Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_4_527590_Hre0Ev.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 20.13 T-atoms per nm^3
Material density = 2.008 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6205 Angstrom
T1  -- O2  = 1.6218 Angstrom
T1  -- O3  = 1.6134 Angstrom
T1  -- O4  = 1.6233 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006511  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001654  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6166 Angstrom
T2  -- O5  = 1.6211 Angstrom
T2  -- O6  = 1.6206 Angstrom
T2  -- O7  = 1.6214 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.006849  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002348  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6217 Angstrom
T3  -- O8  = 1.6212 Angstrom
T3  -- O9  = 1.6208 Angstrom
T3  -- O10 = 1.6173 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.007086  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003060  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6234 Angstrom
T4  -- O10 = 1.6131 Angstrom
T4  -- O11 = 1.6210 Angstrom
T4  -- O12 = 1.6215 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.006583  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002000  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6131 A <--> 1.6234 A
          Mean   = 1.6199 A
          StdDev = 0.0030 A

       t1 Range  = 0.0065 <-- 0.0068 --> 0.0071
       t2 Range  = 0.0017 <-- 0.0023 --> 0.0031

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.512 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.570 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.473 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.593 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.742 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.937 deg; O3  -- O4  = 3 A
       108.937 deg <-- 109.471 deg --> 109.742 deg

O3  -- T2  -- O5  = 109.365 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.963 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.658 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.372 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.494 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.972 deg; O6  -- O7  = 3 A
       108.658 deg <-- 109.471 deg --> 109.972 deg

O4  -- T3  -- O8  = 109.517 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.973 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 108.557 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.387 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.437 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.954 deg; O9  -- O10 = 3 A
       108.557 deg <-- 109.471 deg --> 109.973 deg

O7  -- T4  -- O10 = 108.883 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.519 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.787 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 109.565 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.586 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.486 deg; O11 -- O12 = 3 A
       108.883 deg <-- 109.471 deg --> 109.787 deg

        O-T-O SUMMARY
          Range  = 108.5568 deg <--> 109.9729 deg
          Mean   = 109.4737 deg
          StdDev = 0.3909 deg

        O--O SUMMARY
          Range  = 2.6296 A <--> 2.6556 A
          Mean   = 2.6452 A
          StdDev = 0.0077 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  84.703 deg; T1  -- T2  = 4.1093 A
T1  - O1  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 5.6549 A
T1  - O1  - T1  - O4  - T3  =  90.515 deg; T1  -- T3  = 4.3301 A
T2  - O2  - T1  - O3  - T1  = 136.904 deg; T2  -- T1  = 5.6509 A
T2  - O2  - T1  - O4  - T3  = 108.655 deg; T2  -- T3  = 4.9154 A
T1  - O3  - T1  - O4  - T3  =  89.997 deg; T1  -- T3  = 4.2935 A

T1  - O3  - T2  - O5  - T2  = 126.845 deg; T1  -- T2  = 5.4358 A
T1  - O3  - T2  - O6  - T4  = 108.536 deg; T1  -- T4  = 4.9106 A
T1  - O3  - T2  - O7  - T2  =  82.513 deg; T1  -- T2  = 4.1093 A
T2  - O5  - T2  - O6  - T4  =  89.997 deg; T2  -- T4  = 4.2942 A
T2  - O5  - T2  - O7  - T2  = 123.724 deg; T2  -- T2  = 5.5137 A
T4  - O6  - T2  - O7  - T2  = 128.794 deg; T4  -- T2  = 5.6130 A

T1  - O4  - T3  - O8  - T3  = 128.717 deg; T1  -- T3  = 5.6118 A
T1  - O4  - T3  - O9  - T4  = 108.517 deg; T1  -- T4  = 4.9119 A
T1  - O4  - T3  - O10 - T3  =  90.003 deg; T1  -- T3  = 4.2935 A
T3  - O8  - T3  - O9  - T4  =  82.510 deg; T3  -- T4  = 4.1093 A
T3  - O8  - T3  - O10 - T3  = 123.754 deg; T3  -- T3  = 5.5114 A
T4  - O9  - T3  - O10 - T3  = 126.905 deg; T4  -- T3  = 5.4355 A

T2  - O7  - T4  - O10 - T3  = 108.600 deg; T2  -- T3  = 4.9133 A
T2  - O7  - T4  - O11 - T4  =  90.528 deg; T2  -- T4  = 4.3267 A
T2  - O7  - T4  - O12 - T4  =  90.003 deg; T2  -- T4  = 4.2942 A
T3  - O10 - T4  - O11 - T4  =  84.756 deg; T3  -- T4  = 4.1093 A
T3  - O10 - T4  - O12 - T4  = 136.866 deg; T3  -- T4  = 5.6530 A
T4  - O11 - T4  - O12 - T4  = 135.000 deg; T4  -- T4  = 5.6533 A

        T-T-T SUMMARY
          Range  = 82.5097 deg <--> 136.9035 deg
          Mean   = 109.8289 deg
          StdDev = 19.4401 deg

        T--T SUMMARY
          Range  = 4.1093 A <--> 5.6549 A
          Mean   = 4.9350 A
          StdDev = 0.6081 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.295 deg ; T1  -- T1   3.0483 A

T1  -- O2  -- T1  = 142.605 deg ; T1  -- T1   3.0725 A

T1  -- O3  -- T2  = 139.166 deg ; T1  -- T2   3.0272 A

T1  -- O4  -- T3  = 137.430 deg ; T1  -- T3   3.0236 A

T2  -- O5  -- T2  = 140.439 deg ; T2  -- T2   3.0509 A

T2  -- O6  -- T2  = 161.995 deg ; T2  -- T2   3.2013 A

T2  -- O7  -- T4  = 137.308 deg ; T2  -- T4   3.0222 A

T3  -- O8  -- T3  = 140.116 deg ; T3  -- T3   3.0480 A

T3  -- O9  -- T3  = 161.762 deg ; T3  -- T3   3.2006 A

T3  -- O10 -- T4  = 139.228 deg ; T3  -- T4   3.0280 A

T4  -- O11 -- T4  = 140.423 deg ; T4  -- T4   3.0506 A

T4  -- O12 -- T4  = 142.240 deg ; T4  -- T4   3.0685 A


        T-O-T SUMMARY
          Range  = 137.3076° <--> 161.9953 deg
          Mean   = 143.5840 deg
          StdDev = 8.3418 deg

        T--T SUMMARY
          Range  = 3.0222 A <--> 3.2013 A
          Mean   = 3.0701 A
          StdDev = 0.0607 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

<TD10> = 840.000
Average ring size = 6.2609