Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_111_2_4407_H0x7nD.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 16.11 T-atoms per nm^3
Material density = 1.607 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6159 Angstrom
T1  -- O2  = 1.6240 Angstrom
T1  -- O3  = 1.6240 Angstrom
T1  -- O4  = 1.6133 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.007047  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003414  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6137 Angstrom
T2  -- O5  = 1.6218 Angstrom
T2  -- O6  = 1.6218 Angstrom
T2  -- O7  = 1.6156 Angstrom
      mean = 1.6182 Angstrom
        t1 = 0.006968  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003041  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6133 A <--> 1.6240 A
          Mean   = 1.6188 A
          StdDev = 0.0043 A

       t1 Range  = 0.0070 <-- 0.0070 --> 0.0070
       t2 Range  = 0.0030 <-- 0.0032 --> 0.0034

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.825 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.825 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.890 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.364 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.463 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.460 deg; O3  -- O4  = 3 A
       108.825 deg <-- 109.471 deg --> 110.364 deg

O4  -- T2  -- O5  = 109.655 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.652 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 108.801 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.589 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.055 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.058 deg; O6  -- O7  = 3 A
       108.801 deg <-- 109.468 deg --> 110.589 deg

        O-T-O SUMMARY
          Range  = 108.8008 deg <--> 110.5885 deg
          Mean   = 109.4754 deg
          StdDev = 0.5095 deg

        O--O SUMMARY
          Range  = 2.6258 A <--> 2.6665 A
          Mean   = 2.6425 A
          StdDev = 0.0104 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 111.737 deg; T2  -- T1  = 5.0032 A
T2  - O1  - T1  - O3  - T1  =  98.309 deg; T2  -- T1  = 4.8364 A
T2  - O1  - T1  - O4  - T1  = 111.737 deg; T2  -- T1  = 5.0032 A
T1  - O2  - T1  - O3  - T1  =  82.694 deg; T1  -- T1  = 4.0461 A
T1  - O2  - T1  - O4  - T1  = 135.611 deg; T1  -- T1  = 5.3331 A
T1  - O3  - T1  - O4  - T1  =  82.694 deg; T1  -- T1  = 4.0461 A

T1  - O4  - T2  - O5  - T2  =  96.322 deg; T1  -- T2  = 4.7513 A
T1  - O4  - T2  - O6  - T2  = 123.638 deg; T1  -- T2  = 5.6303 A
T1  - O4  - T2  - O7  - T2  =  96.322 deg; T1  -- T2  = 4.7513 A
T2  - O5  - T2  - O6  - T2  = 113.281 deg; T2  -- T2  = 5.3805 A
T2  - O5  - T2  - O7  - T2  = 112.033 deg; T2  -- T2  = 5.3331 A
T2  - O6  - T2  - O7  - T2  = 113.281 deg; T2  -- T2  = 5.3805 A

        T-T-T SUMMARY
          Range  = 82.6945 deg <--> 135.6113 deg
          Mean   = 106.8881 deg
          StdDev = 16.2134 deg

        T--T SUMMARY
          Range  = 4.0461 A <--> 5.6303 A
          Mean   = 4.9450 A
          StdDev = 0.4960 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2318 A

T1  -- O2  -- T1  = 124.915 deg ; T1  -- T1   2.8799 A

T1  -- O3  -- T1  = 124.915 deg ; T1  -- T1   2.8799 A

T1  -- O4  -- T2  = 156.842 deg ; T1  -- T2   3.1613 A

T2  -- O5  -- T2  = 164.983 deg ; T2  -- T2   3.2158 A

T2  -- O6  -- T2  = 164.983 deg ; T2  -- T2   3.2158 A

T2  -- O7  -- T2  = 173.481 deg ; T2  -- T2   3.2260 A


        T-O-T SUMMARY
          Range  = 124.9147° <--> 180.0000 deg
          Mean   = 155.7312 deg
          StdDev = 20.8048 deg

        T--T SUMMARY
          Range  = 2.8799 A <--> 3.2318 A
          Mean   = 3.1158 A
          StdDev = 0.1520 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 16 32 56 69 87 127 170 212 252 270 325 408 476 524
TD10 = 784
Circuit symbol = 4.5.4.5.5_{2}.6_{2}
Weight = 12
Vertex symbol  = 4.5.4.5.5_{2}.*
Weight = 9

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 23 35 50 74 104 141 172 198 239 301 352 414 469 511
TD10 = 814
Circuit symbol = 5_{2}.6.5_{2}.6.6_{2}.8_{2}
Weight = 21
Vertex symbol  = 5_{2}.6.5_{2}.6.6.16_{6}
Weight = 46

<TD10> = 799.000
Average ring size = 6.3866