Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_5_31623518_t0ij4Z.cif"

There are 80 T-atoms per unit cell
There are 160 O-atoms per unit cell

Framework density = 24.82 T-atoms per nm^3
Material density = 2.477 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6083 Angstrom
T1  -- O2  = 1.6665 Angstrom
T1  -- O3  = 1.5135 Angstrom
T1  -- O4  = 1.6392 Angstrom
      mean = 1.6069 Angstrom
        t1 = 0.075056  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.070475  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5542 Angstrom
T2  -- O5  = 1.5971 Angstrom
T2  -- O6  = 1.7412 Angstrom
T2  -- O7  = 1.6636 Angstrom
      mean = 1.6390 Angstrom
        t1 = 0.087964  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.054329  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6145 Angstrom
T3  -- O10 = 1.5650 Angstrom
T3  -- O6  = 1.7513 Angstrom
T3  -- O9  = 1.6846 Angstrom
      mean = 1.6538 Angstrom
        t1 = 0.045546  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028126  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.7064 Angstrom
T4  -- O11 = 1.6297 Angstrom
T4  -- O12 = 1.6314 Angstrom
T4  -- O13 = 1.6457 Angstrom
      mean = 1.6533 Angstrom
        t1 = 0.061850  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.057978  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O14 = 1.6562 Angstrom
T5  -- O15 = 1.5460 Angstrom
T5  -- O10 = 1.6006 Angstrom
T5  -- O13 = 1.6305 Angstrom
      mean = 1.6083 Angstrom
        t1 = 0.123770  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.095673  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5135 A <--> 1.7513 A
          Mean   = 1.6323 A
          StdDev = 0.0603 A

       t1 Range  = 0.0455 <-- 0.0788 --> 0.1238
       t2 Range  = 0.0281 <-- 0.0613 --> 0.0957

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 118.394 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  99.929 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 110.208 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  99.488 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 121.894 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 101.637 deg; O3  -- O4  = 2 A
       99.488 deg <-- 108.592 deg --> 121.894 deg

O4  -- T2  -- O5  = 111.721 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.599 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  =  96.248 deg; O4  -- O7  = 2 A
O5  -- T2  -- O6  = 112.689 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  97.151 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 130.036 deg; O6  -- O7  = 3 A
       96.248 deg <-- 109.241 deg --> 130.036 deg

O8  -- T3  -- O10 = 113.367 deg; O8  -- O10 = 3 A
O8  -- T3  -- O6  = 110.753 deg; O8  -- O6  = 3 A
O8  -- T3  -- O9  = 111.125 deg; O8  -- O9  = 3 A
O10 -- T3  -- O6  = 105.577 deg; O10 -- O6  = 3 A
O10 -- T3  -- O9  = 103.426 deg; O10 -- O9  = 3 A
O6  -- T3  -- O9  = 112.305 deg; O6  -- O9  = 3 A
       103.426 deg <-- 109.426 deg --> 113.367 deg

O7  -- T4  -- O11 = 108.443 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 119.816 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 114.968 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 =  98.353 deg; O11 -- O12 = 2 A
O11 -- T4  -- O13 = 113.067 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 101.105 deg; O12 -- O13 = 3 A
       98.353 deg <-- 109.292 deg --> 119.816 deg

O14 -- T5  -- O15 = 135.376 deg; O14 -- O15 = 3 A
O14 -- T5  -- O10 = 116.478 deg; O14 -- O10 = 3 A
O14 -- T5  -- O13 = 107.300 deg; O14 -- O13 = 3 A
O15 -- T5  -- O10 = 106.915 deg; O15 -- O10 = 3 A
O15 -- T5  -- O13 =  76.112 deg; O15 -- O13 = 2 A
O10 -- T5  -- O13 =  96.813 deg; O10 -- O13 = 2 A
       76.112 deg <-- 106.499 deg --> 135.376 deg

        O-T-O SUMMARY
          Range  = 76.1117 deg <--> 135.3763 deg
          Mean   = 108.4059 deg
          StdDev = 10.7607 deg

