Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_616_o3QqJr.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 25.77 T-atoms per nm^3
Material density = 2.571 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6728 Angstrom
T1  -- O2  = 1.6234 Angstrom
T1  -- O3  = 1.6534 Angstrom
T1  -- O4  = 1.6691 Angstrom
      mean = 1.6547 Angstrom
        t1 = 0.039851  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018374  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6014 Angstrom
T2  -- O4  = 1.5867 Angstrom
T2  -- O5  = 1.5988 Angstrom
T2  -- O6  = 1.6403 Angstrom
      mean = 1.6068 Angstrom
        t1 = 0.049399  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045700  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5867 A <--> 1.6728 A
          Mean   = 1.6307 A
          StdDev = 0.0316 A

       t1 Range  = 0.0399 <-- 0.0446 --> 0.0494
       t2 Range  = 0.0184 <-- 0.0320 --> 0.0457

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.821 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.338 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 118.024 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.824 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.232 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 105.318 deg; O3  -- O4  = 3 A
       105.318 deg <-- 109.426 deg --> 118.024 deg

O3  -- T2  -- O4  = 102.139 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 118.979 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.311 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  =  99.241 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 118.420 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 107.848 deg; O5  -- O6  = 3 A
       99.241 deg <-- 109.490 deg --> 118.979 deg

        O-T-O SUMMARY
          Range  = 99.2405 deg <--> 118.9792 deg
          Mean   = 109.6055 deg
          StdDev = 6.3096 deg

        O--O SUMMARY
          Range  = 2.4266 A <--> 2.8650 A
          Mean   = 2.6612 A
          StdDev = 0.1201 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  95.761 deg; T2  -- T1  = 4.6078 A
T2  - O1  - T1  - O3  - T1  = 120.131 deg; T2  -- T1  = 5.0969 A
T2  - O1  - T1  - O4  - T2  = 105.759 deg; T2  -- T2  = 4.5802 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4495 A
T1  - O2  - T1  - O4  - T2  = 121.953 deg; T1  -- T2  = 5.3798 A
T1  - O3  - T1  - O4  - T2  = 120.768 deg; T1  -- T2  = 5.0662 A

T1  - O3  - T2  - O4  - T2  = 132.880 deg; T1  -- T2  = 5.5814 A
T1  - O3  - T2  - O5  - T2  = 120.131 deg; T1  -- T2  = 4.9074 A
T1  - O3  - T2  - O6  - T1  = 105.759 deg; T1  -- T1  = 4.5802 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.2192 A
T2  - O4  - T2  - O6  - T1  =  83.815 deg; T2  -- T1  = 4.0380 A
T2  - O5  - T2  - O6  - T1  = 120.768 deg; T2  -- T1  = 4.8755 A

        T-T-T SUMMARY
          Range  = 83.8155 deg <--> 132.8797 deg
          Mean   = 109.0419 deg
          StdDev = 15.7256 deg

        T--T SUMMARY
          Range  = 4.0380 A <--> 5.5814 A
          Mean   = 4.7855 A
          StdDev = 0.4599 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 161.527 deg ; T1  -- T1   3.3023 A

T1  -- O2  -- T1  = 133.411 deg ; T1  -- T1   2.9821 A

T1  -- O3  -- T2  = 125.919 deg ; T1  -- T2   2.8991 A

T1  -- O4  -- T2  = 121.786 deg ; T1  -- T2   2.8449 A

T2  -- O5  -- T2  = 171.350 deg ; T2  -- T2   3.1885 A

T2  -- O6  -- T2  = 114.763 deg ; T2  -- T2   2.7631 A


        T-O-T SUMMARY
          Range  = 114.7635° <--> 171.3497 deg
          Mean   = 138.1260 deg
          StdDev = 21.4090 deg

        T--T SUMMARY
          Range  = 2.7631 A <--> 3.3023 A
          Mean   = 2.9967 A
          StdDev = 0.1945 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7631 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 959.000
Average ring size = 5.6000