Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_114_2_9622_oF5SJo.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.19 T-atoms per nm^3
Material density = 2.214 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6249 Angstrom
T1  -- O1  = 1.6396 Angstrom
T1  -- O2  = 1.6228 Angstrom
T1  -- O3  = 1.6272 Angstrom
      mean = 1.6286 Angstrom
        t1 = 0.020695  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011560  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6220 Angstrom
T2  -- O4  = 1.6259 Angstrom
T2  -- O4  = 1.6417 Angstrom
T2  -- O3  = 1.6277 Angstrom
      mean = 1.6293 Angstrom
        t1 = 0.021350  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011274  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6220 A <--> 1.6417 A
          Mean   = 1.6290 A
          StdDev = 0.0071 A

       t1 Range  = 0.0207 <-- 0.0210 --> 0.0213
       t2 Range  = 0.0113 <-- 0.0114 --> 0.0116

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 107.065 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 108.894 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.573 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 108.768 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 115.183 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.194 deg; O2  -- O3  = 3 A
       107.065 deg <-- 109.446 deg --> 115.183 deg

O2  -- T2  -- O4  = 108.944 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 108.856 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 108.804 deg; O2  -- O3  = 3 A
O4  -- T2  -- O4  = 106.835 deg; O4  -- O4  = 3 A
O4  -- T2  -- O3  = 107.896 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 115.346 deg; O4  -- O3  = 3 A
       106.835 deg <-- 109.447 deg --> 115.346 deg

        O-T-O SUMMARY
          Range  = 106.8351 deg <--> 115.3464 deg
          Mean   = 109.4465 deg
          StdDev = 2.7217 deg

        O--O SUMMARY
          Range  = 2.6239 A <--> 2.7627 A
          Mean   = 2.6590 A
          StdDev = 0.0467 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  =  90.051 deg; T1  -- T2  = 4.1383 A
T1  - O1  - T1  - O2  - T2  = 135.834 deg; T1  -- T2  = 5.6561 A
T1  - O1  - T1  - O3  - T1  = 108.261 deg; T1  -- T1  = 4.6160 A
T2  - O1  - T1  - O2  - T2  = 129.984 deg; T2  -- T2  = 5.6681 A
T2  - O1  - T1  - O3  - T1  =  90.012 deg; T2  -- T1  = 4.1369 A
T2  - O2  - T1  - O3  - T1  =  91.675 deg; T2  -- T1  = 4.3863 A

T1  - O2  - T2  - O4  - T2  =  89.949 deg; T1  -- T2  = 4.1369 A
T1  - O2  - T2  - O4  - T1  = 129.631 deg; T1  -- T1  = 5.6599 A
T1  - O2  - T2  - O3  - T2  =  89.988 deg; T1  -- T2  = 4.1383 A
T2  - O4  - T2  - O4  - T1  = 136.174 deg; T2  -- T1  = 5.6660 A
T2  - O4  - T2  - O3  - T2  = 108.077 deg; T2  -- T2  = 4.6160 A
T1  - O4  - T2  - O3  - T2  =  91.958 deg; T1  -- T2  = 4.3989 A

        T-T-T SUMMARY
          Range  = 89.9490 deg <--> 136.1744 deg
          Mean   = 107.6328 deg
          StdDev = 19.1130 deg

        T--T SUMMARY
          Range  = 4.1369 A <--> 5.6681 A
          Mean   = 4.7682 A
          StdDev = 0.6565 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.489 deg ; T1  -- T1   2.8481 A

T1  -- O2  -- T2  = 135.178 deg ; T1  -- T2   2.9998 A

T1  -- O3  -- T2  = 176.708 deg ; T1  -- T2   3.2536 A

T2  -- O4  -- T2  = 121.535 deg ; T2  -- T2   2.8515 A


        T-O-T SUMMARY
          Range  = 121.4895° <--> 176.7079 deg
          Mean   = 138.7275 deg
          StdDev = 22.9887 deg

        T--T SUMMARY
          Range  = 2.8481 A <--> 3.2536 A
          Mean   = 2.9882 A
          StdDev = 0.1676 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 833.000
Average ring size = 5.3333