Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_112_1_16_Hqt08_.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6882 Angstrom
T1  -- O2  = 1.9278 Angstrom
T1  -- O2  = 1.9279 Angstrom
T1  -- O3  = 1.4931 Angstrom
T1  -- O3  = 1.9330 Angstrom
T1  -- O3  = 1.8797 Angstrom
      mean = 1.8083 Angstrom

        T-O SUMMARY
          Range  = 1.4931 A <--> 1.9330 A
          Mean   = 1.8083 A
          StdDev = 0.1666 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  55.599 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  =  55.597 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 112.975 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 132.546 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  85.751 deg; O1  -- O3  = 2 A
O2  -- T1  -- O2  =  71.050 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  =  89.636 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  = 121.788 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 139.806 deg; O2  -- O3  = 4 A
O2  -- T1  -- O3  = 160.671 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  =  78.045 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  =  97.561 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  = 114.394 deg; O3  -- O3  = 3 A
O3  -- T1  -- O3  =  96.875 deg; O3  -- O3  = 3 A
O3  -- T1  -- O3  =  91.349 deg; O3  -- O3  = 3 A
       55.597 deg <-- 100.243 deg --> 160.671 deg

        O-T-O SUMMARY
          Range  = 55.5970 deg <--> 160.6714 deg
          Mean   = 104.6312 deg
          StdDev = 27.5601 deg

        O--O SUMMARY
          Range  = 1.6997 A <--> 3.5757 A
          Mean   = 2.7722 A
          StdDev = 0.5041 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 124.119 deg ; T1  -- T1   2.9828 A

T1  -- O2  -- T1  =  29.284 deg ; T1  -- T1   0.9746 A
T1  -- O2  -- T1  = 101.359 deg ; T1  -- T1   2.9828 A
T1  -- O2  -- T1  = 108.954 deg ; T1  -- T1   3.1380 A
T1  -- O2  -- T1  = 108.947 deg ; T1  -- T1   3.1380 A
T1  -- O2  -- T1  = 101.359 deg ; T1  -- T1   2.9828 A
T1  -- O2  -- T1  =  29.284 deg ; T1  -- T1   0.9746 A

T1  -- O3  -- T1  =  29.663 deg ; T1  -- T1   0.9746 A
T1  -- O3  -- T1  = 135.241 deg ; T1  -- T1   3.1222 A
T1  -- O3  -- T1  = 159.769 deg ; T1  -- T1   3.7534 A


        T-O-T SUMMARY
          Range  = 29.2842° <--> 159.7685 deg
          Mean   = 92.7979 deg
          StdDev = 44.9922 deg

        T--T SUMMARY
          Range  = 0.9746 A <--> 3.7534 A
          Mean   = 2.5024 A
          StdDev = 1.0288 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.6997 A
O1  -- O2  = 1.6997 A
O2  -- O2  = 2.2404 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 5 neighboring T-atoms within 3.50 A, but 6 bridging O-atoms
  T1  -- T1  = 0.9746 Angstrom
  T1  -- T1  = 2.9828 Angstrom
  T1  -- T1  = 3.1380 Angstrom
  T1  -- T1  = 3.1222 Angstrom
  T1  -- T1  = 3.1222 Angstrom