Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_4_279209_l2D6Lj.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 19.10 T-atoms per nm^3
Material density = 1.906 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6060 Angstrom
T1  -- O2  = 1.6467 Angstrom
T1  -- O3  = 1.6206 Angstrom
T1  -- O4  = 1.6498 Angstrom
      mean = 1.6308 Angstrom
        t1 = 0.023155  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016495  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6345 Angstrom
T2  -- O5  = 1.6080 Angstrom
T2  -- O6  = 1.6442 Angstrom
T2  -- O7  = 1.6140 Angstrom
      mean = 1.6252 Angstrom
        t1 = 0.026869  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.034353  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6139 Angstrom
T3  -- O8  = 1.6075 Angstrom
T3  -- O9  = 1.6438 Angstrom
T3  -- O10 = 1.6344 Angstrom
      mean = 1.6249 Angstrom
        t1 = 0.026944  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016361  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6508 Angstrom
T4  -- O11 = 1.6059 Angstrom
T4  -- O12 = 1.6465 Angstrom
T4  -- O13 = 1.6208 Angstrom
      mean = 1.6310 Angstrom
        t1 = 0.023155  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026742  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6059 A <--> 1.6508 A
          Mean   = 1.6280 A
          StdDev = 0.0169 A

       t1 Range  = 0.0232 <-- 0.0250 --> 0.0269
       t2 Range  = 0.0164 <-- 0.0235 --> 0.0344

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.991 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.294 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.219 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.563 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 113.906 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.678 deg; O3  -- O4  = 3 A
       107.219 deg <-- 109.442 deg --> 113.906 deg

O4  -- T2  -- O5  = 109.484 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 115.977 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 103.541 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 108.770 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.776 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.177 deg; O6  -- O7  = 3 A
       103.541 deg <-- 109.454 deg --> 115.977 deg

O7  -- T3  -- O8  = 110.846 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.113 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 103.511 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 108.772 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.464 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 116.023 deg; O9  -- O10 = 3 A
       103.511 deg <-- 109.455 deg --> 116.023 deg

O10 -- T4  -- O11 = 107.221 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 113.861 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 = 108.738 deg; O10 -- O13 = 3 A
O11 -- T4  -- O12 = 107.978 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 108.326 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 110.531 deg; O12 -- O13 = 3 A
       107.221 deg <-- 109.442 deg --> 113.861 deg

        O-T-O SUMMARY
          Range  = 103.5105 deg <--> 116.0229 deg
          Mean   = 109.5573 deg
          StdDev = 3.3095 deg

        O--O SUMMARY
          Range  = 2.5512 A <--> 2.7804 A
          Mean   = 2.6600 A
          StdDev = 0.0641 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 122.248 deg; T2  -- T1  = 5.1708 A
T2  - O1  - T1  - O3  - T1  =  88.969 deg; T2  -- T1  = 4.3004 A
T2  - O1  - T1  - O4  - T1  = 145.478 deg; T2  -- T1  = 5.7367 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3490 A
T1  - O2  - T1  - O4  - T1  =  92.128 deg; T1  -- T1  = 4.3364 A
T1  - O3  - T1  - O4  - T1  =  87.872 deg; T1  -- T1  = 4.3364 A

T1  - O4  - T2  - O5  - T2  = 137.833 deg; T1  -- T2  = 5.7848 A
T1  - O4  - T2  - O6  - T3  = 101.850 deg; T1  -- T3  = 4.3844 A
T1  - O4  - T2  - O7  - T2  =  91.031 deg; T1  -- T2  = 4.3004 A
T2  - O5  - T2  - O6  - T3  =  72.095 deg; T2  -- T3  = 3.5309 A
T2  - O5  - T2  - O7  - T2  = 127.635 deg; T2  -- T2  = 5.6845 A
T3  - O6  - T2  - O7  - T2  = 124.163 deg; T3  -- T2  = 5.1098 A

