Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_112_2_47345_wFxFJq.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 23.48 T-atoms per nm^3
Material density = 2.343 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6617 Angstrom
T1  -- O2  = 1.6404 Angstrom
T1  -- O3  = 1.6174 Angstrom
T1  -- O4  = 1.6319 Angstrom
      mean = 1.6378 Angstrom
        t1 = 0.040923  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026388  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6402 Angstrom
T2  -- O4  = 1.6173 Angstrom
T2  -- O5  = 1.6616 Angstrom
T2  -- O3  = 1.6321 Angstrom
      mean = 1.6378 Angstrom
        t1 = 0.040860  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049374  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6173 A <--> 1.6617 A
          Mean   = 1.6378 A
          StdDev = 0.0161 A

       t1 Range  = 0.0409 <-- 0.0409 --> 0.0409
       t2 Range  = 0.0264 <-- 0.0379 --> 0.0494

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 119.782 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.071 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.297 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 102.730 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.307 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 113.858 deg; O3  -- O4  = 3 A
       102.730 deg <-- 109.507 deg --> 119.782 deg

O2  -- T2  -- O4  = 102.741 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 119.759 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 106.289 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 106.086 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 113.869 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 108.301 deg; O5  -- O3  = 3 A
       102.741 deg <-- 109.508 deg --> 119.759 deg

        O-T-O SUMMARY
          Range  = 102.7296 deg <--> 119.7815 deg
          Mean   = 109.5075 deg
          StdDev = 5.7114 deg

        O--O SUMMARY
          Range  = 2.5448 A <--> 2.8566 A
          Mean   = 2.6721 A
          StdDev = 0.0991 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  81.883 deg; T2  -- T2  = 4.0727 A
T2  - O1  - T1  - O3  - T1  = 152.256 deg; T2  -- T1  = 5.8329 A
T2  - O1  - T1  - O4  - T2  =  81.889 deg; T2  -- T2  = 4.0727 A
T2  - O2  - T1  - O3  - T1  =  92.987 deg; T2  -- T1  = 4.0993 A
T2  - O2  - T1  - O4  - T2  = 133.082 deg; T2  -- T2  = 5.3604 A
T1  - O3  - T1  - O4  - T2  = 119.618 deg; T1  -- T2  = 4.8833 A

T1  - O2  - T2  - O4  - T1  =  81.883 deg; T1  -- T1  = 4.0724 A
T1  - O2  - T2  - O5  - T2  = 152.263 deg; T1  -- T2  = 5.8322 A
T1  - O2  - T2  - O3  - T1  =  81.878 deg; T1  -- T1  = 4.0724 A
T1  - O4  - T2  - O5  - T2  =  92.999 deg; T1  -- T2  = 4.0989 A
T1  - O4  - T2  - O3  - T1  = 133.082 deg; T1  -- T1  = 5.3604 A
T2  - O5  - T2  - O3  - T1  = 119.616 deg; T2  -- T1  = 4.8829 A

        T-T-T SUMMARY
          Range  = 81.8776 deg <--> 152.2628 deg
          Mean   = 110.2864 deg
          StdDev = 26.8516 deg

        T--T SUMMARY
          Range  = 4.0724 A <--> 5.8329 A
          Mean   = 4.7200 A
          StdDev = 0.6987 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 110.284 deg ; T1  -- T1   2.7270 A

T1  -- O2  -- T2  = 177.045 deg ; T1  -- T2   3.2795 A

T1  -- O3  -- T2  = 128.104 deg ; T1  -- T2   2.9219 A

T1  -- O4  -- T2  = 128.090 deg ; T1  -- T2   2.9215 A

T2  -- O5  -- T2  = 110.250 deg ; T2  -- T2   2.7263 A


        T-O-T SUMMARY
          Range  = 110.2496° <--> 177.0450 deg
          Mean   = 130.7544 deg
          StdDev = 24.7923 deg

        T--T SUMMARY
          Range  = 2.7263 A <--> 3.2795 A
          Mean   = 2.9152 A
          StdDev = 0.2045 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7270 Angstrom
T2  -- T2  = 2.7263 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 60 89 121 157 199 247 299 355 417 485 557 633
TD10 = 946
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{48}
Weight = 39

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 60 89 121 157 199 247 299 355 417 485 557 633
TD10 = 946
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{48}
Weight = 39

<TD10> = 946.000
Average ring size = 10.6000