Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_644_pcapK6.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.83 T-atoms per nm^3
Material density = 1.779 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O2  = 1.6188 Angstrom
T1  -- O4  = 1.6207 Angstrom
T1  -- O3  = 1.6193 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.005562  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001171  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6195 Angstrom
T2  -- O4  = 1.6206 Angstrom
T2  -- O5  = 1.6159 Angstrom
T2  -- O6  = 1.6195 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.005699  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001935  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6158 A <--> 1.6207 A
          Mean   = 1.6188 A
          StdDev = 0.0018 A

       t1 Range  = 0.0056 <-- 0.0056 --> 0.0057
       t2 Range  = 0.0012 <-- 0.0016 --> 0.0019

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.605 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.316 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.291 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.458 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.400 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.757 deg; O4  -- O3  = 3 A
       109.291 deg <-- 109.471 deg --> 109.757 deg

O3  -- T2  -- O4  = 109.711 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.152 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.475 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.453 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.475 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.561 deg; O5  -- O6  = 3 A
       109.152 deg <-- 109.471 deg --> 109.711 deg

        O-T-O SUMMARY
          Range  = 109.1521 deg <--> 109.7574 deg
          Mean   = 109.4610 deg
          StdDev = 0.1711 deg

        O--O SUMMARY
          Range  = 2.6365 A <--> 2.6502 A
          Mean   = 2.6434 A
          StdDev = 0.0040 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 130.982 deg; T2  -- T1  = 5.7081 A
T2  - O1  - T1  - O4  - T1  = 118.478 deg; T2  -- T1  = 5.2859 A
T2  - O1  - T1  - O3  - T2  =  76.527 deg; T2  -- T2  = 3.7825 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4743 A
T1  - O2  - T1  - O3  - T2  = 126.246 deg; T1  -- T2  = 5.6049 A
T1  - O4  - T1  - O3  - T2  = 118.374 deg; T1  -- T2  = 5.2919 A

T1  - O3  - T2  - O4  - T2  = 118.478 deg; T1  -- T2  = 5.2718 A
T1  - O3  - T2  - O5  - T2  = 126.802 deg; T1  -- T2  = 5.6131 A
T1  - O3  - T2  - O6  - T1  =  77.279 deg; T1  -- T1  = 3.8139 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.4659 A
T2  - O4  - T2  - O6  - T1  = 118.374 deg; T2  -- T1  = 5.2778 A
T2  - O5  - T2  - O6  - T1  = 129.711 deg; T2  -- T1  = 5.6918 A

        T-T-T SUMMARY
          Range  = 76.5267 deg <--> 130.9823 deg
          Mean   = 108.2640 deg
          StdDev = 19.7721 deg

        T--T SUMMARY
          Range  = 3.7825 A <--> 5.7081 A
          Mean   = 4.9620 A
          StdDev = 0.6809 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 172.169 deg ; T1  -- T1   3.2240 A

T1  -- O2  -- T1  = 146.782 deg ; T1  -- T1   3.1025 A

T1  -- O3  -- T2  = 141.647 deg ; T1  -- T2   3.0591 A

T1  -- O4  -- T2  = 140.311 deg ; T1  -- T2   3.0488 A

T2  -- O5  -- T2  = 174.418 deg ; T2  -- T2   3.2280 A

T2  -- O6  -- T2  = 144.658 deg ; T2  -- T2   3.0861 A


        T-O-T SUMMARY
          Range  = 140.3108° <--> 174.4182 deg
          Mean   = 153.3307 deg
          StdDev = 14.5883 deg

        T--T SUMMARY
          Range  = 3.0488 A <--> 3.2280 A
          Mean   = 3.1248 A
          StdDev = 0.0753 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 55 79 106 138 175 215 260 309 362 420 482 548
TD10 = 840
Circuit symbol = 4.4.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 26
Vertex symbol  = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 26

<TD10> = 840.000
Average ring size = 6.2609