Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_111_2_26657_1sdLgF.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.03 T-atoms per nm^3
Material density = 2.298 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6401 Angstrom
T1  -- O2  = 1.6170 Angstrom
T1  -- O3  = 1.6307 Angstrom
T1  -- O4  = 1.6485 Angstrom
      mean = 1.6340 Angstrom
        t1 = 0.017076  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005309  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6211 Angstrom
T2  -- O5  = 1.5974 Angstrom
T2  -- O5  = 1.5974 Angstrom
T2  -- O4  = 1.6211 Angstrom
      mean = 1.6092 Angstrom
        t1 = 0.044165  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046309  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5974 A <--> 1.6485 A
          Mean   = 1.6258 A
          StdDev = 0.0168 A

       t1 Range  = 0.0171 <-- 0.0306 --> 0.0442
       t2 Range  = 0.0053 <-- 0.0258 --> 0.0463

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.621 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.056 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.966 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.025 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.033 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.133 deg; O3  -- O4  = 3 A
       108.025 deg <-- 109.472 deg --> 111.621 deg

O4  -- T2  -- O5  = 101.867 deg; O4  -- O5  = 2 A
O4  -- T2  -- O5  = 119.345 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 105.447 deg; O4  -- O4  = 3 A
O5  -- T2  -- O5  = 109.893 deg; O5  -- O5  = 3 A
O5  -- T2  -- O4  = 119.345 deg; O5  -- O4  = 3 A
O5  -- T2  -- O4  = 101.867 deg; O5  -- O4  = 2 A
       101.867 deg <-- 109.627 deg --> 119.345 deg

        O-T-O SUMMARY
          Range  = 101.8667 deg <--> 119.3454 deg
          Mean   = 109.5300 deg
          StdDev = 5.7916 deg

        O--O SUMMARY
          Range  = 2.4989 A <--> 2.7781 A
          Mean   = 2.6458 A
          StdDev = 0.0941 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  88.995 deg; T1  -- T2  = 4.2640 A
T1  - O1  - T1  - O3  - T1  = 113.258 deg; T1  -- T1  = 5.4317 A
T1  - O1  - T1  - O4  - T1  = 113.444 deg; T1  -- T1  = 5.4171 A
T2  - O2  - T1  - O3  - T1  =  87.500 deg; T2  -- T1  = 4.2169 A
T2  - O2  - T1  - O4  - T1  = 138.763 deg; T2  -- T1  = 5.6705 A
T1  - O3  - T1  - O4  - T1  = 111.813 deg; T1  -- T1  = 5.3763 A

T1  - O4  - T2  - O5  - T2  = 151.375 deg; T1  -- T2  = 5.7848 A
T1  - O4  - T2  - O5  - T2  =  91.005 deg; T1  -- T2  = 4.2640 A
T1  - O4  - T2  - O4  - T1  = 101.445 deg; T1  -- T1  = 4.3702 A
T2  - O5  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.4502 A
T2  - O5  - T2  - O4  - T1  =  91.005 deg; T2  -- T1  = 4.2640 A
T2  - O5  - T2  - O4  - T1  = 151.375 deg; T2  -- T1  = 5.7848 A

        T-T-T SUMMARY
          Range  = 87.4999 deg <--> 151.3747 deg
          Mean   = 114.0100 deg
          StdDev = 23.7694 deg

        T--T SUMMARY
          Range  = 4.2169 A <--> 5.7848 A
          Mean   = 5.0113 A
          StdDev = 0.6597 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 166.765 deg ; T1  -- T1   3.2583 A

T1  -- O2  -- T1  = 179.365 deg ; T1  -- T1   3.2339 A

T1  -- O3  -- T1  = 168.749 deg ; T1  -- T1   3.2457 A

T1  -- O4  -- T2  = 119.391 deg ; T1  -- T2   2.8228 A

T2  -- O5  -- T2  = 160.107 deg ; T2  -- T2   3.1468 A


        T-O-T SUMMARY
          Range  = 119.3908° <--> 179.3652 deg
          Mean   = 158.7385 deg
          StdDev = 22.1128 deg

        T--T SUMMARY
          Range  = 2.8228 A <--> 3.2583 A
          Mean   = 3.1409 A
          StdDev = 0.1754 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 43 69 101 138 180 225 277 336 401 473 545 623 709
TD10 = 1073
Circuit symbol = 4.6.6.6.6.8_{3}
Weight = 22
Vertex symbol  = 4.6.6.6.6.8_{2}
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 9 21 44 72 102 135 175 226 282 340 399 463 542 630 718
TD10 = 1071
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.10_{4}.10_{4}
Weight = 41

<TD10> = 1072.333
Average ring size = 6.4198