Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_114_2_5964_nQq7Gc.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.04 T-atoms per nm^3
Material density = 1.800 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O2  = 1.6098 Angstrom
T1  -- O1  = 1.6150 Angstrom
T1  -- O3  = 1.6105 Angstrom
      mean = 1.6126 Angstrom
        t1 = 0.003814  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005166  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O3  = 1.6099 Angstrom
T2  -- O4  = 1.6151 Angstrom
T2  -- O4  = 1.6152 Angstrom
      mean = 1.6125 Angstrom
        t1 = 0.003848  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002264  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6098 A <--> 1.6152 A
          Mean   = 1.6126 A
          StdDev = 0.0026 A

       t1 Range  = 0.0038 <-- 0.0038 --> 0.0038
       t2 Range  = 0.0023 <-- 0.0037 --> 0.0052

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.428 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 110.425 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 108.988 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  = 109.442 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 109.442 deg; O2  -- O3  = 3 A
O1  -- T1  -- O3  = 109.099 deg; O1  -- O3  = 3 A
       108.988 deg <-- 109.471 deg --> 110.425 deg

O2  -- T2  -- O3  = 109.433 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.365 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.520 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 108.997 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.085 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 110.423 deg; O4  -- O4  = 3 A
       108.997 deg <-- 109.471 deg --> 110.423 deg

        O-T-O SUMMARY
          Range  = 108.9879 deg <--> 110.4251 deg
          Mean   = 109.4705 deg
          StdDev = 0.4661 deg

        O--O SUMMARY
          Range  = 2.6255 A <--> 2.6529 A
          Mean   = 2.6333 A
          StdDev = 0.0092 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 110.067 deg; T2  -- T1  = 5.1999 A
T2  - O1  - T1  - O1  - T1  = 110.120 deg; T2  -- T1  = 5.2016 A
T2  - O1  - T1  - O3  - T2  = 109.481 deg; T2  -- T2  = 5.2586 A
T1  - O2  - T1  - O1  - T1  =  83.221 deg; T1  -- T1  = 4.1508 A
T1  - O2  - T1  - O3  - T2  = 120.705 deg; T1  -- T2  = 5.5151 A
T1  - O1  - T1  - O3  - T2  = 120.820 deg; T1  -- T2  = 5.5183 A

T1  - O2  - T2  - O3  - T1  = 109.479 deg; T1  -- T1  = 5.2585 A
T1  - O2  - T2  - O4  - T2  = 110.128 deg; T1  -- T2  = 5.2019 A
T1  - O2  - T2  - O4  - T2  = 110.076 deg; T1  -- T2  = 5.2002 A
T1  - O3  - T2  - O4  - T2  = 120.800 deg; T1  -- T2  = 5.5177 A
T1  - O3  - T2  - O4  - T2  = 120.717 deg; T1  -- T2  = 5.5155 A
T2  - O4  - T2  - O4  - T2  =  83.217 deg; T2  -- T2  = 4.1506 A

        T-T-T SUMMARY
          Range  = 83.2169 deg <--> 120.8201 deg
          Mean   = 109.0691 deg
          StdDev = 12.6084 deg

        T--T SUMMARY
          Range  = 4.1506 A <--> 5.5183 A
          Mean   = 5.1407 A
          StdDev = 0.4650 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 150.708 deg ; T1  -- T1   3.1253 A

T1  -- O2  -- T2  = 179.865 deg ; T1  -- T2   3.2197 A

T1  -- O3  -- T2  = 179.991 deg ; T1  -- T2   3.2204 A

T2  -- O4  -- T2  = 150.705 deg ; T2  -- T2   3.1253 A


        T-O-T SUMMARY
          Range  = 150.7050° <--> 179.9905 deg
          Mean   = 165.3173 deg
          StdDev = 14.8445 deg

        T--T SUMMARY
          Range  = 3.1253 A <--> 3.2204 A
          Mean   = 3.1727 A
          StdDev = 0.0481 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 915.000
Average ring size = 5.7391