Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_112_2_54144_ZJh9rN.cif"

There are 10 T-atoms per unit cell
There are 20 O-atoms per unit cell

Framework density = 22.86 T-atoms per nm^3
Material density = 2.281 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5814 Angstrom
T1  -- O2  = 1.6950 Angstrom
T1  -- O3  = 1.5484 Angstrom
T1  -- O4  = 1.6560 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.089420  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058386  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6440 Angstrom
T2  -- O4  = 1.6440 Angstrom
T2  -- O4  = 1.6440 Angstrom
T2  -- O4  = 1.6440 Angstrom
      mean = 1.6440 Angstrom
        t1 = 0.033097  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019536  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5484 A <--> 1.6950 A
          Mean   = 1.6250 A
          StdDev = 0.0536 A

       t1 Range  = 0.0331 <-- 0.0613 --> 0.0894
       t2 Range  = 0.0195 <-- 0.0390 --> 0.0584

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.052 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.111 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.847 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 102.051 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 135.693 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  93.474 deg; O3  -- O4  = 2 A
       93.474 deg <-- 109.038 deg --> 135.693 deg

O4  -- T2  -- O4  = 115.419 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 106.582 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 106.582 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 106.582 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 106.582 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 115.419 deg; O4  -- O4  = 3 A
       106.582 deg <-- 109.527 deg --> 115.419 deg

        O-T-O SUMMARY
          Range  = 93.4740 deg <--> 135.6931 deg
          Mean   = 109.6463 deg
          StdDev = 10.2849 deg

        O--O SUMMARY
          Range  = 2.3347 A <--> 3.1037 A
          Mean   = 2.6646 A
          StdDev = 0.1852 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 105.419 deg; T1  -- T2  = 4.4963 A
T1  - O1  - T1  - O3  - T1  =  63.451 deg; T1  -- T1  = 2.7965 A
T1  - O1  - T1  - O4  - T1  =  56.839 deg; T1  -- T1  = 2.6170 A
T2  - O2  - T1  - O3  - T1  = 109.233 deg; T2  -- T1  = 4.5421 A
T2  - O2  - T1  - O4  - T1  = 161.398 deg; T2  -- T1  = 5.6701 A
T1  - O3  - T1  - O4  - T1  =  59.710 deg; T1  -- T1  = 2.6993 A

T1  - O4  - T2  - O4  - T1  = 103.859 deg; T1  -- T1  = 4.6434 A
T1  - O4  - T2  - O4  - T1  = 112.348 deg; T1  -- T1  = 4.8999 A
T1  - O4  - T2  - O4  - T1  = 112.348 deg; T1  -- T1  = 4.8999 A
T1  - O4  - T2  - O4  - T1  = 112.348 deg; T1  -- T1  = 4.8999 A
T1  - O4  - T2  - O4  - T1  = 112.348 deg; T1  -- T1  = 4.8999 A
T1  - O4  - T2  - O4  - T1  = 103.859 deg; T1  -- T1  = 4.6434 A

        T-T-T SUMMARY
          Range  = 56.8388 deg <--> 161.3983 deg
          Mean   = 102.2961 deg
          StdDev = 28.7331 deg

        T--T SUMMARY
          Range  = 2.6170 A <--> 5.6701 A
          Mean   = 4.3610 A
          StdDev = 0.9860 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 111.675 deg ; T1  -- T1   2.6170 A

T1  -- O2  -- T1  = 111.165 deg ; T1  -- T1   2.7965 A

T1  -- O3  -- T1  = 121.300 deg ; T1  -- T1   2.6993 A

T1  -- O4  -- T2  = 126.672 deg ; T1  -- T2   2.9491 A


        T-O-T SUMMARY
          Range  = 111.1653° <--> 126.6724 deg
          Mean   = 117.7032 deg
          StdDev = 6.6715 deg

        T--T SUMMARY
          Range  = 2.6170 A <--> 2.9491 A
          Mean   = 2.7655 A
          StdDev = 0.1256 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6993 Angstrom
T1  -- T1  = 2.6170 Angstrom
T1  -- T1  = 2.7965 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 6 17 27 37 85 88 96 185 177 187 323 300 304 507 447
TD10 = 723
Circuit symbol = 3.6.3.7.3.7
Weight = 8
Vertex symbol  = 3.6.3.12_{2}.3.12_{8}
Weight = 54

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 10 28 68 42 100 156 90 204 292 162 356 460 250 540
TD10 = 715
Circuit symbol = 6.6.12_{7}.12_{7}.12_{7}.12_{7}
Weight = 99
Vertex symbol  = 6.6.12_{7}.12_{7}.12_{7}.12_{7}
Weight = 99

<TD10> = 721.400
Average ring size = 8.0625