Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_113_2_734_xiReLu.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 25.73 T-atoms per nm^3
Material density = 2.567 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6303 Angstrom
T1  -- O2  = 1.6107 Angstrom
T1  -- O1  = 1.6296 Angstrom
T1  -- O3  = 1.6675 Angstrom
      mean = 1.6345 Angstrom
        t1 = 0.032842  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019262  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6026 Angstrom
T2  -- O3  = 1.6331 Angstrom
T2  -- O4  = 1.6202 Angstrom
T2  -- O5  = 1.6235 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.008900  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005395  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6026 A <--> 1.6675 A
          Mean   = 1.6272 A
          StdDev = 0.0182 A

       t1 Range  = 0.0089 <-- 0.0209 --> 0.0328
       t2 Range  = 0.0054 <-- 0.0123 --> 0.0193

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.568 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 108.365 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 114.705 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  = 106.431 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 105.709 deg; O2  -- O3  = 3 A
O1  -- T1  -- O3  = 114.417 deg; O1  -- O3  = 3 A
       105.709 deg <-- 109.366 deg --> 114.705 deg

O2  -- T2  -- O3  = 108.276 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.406 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.454 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.788 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 110.003 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.888 deg; O4  -- O5  = 3 A
       108.276 deg <-- 109.469 deg --> 110.003 deg

        O-T-O SUMMARY
          Range  = 105.7091 deg <--> 114.7046 deg
          Mean   = 109.3970 deg
          StdDev = 2.7614 deg

        O--O SUMMARY
          Range  = 2.5952 A <--> 2.7768 A
          Mean   = 2.6558 A
          StdDev = 0.0589 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  95.824 deg; T2  -- T1  = 4.3907 A
T2  - O1  - T1  - O1  - T1  =  94.594 deg; T2  -- T1  = 4.3483 A
T2  - O1  - T1  - O3  - T2  = 107.252 deg; T2  -- T2  = 4.5218 A
T1  - O2  - T1  - O1  - T1  =  81.600 deg; T1  -- T1  = 4.1219 A
T1  - O2  - T1  - O3  - T2  = 134.496 deg; T1  -- T2  = 5.5512 A
T1  - O1  - T1  - O3  - T2  = 132.869 deg; T1  -- T2  = 5.5176 A

T1  - O2  - T2  - O3  - T2  = 114.927 deg; T1  -- T2  = 4.8697 A
T1  - O2  - T2  - O4  - T2  = 115.718 deg; T1  -- T2  = 4.8944 A
T1  - O2  - T2  - O5  - T1  = 107.252 deg; T1  -- T1  = 4.5218 A
T2  - O3  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.2773 A
T2  - O3  - T2  - O5  - T1  = 113.880 deg; T2  -- T1  = 4.9345 A
T2  - O4  - T2  - O5  - T1  = 114.634 deg; T2  -- T1  = 4.9588 A

        T-T-T SUMMARY
          Range  = 81.6002 deg <--> 134.4964 deg
          Mean   = 108.3243 deg
          StdDev = 15.7829 deg

        T--T SUMMARY
          Range  = 4.1219 A <--> 5.5512 A
          Mean   = 4.7329 A
          StdDev = 0.4527 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 150.729 deg ; T1  -- T1   3.1541 A

T1  -- O2  -- T2  = 117.780 deg ; T1  -- T2   2.7512 A

T1  -- O3  -- T2  = 120.404 deg ; T1  -- T2   2.8642 A

T2  -- O4  -- T2  = 137.746 deg ; T2  -- T2   3.0225 A

T2  -- O5  -- T2  = 137.525 deg ; T2  -- T2   3.0265 A


        T-O-T SUMMARY
          Range  = 117.7805° <--> 150.7289 deg
          Mean   = 132.8369 deg
          StdDev = 12.3826 deg

        T--T SUMMARY
          Range  = 2.7512 A <--> 3.1541 A
          Mean   = 2.9637 A
          StdDev = 0.1423 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7512 Angstrom
T2  -- T1  = 2.7512 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 959.000
Average ring size = 5.6000