T2  - O7  - T3  - O8  - T3  = 124.098 deg; T2  -- T3  = 5.1050 A
T2  - O7  - T3  - O9  - T3  =  72.113 deg; T2  -- T3  = 3.5309 A
T2  - O7  - T3  - O10 - T4  = 101.734 deg; T2  -- T4  = 4.3804 A
T3  - O8  - T3  - O9  - T3  = 127.594 deg; T3  -- T3  = 5.6793 A
T3  - O8  - T3  - O10 - T4  =  91.065 deg; T3  -- T4  = 4.2987 A
T3  - O9  - T3  - O10 - T4  = 137.907 deg; T3  -- T4  = 5.7848 A

T3  - O10 - T4  - O11 - T4  =  88.935 deg; T3  -- T4  = 4.2987 A
T3  - O10 - T4  - O12 - T4  = 122.332 deg; T3  -- T4  = 5.1741 A
T3  - O10 - T4  - O13 - T4  = 145.413 deg; T3  -- T4  = 5.7367 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.3500 A
T4  - O11 - T4  - O13 - T4  =  87.893 deg; T4  -- T4  = 4.3380 A
T4  - O12 - T4  - O13 - T4  =  92.107 deg; T4  -- T4  = 4.3380 A

        T-T-T SUMMARY
          Range  = 72.0950 deg <--> 145.4781 deg
          Mean   = 108.8520 deg
          StdDev = 22.8583 deg

        T--T SUMMARY
          Range  = 3.5309 A <--> 5.7848 A
          Mean   = 4.8005 A
          StdDev = 0.6993 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 165.637 deg ; T1  -- T1   3.1868 A

T1  -- O2  -- T1  = 127.944 deg ; T1  -- T1   2.9594 A

T1  -- O3  -- T1  = 141.676 deg ; T1  -- T1   3.0616 A

T1  -- O4  -- T2  = 127.493 deg ; T1  -- T2   2.9455 A

T2  -- O5  -- T2  = 146.646 deg ; T2  -- T2   3.0807 A

T2  -- O6  -- T2  = 163.231 deg ; T2  -- T2   3.2532 A

T2  -- O7  -- T3  = 113.442 deg ; T2  -- T3   2.6986 A

T3  -- O8  -- T3  = 146.307 deg ; T3  -- T3   3.0770 A

T3  -- O9  -- T3  = 163.130 deg ; T3  -- T3   3.2521 A

T3  -- O10 -- T4  = 127.392 deg ; T3  -- T4   2.9451 A

T4  -- O11 -- T4  = 165.593 deg ; T4  -- T4   3.1865 A

T4  -- O12 -- T4  = 128.128 deg ; T4  -- T4   2.9613 A

T4  -- O13 -- T4  = 141.792 deg ; T4  -- T4   3.0631 A


        T-O-T SUMMARY
          Range  = 113.4421° <--> 165.6372 deg
          Mean   = 142.9546 deg
          StdDev = 16.8435 deg

        T--T SUMMARY
          Range  = 2.6986 A <--> 3.2532 A
          Mean   = 3.0516 A
          StdDev = 0.1479 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T3  = 2.6986 Angstrom
T3  -- T2  = 2.6986 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 14 27 50 78 104 132 171 219 263 300 350 421 490 547
TD10 = 808
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.10_{4}
Weight = 20

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 33 50 75 105 136 171 210 256 309 361 415 476 544
TD10 = 815
Circuit symbol = 4.4.6.8.6.8_{2}
Weight = 18
Vertex symbol  = 4.4.6.8.6.10_{2}
Weight = 25

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 33 50 75 105 136 171 210 256 309 361 415 476 544
TD10 = 815
Circuit symbol = 4.4.6.8.6.8_{2}
Weight = 18
Vertex symbol  = 4.4.6.8.6.10_{2}
Weight = 25

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 14 27 50 78 104 132 171 219 263 300 350 421 490 547
TD10 = 808
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.10_{4}
Weight = 20

<TD10> = 811.500
Average ring size = 5.8716