Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_619_hmRczU.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.26 T-atoms per nm^3
Material density = 2.221 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6202 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6201 Angstrom
T1  -- O4  = 1.6200 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.006426  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000638  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6199 Angstrom
T2  -- O6  = 1.6212 Angstrom
T2  -- O4  = 1.6198 Angstrom
T2  -- O5  = 1.6207 Angstrom
      mean = 1.6204 Angstrom
        t1 = 0.006525  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000677  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6198 A <--> 1.6212 A
          Mean   = 1.6203 A
          StdDev = 0.0005 A

       t1 Range  = 0.0064 <-- 0.0065 --> 0.0065
       t2 Range  = 0.0006 <-- 0.0007 --> 0.0007

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.578 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.395 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.353 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.567 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.617 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.316 deg; O3  -- O4  = 3 A
       109.316 deg <-- 109.471 deg --> 109.617 deg

O3  -- T2  -- O6  = 109.539 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.413 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.482 deg; O3  -- O5  = 3 A
O6  -- T2  -- O4  = 109.503 deg; O6  -- O4  = 3 A
O6  -- T2  -- O5  = 109.612 deg; O6  -- O5  = 3 A
O4  -- T2  -- O5  = 109.277 deg; O4  -- O5  = 3 A
       109.277 deg <-- 109.471 deg --> 109.612 deg

        O-T-O SUMMARY
          Range  = 109.2774 deg <--> 109.6171 deg
          Mean   = 109.4599 deg
          StdDev = 0.1120 deg

        O--O SUMMARY
          Range  = 2.6427 A <--> 2.6494 A
          Mean   = 2.6458 A
          StdDev = 0.0021 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 118.597 deg; T2  -- T1  = 5.2409 A
T2  - O1  - T1  - O3  - T1  = 108.663 deg; T2  -- T1  = 4.9400 A
T2  - O1  - T1  - O4  - T2  = 107.811 deg; T2  -- T2  = 4.9194 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3030 A
T1  - O2  - T1  - O4  - T2  = 120.681 deg; T1  -- T2  = 5.2945 A
T1  - O3  - T1  - O4  - T2  = 108.679 deg; T1  -- T2  = 4.9384 A

T1  - O3  - T2  - O6  - T2  = 108.663 deg; T1  -- T2  = 4.9405 A
T1  - O3  - T2  - O4  - T1  = 107.811 deg; T1  -- T1  = 4.9194 A
T1  - O3  - T2  - O5  - T2  = 120.864 deg; T1  -- T2  = 5.2999 A
T2  - O6  - T2  - O4  - T1  = 108.679 deg; T2  -- T1  = 4.9389 A
T2  - O6  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.3023 A
T1  - O4  - T2  - O5  - T2  = 118.414 deg; T1  -- T2  = 5.2323 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 120.8636 deg
          Mean   = 109.5057 deg
          StdDev = 9.4195 deg

        T--T SUMMARY
          Range  = 4.3023 A <--> 5.2999 A
          Mean   = 4.9544 A
          StdDev = 0.3040 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.525 deg ; T1  -- T1   3.0500 A

T1  -- O2  -- T1  = 138.910 deg ; T1  -- T1   3.0354 A

T1  -- O3  -- T2  = 140.073 deg ; T1  -- T2   3.0453 A

T1  -- O4  -- T2  = 139.825 deg ; T1  -- T2   3.0428 A

T2  -- O5  -- T2  = 140.237 deg ; T2  -- T2   3.0482 A

T2  -- O6  -- T2  = 138.889 deg ; T2  -- T2   3.0360 A


        T-O-T SUMMARY
          Range  = 138.8889° <--> 140.5252 deg
          Mean   = 139.7431 deg
          StdDev = 0.6455 deg

        T--T SUMMARY
          Range  = 3.0354 A <--> 3.0500 A
          Mean   = 3.0430 A
          StdDev = 0.0057 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 959.000
Average ring size = 5.6000