Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_4_521013__YU9_O.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 20.38 T-atoms per nm^3
Material density = 2.034 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6151 Angstrom
T1  -- O3  = 1.6079 Angstrom
T1  -- O1  = 1.6281 Angstrom
T1  -- O4  = 1.6403 Angstrom
      mean = 1.6229 Angstrom
        t1 = 0.022849  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015650  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5876 Angstrom
T2  -- O5  = 1.6463 Angstrom
T2  -- O6  = 1.6152 Angstrom
T2  -- O7  = 1.6362 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.027409  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019445  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6358 Angstrom
T3  -- O8  = 1.6465 Angstrom
T3  -- O9  = 1.6144 Angstrom
T3  -- O10 = 1.5872 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.027429  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017642  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6086 Angstrom
T4  -- O12 = 1.6152 Angstrom
T4  -- O7  = 1.6408 Angstrom
T4  -- O11 = 1.6279 Angstrom
      mean = 1.6231 Angstrom
        t1 = 0.022726  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014215  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5872 A <--> 1.6465 A
          Mean   = 1.6221 A
          StdDev = 0.0183 A

       t1 Range  = 0.0227 <-- 0.0251 --> 0.0274
       t2 Range  = 0.0142 <-- 0.0167 --> 0.0194

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 104.269 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 111.561 deg; O2  -- O1  = 3 A
O2  -- T1  -- O4  = 113.787 deg; O2  -- O4  = 3 A
O3  -- T1  -- O1  = 108.126 deg; O3  -- O1  = 3 A
O3  -- T1  -- O4  = 110.470 deg; O3  -- O4  = 3 A
O1  -- T1  -- O4  = 108.458 deg; O1  -- O4  = 3 A
       104.269 deg <-- 109.445 deg --> 113.787 deg

O3  -- T2  -- O5  = 105.877 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.828 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 106.449 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.042 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 115.950 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.384 deg; O6  -- O7  = 3 A
       105.877 deg <-- 109.422 deg --> 115.950 deg

O4  -- T3  -- O8  = 116.001 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 110.355 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 106.542 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 108.982 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 105.833 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.819 deg; O9  -- O10 = 3 A
       105.833 deg <-- 109.422 deg --> 116.001 deg

O10 -- T4  -- O12 = 104.336 deg; O10 -- O12 = 3 A
O10 -- T4  -- O7  = 110.444 deg; O10 -- O7  = 3 A
O10 -- T4  -- O11 = 108.127 deg; O10 -- O11 = 3 A
O12 -- T4  -- O7  = 113.761 deg; O12 -- O7  = 3 A
O12 -- T4  -- O11 = 111.567 deg; O12 -- O11 = 3 A
O7  -- T4  -- O11 = 108.440 deg; O7  -- O11 = 3 A
       104.336 deg <-- 109.446 deg --> 113.761 deg

        O-T-O SUMMARY
          Range  = 104.2688 deg <--> 116.0008 deg
          Mean   = 109.3559 deg
          StdDev = 3.2615 deg

        O--O SUMMARY
          Range  = 2.5445 A <--> 2.7836 A
          Mean   = 2.6456 A
          StdDev = 0.0662 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O2  - T1  - O3  - T1  =  91.420 deg; T2  -- T1  = 3.9093 A
T2  - O2  - T1  - O1  - T1  = 124.362 deg; T2  -- T1  = 5.2327 A
T2  - O2  - T1  - O4  - T3  =  74.541 deg; T2  -- T3  = 3.6256 A
T1  - O3  - T1  - O1  - T1  = 134.928 deg; T1  -- T1  = 5.4806 A
T1  - O3  - T1  - O4  - T3  =  99.457 deg; T1  -- T3  = 4.5654 A
T1  - O1  - T1  - O4  - T3  = 114.834 deg; T1  -- T3  = 5.4090 A

T1  - O3  - T2  - O5  - T2  = 136.743 deg; T1  -- T2  = 5.5243 A
T1  - O3  - T2  - O6  - T2  =  88.580 deg; T1  -- T2  = 3.9093 A
T1  - O3  - T2  - O7  - T4  =  77.680 deg; T1  -- T4  = 3.7530 A
T2  - O5  - T2  - O6  - T2  =  98.259 deg; T2  -- T2  = 4.6135 A
T2  - O5  - T2  - O7  - T4  = 115.251 deg; T2  -- T4  = 5.4462 A
T2  - O6  - T2  - O7  - T4  = 143.131 deg; T2  -- T4  = 5.7930 A

