Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_4_510749_40J7iy.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 20.07 T-atoms per nm^3
Material density = 2.003 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6445 Angstrom
T1  -- O2  = 1.6122 Angstrom
T1  -- O3  = 1.5915 Angstrom
T1  -- O4  = 1.6435 Angstrom
      mean = 1.6230 Angstrom
        t1 = 0.027195  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021912  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6160 Angstrom
T2  -- O5  = 1.6296 Angstrom
T2  -- O6  = 1.6222 Angstrom
T2  -- O7  = 1.6441 Angstrom
      mean = 1.6280 Angstrom
        t1 = 0.023340  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025491  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6510 Angstrom
T3  -- O8  = 1.6280 Angstrom
T3  -- O9  = 1.6092 Angstrom
T3  -- O10 = 1.6152 Angstrom
      mean = 1.6259 Angstrom
        t1 = 0.031401  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031302  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6376 Angstrom
T4  -- O10 = 1.6045 Angstrom
T4  -- O11 = 1.6471 Angstrom
T4  -- O12 = 1.6187 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.028353  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035279  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5915 A <--> 1.6510 A
          Mean   = 1.6259 A
          StdDev = 0.0170 A

       t1 Range  = 0.0233 <-- 0.0276 --> 0.0314
       t2 Range  = 0.0219 <-- 0.0285 --> 0.0353

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.121 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.208 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 116.104 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.707 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.297 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.218 deg; O3  -- O4  = 3 A
       106.208 deg <-- 109.442 deg --> 116.104 deg

O3  -- T2  -- O5  = 107.886 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 104.769 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 110.262 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 111.528 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.153 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 114.066 deg; O6  -- O7  = 3 A
       104.769 deg <-- 109.444 deg --> 114.066 deg

O4  -- T3  -- O8  = 109.418 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 115.458 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 108.663 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 112.537 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.836 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 101.443 deg; O9  -- O10 = 2 A
       101.443 deg <-- 109.392 deg --> 115.458 deg

O7  -- T4  -- O10 = 105.400 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 115.979 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 110.747 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 105.228 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.276 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.815 deg; O11 -- O12 = 3 A
       105.228 deg <-- 109.408 deg --> 115.979 deg

        O-T-O SUMMARY
          Range  = 101.4433 deg <--> 116.1036 deg
          Mean   = 109.3008 deg
          StdDev = 3.6959 deg

        O--O SUMMARY
          Range  = 2.4960 A <--> 2.7900 A
          Mean   = 2.6512 A
          StdDev = 0.0714 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T3  =  77.865 deg; T2  -- T3  = 3.7780 A
T2  - O1  - T1  - O3  - T1  =  88.901 deg; T2  -- T1  = 3.9177 A
T2  - O1  - T1  - O4  - T1  = 137.353 deg; T2  -- T1  = 5.5378 A
T3  - O2  - T1  - O3  - T1  = 144.102 deg; T3  -- T1  = 5.8127 A
T3  - O2  - T1  - O4  - T1  = 113.925 deg; T3  -- T1  = 5.4137 A
T1  - O3  - T1  - O4  - T1  =  98.475 deg; T1  -- T1  = 4.6051 A

T1  - O3  - T2  - O5  - T2  = 124.842 deg; T1  -- T2  = 5.2690 A
T1  - O3  - T2  - O6  - T4  =  75.952 deg; T1  -- T4  = 3.6939 A
T1  - O3  - T2  - O7  - T2  =  91.099 deg; T1  -- T2  = 3.9177 A
T2  - O5  - T2  - O6  - T4  = 113.795 deg; T2  -- T4  = 5.3990 A
T2  - O5  - T2  - O7  - T2  = 134.895 deg; T2  -- T2  = 5.5117 A
T4  - O6  - T2  - O7  - T2  =  99.683 deg; T4  -- T2  = 4.5914 A

