Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_111_2_23096_PRDuJo.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.88 T-atoms per nm^3
Material density = 2.283 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6153 Angstrom
T1  -- O3  = 1.5459 Angstrom
T1  -- O4  = 1.7290 Angstrom
T1  -- O2  = 1.6812 Angstrom
      mean = 1.6428 Angstrom
        t1 = 0.075879  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050123  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.7290 Angstrom
T2  -- O5  = 1.6154 Angstrom
T2  -- O6  = 1.6812 Angstrom
T2  -- O7  = 1.5459 Angstrom
      mean = 1.6429 Angstrom
        t1 = 0.075865  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.092687  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5459 A <--> 1.7290 A
          Mean   = 1.6428 A
          StdDev = 0.0696 A

       t1 Range  = 0.0759 <-- 0.0759 --> 0.0759
       t2 Range  = 0.0501 <-- 0.0714 --> 0.0927

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  =  99.564 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 110.529 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 113.322 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 104.541 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 101.136 deg; O3  -- O2  = 2 A
O4  -- T1  -- O2  = 123.729 deg; O4  -- O2  = 3 A
       99.564 deg <-- 108.804 deg --> 123.729 deg

O4  -- T2  -- O5  = 110.527 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 123.730 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 104.556 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 113.308 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  99.575 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 101.132 deg; O6  -- O7  = 2 A
       99.575 deg <-- 108.805 deg --> 123.730 deg

        O-T-O SUMMARY
          Range  = 99.5637 deg <--> 123.7305 deg
          Mean   = 110.1812 deg
          StdDev = 8.4593 deg

        O--O SUMMARY
          Range  = 2.4143 A <--> 3.0073 A
          Mean   = 2.7067 A
          StdDev = 0.1967 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  =  90.000 deg; T1  -- T2  = 4.5918 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3951 A
T1  - O1  - T1  - O2  - T1  =  91.398 deg; T1  -- T1  = 4.2817 A
T2  - O3  - T1  - O4  - T1  = 140.194 deg; T2  -- T1  = 6.2296 A
T2  - O3  - T1  - O2  - T1  = 131.190 deg; T2  -- T1  = 5.8252 A
T1  - O4  - T1  - O2  - T1  =  88.602 deg; T1  -- T1  = 4.2817 A

T1  - O4  - T2  - O5  - T2  = 131.190 deg; T1  -- T2  = 5.8252 A
T1  - O4  - T2  - O6  - T2  = 140.194 deg; T1  -- T2  = 6.2296 A
T1  - O4  - T2  - O7  - T2  =  90.000 deg; T1  -- T2  = 4.5918 A
T2  - O5  - T2  - O6  - T2  =  88.602 deg; T2  -- T2  = 4.2817 A
T2  - O5  - T2  - O7  - T2  =  91.398 deg; T2  -- T2  = 4.2817 A
T2  - O6  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3951 A

        T-T-T SUMMARY
          Range  = 88.6021 deg <--> 140.1936 deg
          Mean   = 107.9414 deg
          StdDev = 22.9918 deg

        T--T SUMMARY
          Range  = 4.2817 A <--> 6.2296 A
          Mean   = 5.0424 A
          StdDev = 0.8302 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.624 deg ; T1  -- T1   2.9470 A

T1  -- O2  -- T1  = 141.970 deg ; T1  -- T1   3.1789 A

T1  -- O3  -- T1  = 158.032 deg ; T1  -- T1   3.0351 A

T1  -- O4  -- T2  = 170.382 deg ; T1  -- T2   3.4457 A

T2  -- O5  -- T2  = 131.619 deg ; T2  -- T2   2.9470 A

T2  -- O6  -- T2  = 141.954 deg ; T2  -- T2   3.1789 A

T2  -- O7  -- T2  = 158.022 deg ; T2  -- T2   3.0351 A


        T-O-T SUMMARY
          Range  = 131.6187° <--> 170.3818 deg
          Mean   = 147.6575 deg
          StdDev = 13.8072 deg

        T--T SUMMARY
          Range  = 2.9470 A <--> 3.4457 A
          Mean   = 3.1097 A
          StdDev = 0.1647 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 13 21 34 52 71 90 115 147 178 207 243 287 331 373
TD10 = 556
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12_{2}
Weight = 33

<TD10> = 556.000
Average ring size = 5.6000