Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_4_521282_C2cJyS.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 17.78 T-atoms per nm^3
Material density = 1.774 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6157 Angstrom
T1  -- O2  = 1.6200 Angstrom
T1  -- O3  = 1.6159 Angstrom
T1  -- O4  = 1.6203 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.005091  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000733  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6160 Angstrom
T2  -- O5  = 1.6156 Angstrom
T2  -- O6  = 1.6192 Angstrom
T2  -- O7  = 1.6210 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005354  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002048  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6207 Angstrom
T3  -- O8  = 1.6158 Angstrom
T3  -- O9  = 1.6193 Angstrom
T3  -- O10 = 1.6170 Angstrom
      mean = 1.6182 Angstrom
        t1 = 0.005390  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002448  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6207 Angstrom
T4  -- O10 = 1.6170 Angstrom
T4  -- O11 = 1.6154 Angstrom
T4  -- O12 = 1.6203 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.005298  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000949  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6210 A
          Mean   = 1.6181 A
          StdDev = 0.0021 A

       t1 Range  = 0.0051 <-- 0.0053 --> 0.0054
       t2 Range  = 0.0007 <-- 0.0015 --> 0.0024

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.287 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.652 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.323 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.379 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.594 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.592 deg; O3  -- O4  = 3 A
       109.287 deg <-- 109.471 deg --> 109.652 deg

O3  -- T2  -- O5  = 109.615 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.105 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.631 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.287 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.305 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.884 deg; O6  -- O7  = 3 A
       109.105 deg <-- 109.471 deg --> 109.884 deg

O4  -- T3  -- O8  = 109.321 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.846 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.603 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.277 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.595 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.186 deg; O9  -- O10 = 3 A
       109.186 deg <-- 109.471 deg --> 109.846 deg

O7  -- T4  -- O10 = 109.552 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.336 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.567 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 109.644 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.417 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.310 deg; O11 -- O12 = 3 A
       109.310 deg <-- 109.471 deg --> 109.644 deg

        O-T-O SUMMARY
          Range  = 109.1047 deg <--> 109.8838 deg
          Mean   = 109.4876 deg
          StdDev = 0.1997 deg

        O--O SUMMARY
          Range  = 2.6355 A <--> 2.6523 A
          Mean   = 2.6427 A
          StdDev = 0.0042 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  90.000 deg; T2  -- T1  = 4.4743 A
T2  - O1  - T1  - O3  - T1  = 113.592 deg; T2  -- T1  = 5.1476 A
T2  - O1  - T1  - O4  - T3  = 118.412 deg; T2  -- T3  = 5.2912 A
T1  - O2  - T1  - O3  - T1  = 130.334 deg; T1  -- T1  = 5.6917 A
T1  - O2  - T1  - O4  - T3  = 130.045 deg; T1  -- T3  = 5.6918 A
T1  - O3  - T1  - O4  - T3  =  77.422 deg; T1  -- T3  = 3.8175 A

T1  - O3  - T2  - O5  - T2  = 122.185 deg; T1  -- T2  = 5.4298 A
T1  - O3  - T2  - O6  - T4  = 118.406 deg; T1  -- T4  = 5.2913 A
T1  - O3  - T2  - O7  - T2  =  90.000 deg; T1  -- T2  = 4.4743 A
T2  - O5  - T2  - O6  - T4  =  76.658 deg; T2  -- T4  = 3.8175 A
T2  - O5  - T2  - O7  - T2  = 126.686 deg; T2  -- T2  = 5.6501 A
T4  - O6  - T2  - O7  - T2  = 127.146 deg; T4  -- T2  = 5.6233 A

T3  - O4  - T3  - O8  - T4  =  89.992 deg; T3  -- T4  = 4.4703 A
T3  - O4  - T3  - O9  - T1  = 126.980 deg; T3  -- T1  = 5.6215 A
T3  - O4  - T3  - O10 - T3  = 126.580 deg; T3  -- T3  = 5.6474 A
T4  - O8  - T3  - O9  - T1  = 118.281 deg; T4  -- T1  = 5.2805 A
T4  - O8  - T3  - O10 - T3  = 122.557 deg; T4  -- T3  = 5.4298 A
T1  - O9  - T3  - O10 - T3  =  76.707 deg; T1  -- T3  = 3.8175 A

T2  - O7  - T4  - O10 - T3  = 118.254 deg; T2  -- T3  = 5.2801 A
T2  - O7  - T4  - O11 - T4  = 129.895 deg; T2  -- T4  = 5.6905 A
T2  - O7  - T4  - O12 - T4  =  77.503 deg; T2  -- T4  = 3.8175 A
T3  - O10 - T4  - O11 - T4  =  90.008 deg; T3  -- T4  = 4.4703 A
T3  - O10 - T4  - O12 - T4  = 113.933 deg; T3  -- T4  = 5.1459 A
T4  - O11 - T4  - O12 - T4  = 130.257 deg; T4  -- T4  = 5.6865 A

        T-T-T SUMMARY
          Range  = 76.6582 deg <--> 130.3340 deg
          Mean   = 110.6471 deg
          StdDev = 19.4542 deg

        T--T SUMMARY
          Range  = 3.8175 A <--> 5.6918 A
          Mean   = 5.0513 A
          StdDev = 0.6683 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.589 deg ; T1  -- T1   3.2228 A

T1  -- O2  -- T1  = 140.381 deg ; T1  -- T1   3.0483 A

T1  -- O3  -- T2  = 147.611 deg ; T1  -- T2   3.1037 A

T1  -- O4  -- T3  = 141.087 deg ; T1  -- T3   3.0559 A

T2  -- O5  -- T2  = 171.682 deg ; T2  -- T2   3.2228 A

T2  -- O6  -- T2  = 146.265 deg ; T2  -- T2   3.0990 A

T2  -- O7  -- T4  = 141.055 deg ; T2  -- T4   3.0562 A

T3  -- O8  -- T3  = 173.044 deg ; T3  -- T3   3.2256 A

T3  -- O9  -- T3  = 145.892 deg ; T3  -- T3   3.0961 A

T3  -- O10 -- T4  = 146.338 deg ; T3  -- T4   3.0955 A

T4  -- O11 -- T4  = 172.978 deg ; T4  -- T4   3.2247 A

T4  -- O12 -- T4  = 139.722 deg ; T4  -- T4   3.0425 A


        T-O-T SUMMARY
          Range  = 139.7220° <--> 173.0440 deg
          Mean   = 153.1369 deg
          StdDev = 13.8343 deg

        T--T SUMMARY
          Range  = 3.0425 A <--> 3.2256 A
          Mean   = 3.1244 A
          StdDev = 0.0733 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

<TD10> = 840.000
Average ring size = 6.2609