        O--O SUMMARY
          Range  = 1.9592 A <--> 3.0864 A
          Mean   = 2.6427 A
          StdDev = 0.2190 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 115.563 deg ; T1  -- T1   2.7214 A

T1  -- O2  -- T1  = 142.831 deg ; T1  -- T1   3.1592 A

T1  -- O3  -- T1  = 166.089 deg ; T1  -- T1   3.0047 A

T1  -- O4  -- T2  = 116.776 deg ; T1  -- T2   2.7200 A

T2  -- O5  -- T2  = 151.838 deg ; T2  -- T2   3.0983 A

T2  -- O6  -- T3  = 154.582 deg ; T2  -- T3   3.4069 A

T2  -- O7  -- T4  = 146.817 deg ; T2  -- T4   3.2297 A

T3  -- O8  -- T3  = 104.202 deg ; T3  -- T3   2.5480 A

T3  -- O9  -- T3  = 158.205 deg ; T3  -- T3   3.3085 A

T3  -- O10 -- T5  = 120.087 deg ; T3  -- T5   2.7427 A

T4  -- O11 -- T4  = 117.759 deg ; T4  -- T4   2.7904 A

T4  -- O12 -- T4  = 124.984 deg ; T4  -- T4   2.8939 A

T4  -- O13 -- T5  = 156.230 deg ; T4  -- T5   3.2060 A

T5  -- O14 -- T5  = 124.098 deg ; T5  -- T5   2.9259 A

T5  -- O15 -- T5  = 161.972 deg ; T5  -- T5   3.0538 A


        T-O-T SUMMARY
          Range  = 104.2015° <--> 166.0892 deg
          Mean   = 137.4688 deg
          StdDev = 19.8015 deg

        T--T SUMMARY
          Range  = 2.5480 A <--> 3.4069 A
          Mean   = 2.9873 A
          StdDev = 0.2425 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O13 -- O15 = 1.9592 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T2  = 2.7200 Angstrom
  T1  -- T4  = 3.1219 Angstrom
  T1  -- T1  = 3.1592 Angstrom
  T1  -- T1  = 2.7214 Angstrom
  T1  -- T1  = 3.0047 Angstrom
T2  -- T1  = 2.7200 Angstrom
T3  -- T5  = 2.7427 Angstrom
T3  -- T3  = 2.5480 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 3.1219 Angstrom
  T4  -- T2  = 3.2297 Angstrom
  T4  -- T4  = 2.7904 Angstrom
  T4  -- T4  = 2.8939 Angstrom
  T4  -- T5  = 3.1710 Angstrom
  T4  -- T5  = 3.2060 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T3  = 2.7427 Angstrom
  T5  -- T4  = 3.1710 Angstrom
  T5  -- T5  = 2.9259 Angstrom
  T5  -- T5  = 3.0538 Angstrom
  T5  -- T4  = 3.2060 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 38 64 91 117 149 195 250 304 356 408 467 544 633
TD10 = 937
Circuit symbol = 4.6.4.6_{2}.4.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6_{2}.4.8_{3}
Weight = 23

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 12 24 36 56 86 125 164 195 233 289 354 421 483 542 613
TD10 = 936
Circuit symbol = 6.6.6.6_{2}.6.8_{2}
Weight = 23
Vertex symbol  = 6.6.6.6_{2}.6.8_{2}
Weight = 23

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 23 42 61 83 116 162 211 250 285 336 413 500 569 619
TD10 = 963
Circuit symbol = 4.6.4.6_{2}.6.8_{7}
Weight = 23
Vertex symbol  = 4.6.4.6_{2}.8_{4}.12_{4}
Weight = 35

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 38 63 94 123 151 188 242 309 368 410 458 535 635
TD10 = 935
Circuit symbol = 4.6.4.6_{2}.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6_{2}.6.6
Weight = 19

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 36 60 89 120 152 193 245 299 356 412 469 542 628
TD10 = 930
Circuit symbol = 4.6.4.6_{2}.6.6
Weight = 18
Vertex symbol  = 4.6.4.6_{2}.6.8
Weight = 20

<TD10> = 940.200
Average ring size = 6.0000