Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_118_2_169416_ZAECl5.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 23.80 T-atoms per nm^3
Material density = 2.375 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5947 Angstrom
T1  -- O1  = 1.6416 Angstrom
T1  -- O2  = 1.6707 Angstrom
T1  -- O3  = 1.6329 Angstrom
      mean = 1.6349 Angstrom
        t1 = 0.053194  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036955  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6485 Angstrom
T2  -- O3  = 1.6147 Angstrom
T2  -- O4  = 1.6115 Angstrom
T2  -- O4  = 1.6049 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.080555  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.088056  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5947 A <--> 1.6707 A
          Mean   = 1.6274 A
          StdDev = 0.0240 A

       t1 Range  = 0.0532 <-- 0.0669 --> 0.0806
       t2 Range  = 0.0370 <-- 0.0625 --> 0.0881

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 106.860 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 114.142 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  95.777 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 108.778 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.257 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 114.394 deg; O2  -- O3  = 3 A
       95.777 deg <-- 109.368 deg --> 116.257 deg

O2  -- T2  -- O3  = 109.967 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  =  89.796 deg; O2  -- O4  = 2 A
O2  -- T2  -- O4  = 123.638 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  =  99.954 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 122.946 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  =  98.398 deg; O4  -- O4  = 2 A
       89.796 deg <-- 107.450 deg --> 123.638 deg

        O-T-O SUMMARY
          Range  = 89.7959 deg <--> 123.6380 deg
          Mean   = 108.4090 deg
          StdDev = 10.2853 deg

        O--O SUMMARY
          Range  = 2.3012 A <--> 2.8677 A
          Mean   = 2.6301 A
          StdDev = 0.1804 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O1  - T2  =  94.499 deg; T2  -- T2  = 4.5460 A
T2  - O1  - T1  - O2  - T1  = 147.922 deg; T2  -- T1  = 5.9427 A
T2  - O1  - T1  - O3  - T1  = 108.885 deg; T2  -- T1  = 5.0304 A
T2  - O1  - T1  - O2  - T1  = 108.703 deg; T2  -- T1  = 5.0601 A
T2  - O1  - T1  - O3  - T1  = 120.671 deg; T2  -- T1  = 5.4109 A
T1  - O2  - T1  - O3  - T1  =  78.424 deg; T1  -- T1  = 3.9321 A

T1  - O2  - T2  - O3  - T1  =  84.166 deg; T1  -- T1  = 4.1491 A
T1  - O2  - T2  - O4  - T2  =  83.946 deg; T1  -- T2  = 4.1173 A
T1  - O2  - T2  - O4  - T2  = 148.293 deg; T1  -- T2  = 5.9222 A
T1  - O3  - T2  - O4  - T2  = 113.493 deg; T1  -- T2  = 5.1848 A
T1  - O3  - T2  - O4  - T2  = 126.138 deg; T1  -- T2  = 5.5277 A
T2  - O4  - T2  - O4  - T2  =  75.671 deg; T2  -- T2  = 3.7821 A

        T-T-T SUMMARY
          Range  = 75.6707 deg <--> 148.2925 deg
          Mean   = 107.5675 deg
          StdDev = 24.2527 deg

        T--T SUMMARY
          Range  = 3.7821 A <--> 5.9427 A
          Mean   = 4.8838 A
          StdDev = 0.7339 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.866 deg ; T1  -- T1   3.1099 A

T1  -- O2  -- T2  = 135.636 deg ; T1  -- T2   3.0735 A

T1  -- O3  -- T2  = 147.405 deg ; T1  -- T2   3.1171 A

T2  -- O4  -- T2  = 146.873 deg ; T2  -- T2   3.0829 A


        T-O-T SUMMARY
          Range  = 135.6358° <--> 147.8661 deg
          Mean   = 144.4451 deg
          StdDev = 5.1797 deg

        T--T SUMMARY
          Range  = 3.0735 A <--> 3.1171 A
          Mean   = 3.0959 A
          StdDev = 0.0184 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

<TD10> = 840.000
Average ring size = 6.2609