Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_111_2_19907_A9At4l.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.18 T-atoms per nm^3
Material density = 1.914 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6124 Angstrom
T1  -- O2  = 1.6450 Angstrom
T1  -- O3  = 1.6084 Angstrom
T1  -- O4  = 1.6284 Angstrom
      mean = 1.6235 Angstrom
        t1 = 0.027405  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016580  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6219 Angstrom
T2  -- O7  = 1.6461 Angstrom
T2  -- O4  = 1.6358 Angstrom
T2  -- O6  = 1.6057 Angstrom
      mean = 1.6274 Angstrom
        t1 = 0.021180  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011614  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6057 A <--> 1.6461 A
          Mean   = 1.6255 A
          StdDev = 0.0151 A

       t1 Range  = 0.0212 <-- 0.0243 --> 0.0274
       t2 Range  = 0.0116 <-- 0.0141 --> 0.0166

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.782 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.229 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 103.460 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.187 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 116.201 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.870 deg; O3  -- O4  = 3 A
       103.460 deg <-- 109.455 deg --> 116.201 deg

O5  -- T2  -- O7  = 110.753 deg; O5  -- O7  = 3 A
O5  -- T2  -- O4  = 108.891 deg; O5  -- O4  = 3 A
O5  -- T2  -- O6  = 108.065 deg; O5  -- O6  = 3 A
O7  -- T2  -- O4  = 113.652 deg; O7  -- O4  = 3 A
O7  -- T2  -- O6  = 107.982 deg; O7  -- O6  = 3 A
O4  -- T2  -- O6  = 107.296 deg; O4  -- O6  = 3 A
       107.296 deg <-- 109.440 deg --> 113.652 deg

        O-T-O SUMMARY
          Range  = 103.4599 deg <--> 116.2006 deg
          Mean   = 109.5410 deg
          StdDev = 3.4943 deg

        O--O SUMMARY
          Range  = 2.5443 A <--> 2.7790 A
          Mean   = 2.6557 A
          StdDev = 0.0677 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 124.175 deg; T1  -- T1  = 5.0546 A
T1  - O1  - T1  - O3  - T2  =  91.255 deg; T1  -- T2  = 4.3149 A
T1  - O1  - T1  - O4  - T1  = 127.934 deg; T1  -- T1  = 5.6823 A
T1  - O2  - T1  - O3  - T2  = 102.550 deg; T1  -- T2  = 4.3886 A
T1  - O2  - T1  - O4  - T1  =  72.534 deg; T1  -- T1  = 3.5283 A
T2  - O3  - T1  - O4  - T1  = 136.644 deg; T2  -- T1  = 5.7874 A

T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3656 A
T2  - O5  - T2  - O4  - T1  = 121.114 deg; T2  -- T1  = 5.1758 A
T2  - O5  - T2  - O6  - T2  =  92.115 deg; T2  -- T2  = 4.3113 A
T2  - O7  - T2  - O4  - T1  =  88.745 deg; T2  -- T1  = 4.3149 A
T2  - O7  - T2  - O6  - T2  =  87.885 deg; T2  -- T2  = 4.3113 A
T1  - O4  - T2  - O6  - T2  = 146.597 deg; T1  -- T2  = 5.7311 A

        T-T-T SUMMARY
          Range  = 72.5343 deg <--> 146.5973 deg
          Mean   = 109.7287 deg
          StdDev = 24.3394 deg

        T--T SUMMARY
          Range  = 3.5283 A <--> 5.7874 A
          Mean   = 4.8437 A
          StdDev = 0.7628 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 110.504 deg ; T1  -- T1   2.6497 A

T1  -- O2  -- T1  = 163.791 deg ; T1  -- T1   3.2571 A

T1  -- O3  -- T1  = 144.777 deg ; T1  -- T1   3.0661 A

T1  -- O4  -- T2  = 130.947 deg ; T1  -- T2   2.9697 A

T2  -- O5  -- T2  = 136.594 deg ; T2  -- T2   3.0138 A

T2  -- O6  -- T2  = 168.857 deg ; T2  -- T2   3.1962 A

T2  -- O7  -- T2  = 129.180 deg ; T2  -- T2   2.9738 A


        T-O-T SUMMARY
          Range  = 110.5037° <--> 168.8565 deg
          Mean   = 140.6642 deg
          StdDev = 19.0658 deg

        T--T SUMMARY
          Range  = 2.6497 A <--> 3.2571 A
          Mean   = 3.0180 A
          StdDev = 0.1834 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6497 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 33 50 75 105 136 171 210 256 309 361 415 476 544
TD10 = 815
Circuit symbol = 4.4.6.8.6.8_{2}
Weight = 18
Vertex symbol  = 4.4.6.8.6.10_{2}
Weight = 25

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 27 50 78 104 132 171 219 263 300 350 421 490 547
TD10 = 808
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.10_{4}
Weight = 20

<TD10> = 811.500
Average ring size = 5.8716