Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_111_1_11_di5Z3v.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8618 Angstrom
T1  -- O1  = 1.8641 Angstrom
T1  -- O2  = 1.8587 Angstrom
T1  -- O2  = 1.8610 Angstrom
T1  -- O3  = 1.5950 Angstrom
T1  -- O4  = 1.9380 Angstrom
      mean = 1.8298 Angstrom

        T-O SUMMARY
          Range  = 1.5950 A <--> 1.9380 A
          Mean   = 1.8298 A
          StdDev = 0.1098 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  75.018 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  89.761 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 136.628 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 142.113 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 124.807 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 136.625 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  89.620 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 141.888 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  80.851 deg; O1  -- O4  = 2 A
O2  -- T1  -- O2  =  73.932 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  =  67.920 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 137.674 deg; O2  -- O4  = 4 A
O2  -- T1  -- O3  =  67.860 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  =  91.051 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  69.761 deg; O3  -- O4  = 2 A
       67.860 deg <-- 101.701 deg --> 142.113 deg

        O-T-O SUMMARY
          Range  = 67.8599 deg <--> 142.1132 deg
          Mean   = 101.7006 deg
          StdDev = 29.8493 deg

        O--O SUMMARY
          Range  = 1.9416 A <--> 3.5407 A
          Mean   = 2.7484 A
          StdDev = 0.5807 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 105.074 deg ; T1  -- T1   2.9556 A
T1  -- O1  -- T1  =  43.331 deg ; T1  -- T1   1.3756 A
T1  -- O1  -- T1  =  89.193 deg ; T1  -- T1   2.6160 A
T1  -- O1  -- T1  =  89.193 deg ; T1  -- T1   2.6160 A
T1  -- O1  -- T1  =  43.331 deg ; T1  -- T1   1.3756 A
T1  -- O1  -- T1  = 104.889 deg ; T1  -- T1   2.9556 A

T1  -- O2  -- T1  =  90.187 deg ; T1  -- T1   2.6345 A
T1  -- O2  -- T1  =  43.408 deg ; T1  -- T1   1.3756 A
T1  -- O2  -- T1  = 106.162 deg ; T1  -- T1   2.9720 A
T1  -- O2  -- T1  = 105.975 deg ; T1  -- T1   2.9720 A
T1  -- O2  -- T1  =  43.408 deg ; T1  -- T1   1.3756 A
T1  -- O2  -- T1  =  90.187 deg ; T1  -- T1   2.6345 A

T1  -- O3  -- T1  = 111.350 deg ; T1  -- T1   2.6345 A

T1  -- O4  -- T1  = 158.934 deg ; T1  -- T1   3.8107 A


        T-O-T SUMMARY
          Range  = 43.3312° <--> 158.9337 deg
          Mean   = 87.4730 deg
          StdDev = 32.6406 deg

        T--T SUMMARY
          Range  = 1.3756 A <--> 3.8107 A
          Mean   = 2.4503 A
          StdDev = 0.7441 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.2687 A
O2  -- O2  = 2.2368 A
O2  -- O3  = 1.9416 A
O2  -- O3  = 1.9416 A
O3  -- O4  = 2.0399 A
O3  -- O4  = 2.0399 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 5 neighboring T-atoms within 3.50 A, but 6 bridging O-atoms
  T1  -- T1  = 2.6345 Angstrom
  T1  -- T1  = 2.9556 Angstrom
  T1  -- T1  = 1.3756 Angstrom
  T1  -- T1  = 2.9720 Angstrom
  T1  -- T1  = 2.6160 Angstrom