Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_684_BKLxUB.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 21.32 T-atoms per nm^3
Material density = 2.127 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6201 Angstrom
T1  -- O2  = 1.6243 Angstrom
T1  -- O4  = 1.6313 Angstrom
T1  -- O3  = 1.6304 Angstrom
      mean = 1.6265 Angstrom
        t1 = 0.013080  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005171  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6199 Angstrom
T2  -- O3  = 1.6300 Angstrom
T2  -- O4  = 1.6322 Angstrom
T2  -- O5  = 1.6211 Angstrom
      mean = 1.6258 Angstrom
        t1 = 0.013402  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007403  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6199 A <--> 1.6322 A
          Mean   = 1.6262 A
          StdDev = 0.0051 A

       t1 Range  = 0.0131 <-- 0.0132 --> 0.0134
       t2 Range  = 0.0052 <-- 0.0063 --> 0.0074

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.382 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.677 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.506 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 108.115 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 108.318 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 111.796 deg; O4  -- O3  = 3 A
       108.115 deg <-- 109.466 deg --> 111.796 deg

O2  -- T2  -- O3  = 108.258 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.253 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.430 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 112.024 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.056 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.776 deg; O4  -- O5  = 3 A
       108.253 deg <-- 109.466 deg --> 112.024 deg

        O-T-O SUMMARY
          Range  = 108.1150 deg <--> 112.0238 deg
          Mean   = 109.4659 deg
          StdDev = 1.2501 deg

        O--O SUMMARY
          Range  = 2.6336 A <--> 2.7049 A
          Mean   = 2.6553 A
          StdDev = 0.0232 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  90.518 deg; T2  -- T2  = 4.2453 A
T2  - O1  - T1  - O4  - T2  =  89.327 deg; T2  -- T2  = 4.1979 A
T2  - O1  - T1  - O3  - T1  = 109.543 deg; T2  -- T1  = 4.9949 A
T2  - O2  - T1  - O4  - T2  = 136.220 deg; T2  -- T2  = 5.4023 A
T2  - O2  - T1  - O3  - T1  = 110.578 deg; T2  -- T1  = 4.9057 A
T2  - O4  - T1  - O3  - T1  = 110.616 deg; T2  -- T1  = 4.9027 A

T1  - O2  - T2  - O3  - T1  =  75.866 deg; T1  -- T1  = 3.6750 A
T1  - O2  - T2  - O4  - T2  = 109.543 deg; T1  -- T2  = 4.9992 A
T1  - O2  - T2  - O5  - T1  =  77.066 deg; T1  -- T1  = 3.7210 A
T1  - O3  - T2  - O4  - T2  = 110.578 deg; T1  -- T2  = 4.9100 A
T1  - O3  - T2  - O5  - T1  = 136.220 deg; T1  -- T1  = 5.4023 A
T2  - O4  - T2  - O5  - T1  = 110.616 deg; T2  -- T1  = 4.9070 A

        T-T-T SUMMARY
          Range  = 75.8664 deg <--> 136.2202 deg
          Mean   = 105.5577 deg
          StdDev = 18.8988 deg

        T--T SUMMARY
          Range  = 3.6750 A <--> 5.4023 A
          Mean   = 4.6886 A
          StdDev = 0.5687 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.885 deg ; T1  -- T1   3.0533 A

T1  -- O2  -- T2  = 141.350 deg ; T1  -- T2   3.0615 A

T1  -- O3  -- T2  = 126.268 deg ; T1  -- T2   2.9085 A

T1  -- O4  -- T2  = 126.457 deg ; T1  -- T2   2.9136 A

T2  -- O5  -- T2  = 141.246 deg ; T2  -- T2   3.0586 A


        T-O-T SUMMARY
          Range  = 126.2684° <--> 141.3496 deg
          Mean   = 135.2410 deg
          StdDev = 7.4395 deg

        T--T SUMMARY
          Range  = 2.9085 A <--> 3.0615 A
          Mean   = 2.9991 A
          StdDev = 0.0738 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 16 22 28 34 40 46 52 58 64 70 76 82 88 94
TD10 = 311
Circuit symbol = 4.6_{3}.4.6_{3}.6_{2}.6_{4}
Weight = 19
Vertex symbol  = 4.6_{3}.4.6_{3}.6.6_{4}
Weight = 19

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 16 22 28 34 40 46 52 58 64 70 76 82 88 94
TD10 = 311
Circuit symbol = 4.6_{3}.4.6_{3}.6_{2}.6_{4}
Weight = 19
Vertex symbol  = 4.6_{3}.4.6_{3}.6.6_{4}
Weight = 19

<TD10> = 311.000
Average ring size = 5.5714