T3  - O4  - T3  - O8  - T3  =  98.266 deg; T3  -- T3  = 4.6133 A
T3  - O4  - T3  - O9  - T4  =  88.560 deg; T3  -- T4  = 3.9091 A
T3  - O4  - T3  - O10 - T1  = 143.125 deg; T3  -- T1  = 5.7930 A
T3  - O8  - T3  - O9  - T4  = 136.748 deg; T3  -- T4  = 5.5222 A
T3  - O8  - T3  - O10 - T1  = 115.242 deg; T3  -- T1  = 5.4435 A
T4  - O9  - T3  - O10 - T1  =  77.706 deg; T4  -- T1  = 3.7530 A

T3  - O10 - T4  - O12 - T4  =  91.440 deg; T3  -- T4  = 3.9091 A
T3  - O10 - T4  - O7  - T2  =  74.529 deg; T3  -- T2  = 3.6256 A
T3  - O10 - T4  - O11 - T4  = 124.386 deg; T3  -- T4  = 5.2327 A
T4  - O12 - T4  - O7  - T2  =  99.446 deg; T4  -- T2  = 4.5654 A
T4  - O12 - T4  - O11 - T4  = 134.925 deg; T4  -- T4  = 5.4800 A
T2  - O7  - T4  - O11 - T4  = 114.810 deg; T2  -- T4  = 5.4091 A

        T-T-T SUMMARY
          Range  = 74.5292 deg <--> 143.1312 deg
          Mean   = 106.8737 deg
          StdDev = 22.4300 deg

        T--T SUMMARY
          Range  = 3.6256 A <--> 5.7930 A
          Mean   = 4.7315 A
          StdDev = 0.7842 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.618 deg ; T1  -- T1   2.7404 A

T1  -- O2  -- T1  = 161.985 deg ; T1  -- T1   3.1904 A

T1  -- O3  -- T2  = 116.742 deg ; T1  -- T2   2.7209 A

T1  -- O4  -- T3  = 160.516 deg ; T1  -- T3   3.2288 A

T2  -- O5  -- T2  = 121.677 deg ; T2  -- T2   2.8752 A

T2  -- O6  -- T2  = 170.155 deg ; T2  -- T2   3.2186 A

T2  -- O7  -- T4  = 160.545 deg ; T2  -- T4   3.2299 A

T3  -- O8  -- T3  = 121.737 deg ; T3  -- T3   2.8765 A

T3  -- O9  -- T3  = 170.096 deg ; T3  -- T3   3.2168 A

T3  -- O10 -- T4  = 116.688 deg ; T3  -- T4   2.7203 A

T4  -- O11 -- T4  = 114.601 deg ; T4  -- T4   2.7398 A

T4  -- O12 -- T4  = 161.947 deg ; T4  -- T4   3.1903 A


        T-O-T SUMMARY
          Range  = 114.6008° <--> 170.1554 deg
          Mean   = 140.9423 deg
          StdDev = 23.6121 deg

        T--T SUMMARY
          Range  = 2.7203 A <--> 3.2299 A
          Mean   = 2.9957 A
          StdDev = 0.2231 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7209 Angstrom
T1  -- T1  = 2.7404 Angstrom
T2  -- T1  = 2.7209 Angstrom
T3  -- T4  = 2.7203 Angstrom
T4  -- T3  = 2.7203 Angstrom
T4  -- T4  = 2.7398 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 38 56 81 112 147 187 226 265 317 381 447 514 575
TD10 = 884
Circuit symbol = 4.6_{2}.4.8_{3}.6_{2}.6_{2}
Weight = 18
Vertex symbol  = 4.6_{2}.4.8.6.6_{2}
Weight = 18

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 35 57 83 111 142 176 222 281 335 379 425 487 574
TD10 = 861
Circuit symbol = 4.6.4.6.6.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6.8_{3}.8_{3}
Weight = 28

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 35 57 83 111 142 176 222 281 335 379 425 487 574
TD10 = 861
Circuit symbol = 4.6.4.6.6.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6.8_{3}.8_{3}
Weight = 28

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 38 56 81 112 147 187 226 265 317 381 447 514 575
TD10 = 884
Circuit symbol = 4.6_{2}.4.8_{3}.6_{2}.6_{2}
Weight = 18
Vertex symbol  = 4.6_{2}.4.8.6.6_{2}
Weight = 18

<TD10> = 872.500
Average ring size = 5.9178