Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_679_E1lsPJ.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.37 T-atoms per nm^3
Material density = 2.232 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6210 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O3  = 1.6210 Angstrom
T1  -- O4  = 1.6207 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.006831  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000382  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6214 Angstrom
T2  -- O5  = 1.6210 Angstrom
T2  -- O6  = 1.6210 Angstrom
T2  -- O4  = 1.6209 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.006888  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000248  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6207 A <--> 1.6214 A
          Mean   = 1.6210 A
          StdDev = 0.0002 A

       t1 Range  = 0.0068 <-- 0.0069 --> 0.0069
       t2 Range  = 0.0002 <-- 0.0003 --> 0.0004

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.545 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.404 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.426 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.579 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.453 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.420 deg; O3  -- O4  = 3 A
       109.404 deg <-- 109.471 deg --> 109.579 deg

O3  -- T2  -- O5  = 109.389 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.480 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.475 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.549 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.396 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.538 deg; O6  -- O4  = 3 A
       109.389 deg <-- 109.471 deg --> 109.549 deg

        O-T-O SUMMARY
          Range  = 109.3894 deg <--> 109.5787 deg
          Mean   = 109.4643 deg
          StdDev = 0.0633 deg

        O--O SUMMARY
          Range  = 2.6458 A <--> 2.6490 A
          Mean   = 2.6470 A
          StdDev = 0.0011 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 120.902 deg; T2  -- T1  = 5.2813 A
T2  - O1  - T1  - O3  - T1  = 108.586 deg; T2  -- T1  = 4.9371 A
T2  - O1  - T1  - O4  - T2  = 108.331 deg; T2  -- T2  = 4.9166 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3037 A
T1  - O2  - T1  - O4  - T2  = 117.919 deg; T1  -- T2  = 5.2016 A
T1  - O3  - T1  - O4  - T2  = 108.586 deg; T1  -- T2  = 4.9371 A

T1  - O3  - T2  - O5  - T2  = 117.825 deg; T1  -- T2  = 5.2027 A
T1  - O3  - T2  - O6  - T2  = 108.586 deg; T1  -- T2  = 4.9381 A
T1  - O3  - T2  - O4  - T1  = 108.331 deg; T1  -- T1  = 4.9166 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3077 A
T2  - O5  - T2  - O4  - T1  = 120.995 deg; T2  -- T1  = 5.2875 A
T2  - O6  - T2  - O4  - T1  = 108.586 deg; T2  -- T1  = 4.9381 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 120.9949 deg
          Mean   = 109.3813 deg
          StdDev = 9.2189 deg

        T--T SUMMARY
          Range  = 4.3037 A <--> 5.2875 A
          Mean   = 4.9431 A
          StdDev = 0.2929 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.204 deg ; T1  -- T1   3.0386 A

T1  -- O2  -- T1  = 140.101 deg ; T1  -- T1   3.0478 A

T1  -- O3  -- T2  = 138.517 deg ; T1  -- T2   3.0323 A

T1  -- O4  -- T2  = 138.596 deg ; T1  -- T2   3.0323 A

T2  -- O5  -- T2  = 139.635 deg ; T2  -- T2   3.0430 A

T2  -- O6  -- T2  = 140.258 deg ; T2  -- T2   3.0490 A


        T-O-T SUMMARY
          Range  = 138.5166° <--> 140.2582 deg
          Mean   = 139.3851 deg
          StdDev = 0.6912 deg

        T--T SUMMARY
          Range  = 3.0323 A <--> 3.0490 A
          Mean   = 3.0405 A
          StdDev = 0.0069 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 959.000
Average ring size = 5.6000