T5   3.3445 A

T4  -- O11 -- T4  = 146.479 deg ; T4  -- T4   3.3691 A

T4  -- O12 -- T4  = 149.053 deg ; T4  -- T4   3.3684 A

T4  -- O13 -- T4  = 173.820 deg ; T4  -- T4   3.6983 A

T5  -- O14 -- T5  = 140.160 deg ; T5  -- T5   3.0136 A


        T-O-T SUMMARY
          Range  = 107.7318° <--> 173.8203 deg
          Mean   = 142.0682 deg
          StdDev = 18.4701 deg

        T--T SUMMARY
          Range  = 2.5438 A <--> 3.6983 A
          Mean   = 3.1242 A
          StdDev = 0.3190 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2255 A
O1  -- O4  = 2.2255 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T2  = 2.8944 Angstrom
  T1  -- T4  = 3.2350 Angstrom
  T1  -- T1  = 2.5438 Angstrom
  T1  -- T1  = 2.7368 Angstrom
  T1  -- T1  = 3.2705 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.8944 Angstrom
  T2  -- T2  = 2.5795 Angstrom
  T2  -- T3  = 3.0540 Angstrom
  T2  -- T2  = 3.0903 Angstrom
  T2  -- T4  = 2.8297 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T2  = 3.0540 Angstrom
  T3  -- T3  = 2.9302 Angstrom
  T3  -- T4  = 2.8845 Angstrom
  T3  -- T5  = 3.3445 Angstrom
  T3  -- T4  = 3.4608 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 3.2350 Angstrom
  T4  -- T3  = 2.8845 Angstrom
  T4  -- T4  = 3.3691 Angstrom
  T4  -- T4  = 3.3684 Angstrom
  T4  -- T2  = 2.8297 Angstrom
  T4  -- T3  = 3.4608 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 22 39 67 108 162 226 300 387 482 579 692 831 973
TD10 = 950
Circuit symbol = 4.4.4.6.4.6_{3}
Weight = 14
Vertex symbol  = 4.4.4.6_{2}.4.8_{3}
Weight = 21

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 57 93 146 208 279 364 454 549 665 796 928 1069
TD10 = 1219
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 16
Vertex symbol  = 4.6.4.6.6.8
Weight = 15

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 25 46 77 121 174 237 314 399 493 604 723 848 990 1142
TD10 = 1409
Circuit symbol = 4.6_{2}.8.8_{2}.8.8_{3}
Weight = 26
Vertex symbol  = 4.6_{2}.8.8_{2}.8.8_{3}
Weight = 26

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 39 59 89 135 196 269 350 440 543 657 779 912 1058
TD10 = 1174
Circuit symbol = 4.6_{2}.4.8_{3}.6.8_{6}
Weight = 29
Vertex symbol  = 4.6_{2}.4.8_{3}.8_{2}.8_{3}
Weight = 29

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 22 50 86 126 182 255 330 410 512 631 752 873 1006 1168
TD10 = 1475
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{2}.8_{2}.8_{2}
Weight = 36

<TD10> = 1219.889
Average ring size = 6.0584