Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_118_2_194486_e3dzZ3.cif"

There are 10 T-atoms per unit cell
There are 20 O-atoms per unit cell

Framework density = 17.30 T-atoms per nm^3
Material density = 1.726 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6582 Angstrom
T1  -- O2  = 1.6177 Angstrom
T1  -- O3  = 1.6178 Angstrom
T1  -- O4  = 1.6170 Angstrom
      mean = 1.6277 Angstrom
        t1 = 0.072029  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.064441  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6141 Angstrom
T2  -- O4  = 1.6141 Angstrom
T2  -- O4  = 1.6141 Angstrom
T2  -- O4  = 1.6141 Angstrom
      mean = 1.6141 Angstrom
        t1 = 0.027961  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021547  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6141 A <--> 1.6582 A
          Mean   = 1.6249 A
          StdDev = 0.0169 A

       t1 Range  = 0.0280 <-- 0.0500 --> 0.0720
       t2 Range  = 0.0215 <-- 0.0430 --> 0.0644

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 118.525 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 118.506 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.196 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 116.171 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  94.310 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  =  94.383 deg; O3  -- O4  = 2 A
       94.310 deg <-- 108.182 deg --> 118.525 deg

O4  -- T2  -- O4  = 112.658 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 112.658 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 103.270 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 103.270 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 112.658 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 112.658 deg; O4  -- O4  = 3 A
       103.270 deg <-- 109.529 deg --> 112.658 deg

        O-T-O SUMMARY
          Range  = 94.3097 deg <--> 118.5253 deg
          Mean   = 107.5869 deg
          StdDev = 7.8980 deg

        O--O SUMMARY
          Range  = 2.3716 A <--> 2.8157 A
          Mean   = 2.6075 A
          StdDev = 0.1392 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  60.082 deg; T1  -- T2  = 3.0022 A
T1  - O1  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 5.6787 A
T1  - O1  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 5.6787 A
T2  - O2  - T1  - O3  - T1  = 110.651 deg; T2  -- T1  = 5.0615 A
T2  - O2  - T1  - O4  - T1  = 110.651 deg; T2  -- T1  = 5.0615 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4568 A

T1  - O4  - T2  - O4  - T1  =  59.836 deg; T1  -- T1  = 2.9948 A
T1  - O4  - T2  - O4  - T1  = 138.698 deg; T1  -- T1  = 5.6186 A
T1  - O4  - T2  - O4  - T1  = 138.698 deg; T1  -- T1  = 5.6186 A
T1  - O4  - T2  - O4  - T1  = 138.698 deg; T1  -- T1  = 5.6186 A
T1  - O4  - T2  - O4  - T1  = 138.698 deg; T1  -- T1  = 5.6186 A
T1  - O4  - T2  - O4  - T1  =  59.836 deg; T1  -- T1  = 2.9948 A

        T-T-T SUMMARY
          Range  = 59.8363 deg <--> 138.6976 deg
          Mean   = 110.7601 deg
          StdDev = 32.4204 deg

        T--T SUMMARY
          Range  = 2.9948 A <--> 5.6787 A
          Mean   = 4.8126 A
          StdDev = 1.0840 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.122 deg ; T1  -- T1   2.9948 A

T1  -- O2  -- T1  = 153.851 deg ; T1  -- T1   3.1514 A

T1  -- O3  -- T1  = 153.808 deg ; T1  -- T1   3.1514 A

T1  -- O4  -- T2  = 136.607 deg ; T1  -- T2   3.0022 A


        T-O-T SUMMARY
          Range  = 129.1224° <--> 153.8513 deg
          Mean   = 143.3472 deg
          StdDev = 10.9842 deg

        T--T SUMMARY
          Range  = 2.9948 A <--> 3.1514 A
          Mean   = 3.0750 A
          StdDev = 0.0777 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 40 55 80 115 138 183 229 260 328 382 421 515 574
TD10 = 873
Circuit symbol = 3.4.8.9_{5}.8.9_{5}
Weight = 31
Vertex symbol  = 3.4.8.9_{4}.8.9_{4}
Weight = 31

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 8 20 40 52 82 116 132 184 236 252 322 396 416 500 592
TD10 = 875
Circuit symbol = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37
Vertex symbol  = 3.3.9_{4}.9_{4}.9_{4}.9_{4}
Weight = 37

<TD10> = 873.400
Average ring size = 7.0714