Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_110_2_4626_lSf8He.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 27.77 T-atoms per nm^3
Material density = 2.770 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6781 Angstrom
T1  -- O1  = 1.7137 Angstrom
T1  -- O3  = 1.6113 Angstrom
T1  -- O4  = 1.6591 Angstrom
      mean = 1.6656 Angstrom
        t1 = 0.076285  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046238  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6136 Angstrom
T2  -- O3  = 1.6198 Angstrom
T2  -- O5  = 1.4995 Angstrom
T2  -- O4  = 1.6515 Angstrom
      mean = 1.5961 Angstrom
        t1 = 0.084641  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.072817  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4995 A <--> 1.7137 A
          Mean   = 1.6308 A
          StdDev = 0.0598 A

       t1 Range  = 0.0763 <-- 0.0805 --> 0.0846
       t2 Range  = 0.0462 <-- 0.0595 --> 0.0728

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O1  = 115.395 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 115.310 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.393 deg; O2  -- O4  = 3 A
O1  -- T1  -- O3  = 103.109 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 121.446 deg; O1  -- O4  = 3 A
O3  -- T1  -- O4  =  93.406 deg; O3  -- O4  = 2 A
       93.406 deg <-- 109.176 deg --> 121.446 deg

O2  -- T2  -- O3  = 118.925 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  =  99.843 deg; O2  -- O5  = 2 A
O2  -- T2  -- O4  = 117.758 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 116.544 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 110.735 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  =  88.664 deg; O5  -- O4  = 2 A
       88.664 deg <-- 108.745 deg --> 118.925 deg

        O-T-O SUMMARY
          Range  = 88.6637 deg <--> 121.4458 deg
          Mean   = 108.9606 deg
          StdDev = 10.2444 deg

        O--O SUMMARY
          Range  = 2.2047 A <--> 2.9421 A
          Mean   = 2.6466 A
          StdDev = 0.2117 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O2  - T1  - O1  - T1  =  80.293 deg; T2  -- T1  = 4.0341 A
T2  - O2  - T1  - O3  - T2  = 136.271 deg; T2  -- T2  = 5.1669 A
T2  - O2  - T1  - O4  - T2  = 116.484 deg; T2  -- T2  = 5.1676 A
T1  - O1  - T1  - O3  - T2  =  87.822 deg; T1  -- T2  = 4.1750 A
T1  - O1  - T1  - O4  - T2  = 144.668 deg; T1  -- T2  = 6.1827 A
T2  - O3  - T1  - O4  - T2  =  97.263 deg; T2  -- T2  = 4.3786 A

T1  - O2  - T2  - O3  - T1  = 109.775 deg; T1  -- T1  = 4.5559 A
T1  - O2  - T2  - O5  - T2  =  88.946 deg; T1  -- T2  = 4.0341 A
T1  - O2  - T2  - O4  - T1  = 134.245 deg; T1  -- T1  = 5.5985 A
T1  - O3  - T2  - O5  - T2  = 132.899 deg; T1  -- T2  = 5.0420 A
T1  - O3  - T2  - O4  - T1  = 109.415 deg; T1  -- T1  = 4.7572 A
T2  - O5  - T2  - O4  - T1  =  81.270 deg; T2  -- T1  = 3.9205 A

        T-T-T SUMMARY
          Range  = 80.2926 deg <--> 144.6685 deg
          Mean   = 109.9460 deg
          StdDev = 22.1407 deg

        T--T SUMMARY
          Range  = 3.9205 A <--> 6.1827 A
          Mean   = 4.7511 A
          StdDev = 0.6742 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 151.957 deg ; T1  -- T1   3.3253 A

T1  -- O2  -- T2  = 124.432 deg ; T1  -- T2   2.9124 A

T1  -- O3  -- T2  = 110.449 deg ; T1  -- T2   2.6541 A

T1  -- O4  -- T2  = 145.668 deg ; T1  -- T2   3.1632 A

T2  -- O5  -- T2  = 143.174 deg ; T2  -- T2   2.8454 A


        T-O-T SUMMARY
          Range  = 110.4488° <--> 151.9568 deg
          Mean   = 135.1359 deg
          StdDev = 15.4756 deg

        T--T SUMMARY
          Range  = 2.6541 A <--> 3.3253 A
          Mean   = 2.9801 A
          StdDev = 0.2389 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O5  = 2.2047 A
T1  -- T2  = 2.6541 Angstrom
T2  -- T1  = 2.6541 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 27 51 80 122 169 225 289 360 438 519 614 718 826 938
TD10 = 1339
Circuit symbol = 4.6.6.7_{2}.6.7_{3}
Weight = 22
Vertex symbol  = 4.6.6.7_{2}.6.7_{3}
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 27 47 82 120 167 227 284 364 432 520 612 716 829 939
TD10 = 1334
Circuit symbol = 4.6.6.7_{2}.6.7_{3}
Weight = 24
Vertex symbol  = 4.6.6.7_{2}.6.7_{3}
Weight = 24

<TD10> = 1336.500
Average ring size = 6.1463