Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_110_2_9913_7zC1RX.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 24.62 T-atoms per nm^3
Material density = 2.456 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5979 Angstrom
T1  -- O3  = 1.6269 Angstrom
T1  -- O4  = 1.6248 Angstrom
T1  -- O2  = 1.6176 Angstrom
      mean = 1.6168 Angstrom
        t1 = 0.013468  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008245  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.5984 Angstrom
T2  -- O2  = 1.6179 Angstrom
T2  -- O3  = 1.6252 Angstrom
T2  -- O4  = 1.6263 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.013415  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008149  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5979 A <--> 1.6269 A
          Mean   = 1.6169 A
          StdDev = 0.0114 A

       t1 Range  = 0.0134 <-- 0.0134 --> 0.0135
       t2 Range  = 0.0081 <-- 0.0082 --> 0.0082

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.662 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.574 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 106.310 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.277 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 110.802 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 111.169 deg; O4  -- O2  = 3 A
       106.310 deg <-- 109.466 deg --> 111.169 deg

O1  -- T2  -- O2  = 106.317 deg; O1  -- O2  = 3 A
O1  -- T2  -- O3  = 109.603 deg; O1  -- O3  = 3 A
O1  -- T2  -- O4  = 109.631 deg; O1  -- O4  = 3 A
O2  -- T2  -- O3  = 111.241 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 110.713 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.288 deg; O3  -- O4  = 3 A
       106.317 deg <-- 109.466 deg --> 111.241 deg

        O-T-O SUMMARY
          Range  = 106.3101 deg <--> 111.2412 deg
          Mean   = 109.4655 deg
          StdDev = 1.5702 deg

        O--O SUMMARY
          Range  = 2.5733 A <--> 2.6766 A
          Mean   = 2.6401 A
          StdDev = 0.0337 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 138.699 deg; T2  -- T2  = 5.6870 A
T2  - O1  - T1  - O4  - T2  =  95.618 deg; T2  -- T2  = 4.5036 A
T2  - O1  - T1  - O2  - T2  = 102.527 deg; T2  -- T2  = 4.7742 A
T2  - O3  - T1  - O4  - T2  =  83.657 deg; T2  -- T2  = 4.0646 A
T2  - O3  - T1  - O2  - T2  = 114.335 deg; T2  -- T2  = 5.1565 A
T2  - O4  - T1  - O2  - T2  = 117.715 deg; T2  -- T2  = 5.2532 A

T1  - O1  - T2  - O2  - T1  = 102.555 deg; T1  -- T1  = 4.7751 A
T1  - O1  - T2  - O3  - T1  =  95.647 deg; T1  -- T1  = 4.5039 A
T1  - O1  - T2  - O4  - T1  = 138.720 deg; T1  -- T1  = 5.6883 A
T1  - O2  - T2  - O3  - T1  = 117.747 deg; T1  -- T1  = 5.2532 A
T1  - O2  - T2  - O4  - T1  = 114.300 deg; T1  -- T1  = 5.1563 A
T1  - O3  - T2  - O4  - T1  =  83.583 deg; T1  -- T1  = 4.0617 A

        T-T-T SUMMARY
          Range  = 83.5831 deg <--> 138.7201 deg
          Mean   = 108.7586 deg
          StdDev = 17.6117 deg

        T--T SUMMARY
          Range  = 4.0617 A <--> 5.6883 A
          Mean   = 4.9065 A
          StdDev = 0.5311 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 142.938 deg ; T1  -- T2   3.0306 A

T1  -- O2  -- T2  = 145.476 deg ; T1  -- T2   3.0898 A

T1  -- O3  -- T2  = 139.073 deg ; T1  -- T2   3.0469 A

T1  -- O4  -- T2  = 139.272 deg ; T1  -- T2   3.0479 A


        T-O-T SUMMARY
          Range  = 139.0730° <--> 145.4762 deg
          Mean   = 141.6898 deg
          StdDev = 2.6947 deg

        T--T SUMMARY
          Range  = 3.0306 A <--> 3.0898 A
          Mean   = 3.0538 A
          StdDev = 0.0221 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 24 43 68 102 139 183 230 283 343 410 479 555 638 727
TD10 = 1088
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 1088.000
Average ring size = 5.6000