Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_111_2_23093_N_ni5r.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.10 T-atoms per nm^3
Material density = 1.906 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6232 Angstrom
T1  -- O3  = 1.5776 Angstrom
T1  -- O4  = 1.6421 Angstrom
T1  -- O2  = 1.6647 Angstrom
      mean = 1.6269 Angstrom
        t1 = 0.027546  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016168  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6321 Angstrom
T2  -- O5  = 1.6134 Angstrom
T2  -- O6  = 1.6448 Angstrom
T2  -- O7  = 1.6112 Angstrom
      mean = 1.6254 Angstrom
        t1 = 0.025854  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032009  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5776 A <--> 1.6647 A
          Mean   = 1.6261 A
          StdDev = 0.0249 A

       t1 Range  = 0.0259 <-- 0.0267 --> 0.0275
       t2 Range  = 0.0162 <-- 0.0241 --> 0.0320

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 107.646 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.425 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 110.580 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 107.066 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 107.813 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 114.048 deg; O4  -- O2  = 3 A
       107.066 deg <-- 109.430 deg --> 114.048 deg

O4  -- T2  -- O5  = 103.756 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 115.484 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.095 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.661 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.200 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.536 deg; O6  -- O7  = 3 A
       103.756 deg <-- 109.455 deg --> 115.484 deg

        O-T-O SUMMARY
          Range  = 103.7555 deg <--> 115.4843 deg
          Mean   = 109.5658 deg
          StdDev = 3.3568 deg

        O--O SUMMARY
          Range  = 2.5533 A <--> 2.7741 A
          Mean   = 2.6583 A
          StdDev = 0.0727 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  =  89.241 deg; T1  -- T2  = 4.3031 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4577 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.3186 A
T2  - O3  - T1  - O4  - T1  = 119.000 deg; T2  -- T1  = 5.2770 A
T2  - O3  - T1  - O2  - T1  = 150.988 deg; T2  -- T1  = 5.7347 A
T1  - O4  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.3186 A

T1  - O4  - T2  - O5  - T2  = 136.544 deg; T1  -- T2  = 5.7830 A
T1  - O4  - T2  - O6  - T2  =  90.759 deg; T1  -- T2  = 4.3031 A
T1  - O4  - T2  - O7  - T2  = 104.972 deg; T1  -- T2  = 4.4634 A
T2  - O5  - T2  - O6  - T2  = 127.767 deg; T2  -- T2  = 5.6808 A
T2  - O5  - T2  - O7  - T2  =  72.145 deg; T2  -- T2  = 3.5097 A
T2  - O6  - T2  - O7  - T2  = 123.947 deg; T2  -- T2  = 5.0563 A

        T-T-T SUMMARY
          Range  = 72.1449 deg <--> 150.9880 deg
          Mean   = 106.4800 deg
          StdDev = 21.4848 deg

        T--T SUMMARY
          Range  = 3.5097 A <--> 5.7830 A
          Mean   = 4.7671 A
          StdDev = 0.6563 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.832 deg ; T1  -- T1   2.9521 A

T1  -- O2  -- T1  = 142.438 deg ; T1  -- T1   3.1520 A

T1  -- O3  -- T1  = 174.949 deg ; T1  -- T1   3.1520 A

T1  -- O4  -- T2  = 130.327 deg ; T1  -- T2   2.9714 A

T2  -- O5  -- T2  = 110.428 deg ; T2  -- T2   2.6502 A

T2  -- O6  -- T2  = 162.827 deg ; T2  -- T2   3.2528 A

T2  -- O7  -- T2  = 145.023 deg ; T2  -- T2   3.0734 A


        T-O-T SUMMARY
          Range  = 110.4281° <--> 174.9494 deg
          Mean   = 142.4036 deg
          StdDev = 20.1282 deg

        T--T SUMMARY
          Range  = 2.6502 A <--> 3.2528 A
          Mean   = 3.0291 A
          StdDev = 0.1849 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.6502 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 27 50 78 104 132 171 219 263 300 350 421 490 547
TD10 = 808
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.10_{4}
Weight = 20

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 33 50 75 105 136 171 210 256 309 361 415 476 544
TD10 = 815
Circuit symbol = 4.4.6.8.6.8_{2}
Weight = 18
Vertex symbol  = 4.4.6.8.6.10_{2}
Weight = 25

<TD10> = 811.500
Average ring size = 5.8716