Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_5_53866139_kiQKxw.cif"

There are 80 T-atoms per unit cell
There are 160 O-atoms per unit cell

Framework density = 18.07 T-atoms per nm^3
Material density = 1.803 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6209 Angstrom
T1  -- O2  = 1.6226 Angstrom
T1  -- O3  = 1.6005 Angstrom
T1  -- O4  = 1.6210 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.010123  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005946  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6056 Angstrom
T2  -- O5  = 1.6540 Angstrom
T2  -- O6  = 1.6726 Angstrom
T2  -- O7  = 1.6611 Angstrom
      mean = 1.6483 Angstrom
        t1 = 0.039104  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026711  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6396 Angstrom
T3  -- O5  = 1.6396 Angstrom
T3  -- O8  = 1.6448 Angstrom
T3  -- O9  = 1.6188 Angstrom
      mean = 1.6357 Angstrom
        t1 = 0.017537  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005165  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6321 Angstrom
T4  -- O10 = 1.6097 Angstrom
T4  -- O11 = 1.5909 Angstrom
T4  -- O12 = 1.6052 Angstrom
      mean = 1.6095 Angstrom
        t1 = 0.167957  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.153738  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6388 Angstrom
T5  -- O12 = 1.5465 Angstrom
T5  -- O13 = 1.5717 Angstrom
T5  -- O14 = 1.5954 Angstrom
      mean = 1.5881 Angstrom
        t1 = 0.070528  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045563  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5465 A <--> 1.6726 A
          Mean   = 1.6196 A
          StdDev = 0.0297 A

       t1 Range  = 0.0101 <-- 0.0610 --> 0.1680
       t2 Range  = 0.0052 <-- 0.0474 --> 0.1537

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.109 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.844 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.949 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.584 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.792 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.514 deg; O3  -- O4  = 3 A
       107.584 deg <-- 109.465 deg --> 110.792 deg

O3  -- T2  -- O5  = 109.707 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.642 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 104.862 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 110.552 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.877 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 116.861 deg; O6  -- O7  = 3 A
       104.862 deg <-- 109.417 deg --> 116.861 deg

O4  -- T3  -- O5  = 108.226 deg; O4  -- O5  = 3 A
O4  -- T3  -- O8  = 109.414 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.205 deg; O4  -- O9  = 3 A
O5  -- T3  -- O8  = 110.700 deg; O5  -- O8  = 3 A
O5  -- T3  -- O9  = 108.585 deg; O5  -- O9  = 3 A
O8  -- T3  -- O9  = 110.660 deg; O8  -- O9  = 3 A
       108.226 deg <-- 109.465 deg --> 110.700 deg

O6  -- T4  -- O10 = 108.060 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 =  76.677 deg; O6  -- O11 = 2 A
O6  -- T4  -- O12 =  66.956 deg; O6  -- O12 = 2 A
O10 -- T4  -- O11 = 113.038 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 113.103 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 127.787 deg; O11 -- O12 = 3 A
       66.956 deg <-- 100.937 deg --> 127.787 deg

O7  -- T5  -- O12 =  93.830 deg; O7  -- O12 = 2 A
O7  -- T5  -- O13 = 109.783 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 =  93.966 deg; O7  -- O14 = 2 A
O12 -- T5  -- O13 = 110.539 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 128.406 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 114.302 deg; O13 -- O14 = 3 A
       93.830 deg <-- 108.471 deg --> 128.406 deg

        O-T-O SUMMARY
          Range  = 66.9557 deg <--> 128.4064 deg
          Mean   = 107.2313 deg
          StdDev = 12.0545 deg

        O--O SUMMARY
          Range  = 1.7859 A <--> 2.8700 A
          Mean   = 2.5952 A
          StdDev = 0.2255 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 174.336 deg ; T1  -- T1   3.2379 A

T1  -- O2  -- T1  = 141.593 deg ; T1  -- T1   3.0645 A

T1  -- O3  -- T2  = 143.946 deg ; T1  -- T2   3.0487 A

T1  -- O4  -- T3  = 140.547 deg ; T1  -- T3   3.0693 A

T2  -- O5  -- T3  = 146.384 deg ; T2  -- T3   3.1528 A

T2  -- O6  -- T4  = 132.562 deg ; T2  -- T4   3.0257 A

T2  -- O7  -- T5  = 144.748 deg ; T2  -- T5   3.1450 A

T3  -- O8  -- T3  = 174.944 deg ; T3  -- T3   3.2863 A

T3  -- O9  -- T3  = 139.750 deg ; T3  -- T3   3.0400 A

T4  -- O10 -- T4  = 162.044 deg ; T4  -- T4   3.1799 A

T4  -- O11 -- T4  = 118.626 deg ; T4  -- T4   2.7362 A

T4  -- O12 -- T5  = 124.584 deg ; T4  -- T5   2.7904 A

T5  -- O13 -- T5  = 158.840 deg ; T5  -- T5   3.0900 A

T5  -- O14 -- T5  = 117.668 deg ; T5  -- T5   2.7302 A


        T-O-T SUMMARY
          Range  = 117.6677° <--> 174.9444 deg
          Mean   = 144.3265 deg
          StdDev = 17.5836 deg

        T--T SUMMARY
          Range  = 2.7302 A <--> 3.2863 A
          Mean   = 3.0426 A
          StdDev = 0.1690 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O6  -- O11 = 1.9995 A
O6  -- O12 = 1.7859 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.0487 Angstrom
  T2  -- T3  = 3.1528 Angstrom
  T2  -- T4  = 2.9728 Angstrom
  T2  -- T4  = 3.0257 Angstrom
  T2  -- T5  = 3.1942 Angstrom
  T2  -- T5  = 3.1450 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 2.9728 Angstrom
  T4  -- T2  = 3.0257 Angstrom
  T4  -- T4  = 2.7362 Angstrom
  T4  -- T5  = 2.7904 Angstrom
  T4  -- T4  = 3.1799 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 3.1942 Angstrom
  T5  -- T2  = 3.1450 Angstrom
  T5  -- T4  = 2.7904 Angstrom
  T5  -- T5  = 3.0900 Angstrom
  T5  -- T5  = 2.7302 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27
Vertex symbol  = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 18 32 52 74 100 128 162 204 244 286 340 396 450 512
TD10 = 783
Circuit symbol = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29
Vertex symbol  = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27
Vertex symbol  = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27
Vertex symbol  = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27
Vertex symbol  = 4.8_{3}.4.8_{3}.4_{2}.8_{4}
Weight = 27

<TD10> = 786.200
Average ring size = 6.3333