T1  - O4  - T3  - O8  - T3  = 117.026 deg; T1  -- T3  = 5.4706 A
T1  - O4  - T3  - O9  - T4  =  74.860 deg; T1  -- T4  = 3.6939 A
T1  - O4  - T3  - O10 - T3  =  99.639 deg; T1  -- T3  = 4.5721 A
T3  - O8  - T3  - O9  - T4  = 120.946 deg; T3  -- T4  = 5.1985 A
T3  - O8  - T3  - O10 - T3  = 135.000 deg; T3  -- T3  = 5.4432 A
T4  - O9  - T3  - O10 - T3  =  92.043 deg; T4  -- T3  = 3.9752 A

T2  - O7  - T4  - O10 - T3  =  77.070 deg; T2  -- T3  = 3.7780 A
T2  - O7  - T4  - O11 - T4  = 142.225 deg; T2  -- T4  = 5.8269 A
T2  - O7  - T4  - O12 - T4  = 116.097 deg; T2  -- T4  = 5.4935 A
T3  - O10 - T4  - O11 - T4  =  87.957 deg; T3  -- T4  = 3.9752 A
T3  - O10 - T4  - O12 - T4  = 138.275 deg; T3  -- T4  = 5.6464 A
T4  - O11 - T4  - O12 - T4  =  98.215 deg; T4  -- T4  = 4.6598 A

        T-T-T SUMMARY
          Range  = 74.8599 deg <--> 144.1015 deg
          Mean   = 108.8559 deg
          StdDev = 22.7719 deg

        T--T SUMMARY
          Range  = 3.6939 A <--> 5.8269 A
          Mean   = 4.8029 A
          StdDev = 0.7734 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.939 deg ; T1  -- T1   2.8618 A

T1  -- O2  -- T1  = 169.434 deg ; T1  -- T1   3.2108 A

T1  -- O3  -- T2  = 116.738 deg ; T1  -- T2   2.7311 A

T1  -- O4  -- T3  = 160.506 deg ; T1  -- T3   3.2470 A

T2  -- O5  -- T2  = 115.536 deg ; T2  -- T2   2.7570 A

T2  -- O6  -- T2  = 162.845 deg ; T2  -- T2   3.2081 A

T2  -- O7  -- T4  = 161.049 deg ; T2  -- T4   3.2369 A

T3  -- O8  -- T3  = 113.365 deg ; T3  -- T3   2.7208 A

T3  -- O9  -- T3  = 159.686 deg ; T3  -- T3   3.1680 A

T3  -- O10 -- T4  = 121.033 deg ; T3  -- T4   2.8028 A

T4  -- O11 -- T4  = 124.902 deg ; T4  -- T4   2.9206 A

T4  -- O12 -- T4  = 179.885 deg ; T4  -- T4   3.2375 A


        T-O-T SUMMARY
          Range  = 113.3655° <--> 179.8849 deg
          Mean   = 142.1598 deg
          StdDev = 24.1708 deg

        T--T SUMMARY
          Range  = 2.7208 A <--> 3.2470 A
          Mean   = 3.0085 A
          StdDev = 0.2170 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7311 Angstrom
T2  -- T1  = 2.7311 Angstrom
T2  -- T2  = 2.7570 Angstrom
T3  -- T3  = 2.7208 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 35 57 83 111 142 176 222 281 335 379 425 487 574
TD10 = 861
Circuit symbol = 4.6.4.6.6.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6.8_{3}.8_{3}
Weight = 28

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 38 56 81 112 147 187 226 265 317 381 447 514 575
TD10 = 884
Circuit symbol = 4.6_{2}.4.8_{3}.6_{2}.6_{2}
Weight = 18
Vertex symbol  = 4.6_{2}.4.8.6.6_{2}
Weight = 18

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 22 38 56 81 112 147 187 226 265 317 381 447 514 575
TD10 = 884
Circuit symbol = 4.6_{2}.4.8_{3}.6_{2}.6_{2}
Weight = 18
Vertex symbol  = 4.6_{2}.4.8.6.6_{2}
Weight = 18

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 35 57 83 111 142 176 222 281 335 379 425 487 574
TD10 = 861
Circuit symbol = 4.6.4.6.6.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6.8_{3}.8_{3}
Weight = 28

<TD10> = 872.500
Average ring size = 5.9178