Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_119_3_2848_mJHv6l.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 19.04 T-atoms per nm^3
Material density = 1.900 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6274 Angstrom
T1  -- O2  = 1.6280 Angstrom
T1  -- O3  = 1.6174 Angstrom
T1  -- O4  = 1.6335 Angstrom
      mean = 1.6266 Angstrom
        t1 = 0.011118  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003252  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6356 Angstrom
T2  -- O5  = 1.6307 Angstrom
T2  -- O6  = 1.6309 Angstrom
T2  -- O7  = 1.6111 Angstrom
      mean = 1.6271 Angstrom
        t1 = 0.014755  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010115  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6063 Angstrom
T3  -- O8  = 1.6347 Angstrom
T3  -- O9  = 1.6356 Angstrom
T3  -- O10 = 1.5909 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.046471  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029500  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5909 A <--> 1.6356 A
          Mean   = 1.6235 A
          StdDev = 0.0136 A

       t1 Range  = 0.0111 <-- 0.0241 --> 0.0465
       t2 Range  = 0.0033 <-- 0.0143 --> 0.0295

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.459 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.398 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.969 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.370 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.900 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.728 deg; O3  -- O4  = 3 A
       108.728 deg <-- 109.471 deg --> 109.969 deg

O4  -- T2  -- O5  = 110.856 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.834 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.619 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.412 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.051 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 107.981 deg; O6  -- O7  = 3 A
       107.981 deg <-- 109.459 deg --> 110.856 deg

O7  -- T3  -- O8  = 109.444 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.411 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 =  95.589 deg; O7  -- O10 = 2 A
O8  -- T3  -- O9  = 112.423 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 114.233 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 114.327 deg; O9  -- O10 = 3 A
       95.589 deg <-- 109.238 deg --> 114.327 deg

        O-T-O SUMMARY
          Range  = 95.5886 deg <--> 114.3273 deg
          Mean   = 108.9443 deg
          StdDev = 3.9496 deg

        O--O SUMMARY
          Range  = 2.3683 A <--> 2.7179 A
          Mean   = 2.6413 A
          StdDev = 0.0789 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 130.798 deg; T2  -- T1  = 5.7635 A
T2  - O1  - T1  - O3  - T1  = 130.827 deg; T2  -- T1  = 5.7615 A
T2  - O1  - T1  - O4  - T1  = 112.437 deg; T2  -- T1  = 5.2971 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4026 A
T1  - O2  - T1  - O4  - T1  =  89.974 deg; T1  -- T1  = 4.4279 A
T1  - O3  - T1  - O4  - T1  =  90.026 deg; T1  -- T1  = 4.4279 A

T1  - O4  - T2  - O5  - T2  = 130.827 deg; T1  -- T2  = 5.5860 A
T1  - O4  - T2  - O6  - T2  = 130.798 deg; T1  -- T2  = 5.5850 A
T1  - O4  - T2  - O7  - T3  = 113.000 deg; T1  -- T3  = 5.3561 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.1253 A
T2  - O5  - T2  - O7  - T3  =  89.552 deg; T2  -- T3  = 4.3125 A
T2  - O6  - T2  - O7  - T3  =  89.651 deg; T2  -- T3  = 4.3160 A

T2  - O7  - T3  - O8  - T3  =  89.437 deg; T2  -- T3  = 4.4895 A
T2  - O7  - T3  - O9  - T3  =  90.448 deg; T2  -- T3  = 4.3125 A
T2  - O7  - T3  - O10 - T3  =  90.349 deg; T2  -- T3  = 4.3160 A
T3  - O8  - T3  - O9  - T3  = 135.000 deg; T3  -- T3  = 5.5897 A
T3  - O8  - T3  - O10 - T3  = 135.000 deg; T3  -- T3  = 5.5994 A
T3  - O9  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.0625 A

        T-T-T SUMMARY
          Range  = 89.4369 deg <--> 135.0000 deg
          Mean   = 104.6420 deg
          StdDev = 18.5100 deg

        T--T SUMMARY
          Range  = 4.0625 A <--> 5.7635 A
          Mean   = 4.8330 A
          StdDev = 0.6018 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.892 deg ; T1  -- T1   3.1117 A

T1  -- O2  -- T1  = 146.097 deg ; T1  -- T1   3.1146 A

T1  -- O3  -- T1  = 153.528 deg ; T1  -- T1   3.1488 A

T1  -- O4  -- T2  = 160.956 deg ; T1  -- T2   3.2241 A

T2  -- O5  -- T2  = 126.885 deg ; T2  -- T2   2.9173 A

T2  -- O6  -- T2  = 126.819 deg ; T2  -- T2   2.9168 A

T2  -- O7  -- T3  = 167.712 deg ; T2  -- T3   3.1989 A

T3  -- O8  -- T3  = 123.348 deg ; T3  -- T3   2.8779 A

T3  -- O9  -- T3  = 122.447 deg ; T3  -- T3   2.8673 A

T3  -- O10 -- T3  = 178.842 deg ; T3  -- T3   3.1816 A


        T-O-T SUMMARY
          Range  = 122.4468° <--> 178.8416 deg
          Mean   = 145.2526 deg
          StdDev = 19.1016 deg

        T--T SUMMARY
          Range  = 2.8673 A <--> 3.2241 A
          Mean   = 3.0559 A
          StdDev = 0.1366 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

<TD10> = 787.000
Average ring size = 6.0000