Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_116_2_156542_gikZr6.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.79 T-atoms per nm^3
Material density = 1.775 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6198 Angstrom
T1  -- O2  = 1.6188 Angstrom
T1  -- O3  = 1.6100 Angstrom
T1  -- O1  = 1.6199 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.005012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002192  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6101 Angstrom
T2  -- O4  = 1.6198 Angstrom
T2  -- O5  = 1.6188 Angstrom
T2  -- O4  = 1.6198 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.005015  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001681  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6100 A <--> 1.6199 A
          Mean   = 1.6171 A
          StdDev = 0.0041 A

       t1 Range  = 0.0050 <-- 0.0050 --> 0.0050
       t2 Range  = 0.0017 <-- 0.0019 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.432 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.278 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.833 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.534 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.473 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.277 deg; O3  -- O1  = 3 A
       109.277 deg <-- 109.471 deg --> 109.833 deg

O3  -- T2  -- O4  = 109.280 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.536 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 109.271 deg; O3  -- O4  = 3 A
O4  -- T2  -- O5  = 109.447 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 109.836 deg; O4  -- O4  = 3 A
O5  -- T2  -- O4  = 109.457 deg; O5  -- O4  = 3 A
       109.271 deg <-- 109.471 deg --> 109.836 deg

        O-T-O SUMMARY
          Range  = 109.2707 deg <--> 109.8356 deg
          Mean   = 109.4712 deg
          StdDev = 0.1894 deg

        O--O SUMMARY
          Range  = 2.6340 A <--> 2.6511 A
          Mean   = 2.6408 A
          StdDev = 0.0062 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.000 deg; T1  -- T2  = 4.4690 A
T1  - O1  - T1  - O3  - T1  = 118.652 deg; T1  -- T1  = 5.3012 A
T1  - O1  - T1  - O1  - T1  = 118.619 deg; T1  -- T1  = 5.3003 A
T2  - O2  - T1  - O3  - T1  = 128.377 deg; T2  -- T1  = 5.6503 A
T2  - O2  - T1  - O1  - T1  = 128.345 deg; T2  -- T1  = 5.6495 A
T1  - O3  - T1  - O1  - T1  =  76.723 deg; T1  -- T1  = 3.7985 A

T1  - O3  - T2  - O4  - T2  =  90.000 deg; T1  -- T2  = 4.4690 A
T1  - O3  - T2  - O5  - T2  = 128.373 deg; T1  -- T2  = 5.6501 A
T1  - O3  - T2  - O4  - T2  = 128.348 deg; T1  -- T2  = 5.6495 A
T2  - O4  - T2  - O5  - T2  = 118.651 deg; T2  -- T2  = 5.3011 A
T2  - O4  - T2  - O4  - T2  = 118.622 deg; T2  -- T2  = 5.3003 A
T2  - O5  - T2  - O4  - T2  =  76.722 deg; T2  -- T2  = 3.7983 A

        T-T-T SUMMARY
          Range  = 76.7218 deg <--> 128.3773 deg
          Mean   = 110.1194 deg
          StdDev = 19.8128 deg

        T--T SUMMARY
          Range  = 3.7983 A <--> 5.6503 A
          Mean   = 5.0281 A
          StdDev = 0.6801 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 141.680 deg ; T1  -- T1   3.0602 A

T1  -- O2  -- T1  = 146.894 deg ; T1  -- T1   3.1033 A

T1  -- O3  -- T2  = 174.039 deg ; T1  -- T2   3.2158 A

T2  -- O4  -- T2  = 141.676 deg ; T2  -- T2   3.0602 A

T2  -- O5  -- T2  = 146.889 deg ; T2  -- T2   3.1033 A


        T-O-T SUMMARY
          Range  = 141.6760° <--> 174.0387 deg
          Mean   = 150.2357 deg
          StdDev = 12.2822 deg

        T--T SUMMARY
          Range  = 3.0602 A <--> 3.2158 A
          Mean   = 3.1086 A
          StdDev = 0.0577 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

<TD10> = 840.000
Average ring size = 6.2609