Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_615_T5aaSs.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 24.99 T-atoms per nm^3
Material density = 2.493 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6219 Angstrom
T1  -- O2  = 1.6204 Angstrom
T1  -- O3  = 1.6234 Angstrom
T1  -- O4  = 1.6230 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.007622  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000712  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O5  = 1.6211 Angstrom
T2  -- O6  = 1.6212 Angstrom
T2  -- O4  = 1.6240 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.007734  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001514  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6204 A <--> 1.6240 A
          Mean   = 1.6220 A
          StdDev = 0.0012 A

       t1 Range  = 0.0076 <-- 0.0077 --> 0.0077
       t2 Range  = 0.0007 <-- 0.0011 --> 0.0015

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.519 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.476 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.739 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.602 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.343 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.149 deg; O3  -- O4  = 3 A
       109.149 deg <-- 109.471 deg --> 109.739 deg

O3  -- T2  -- O5  = 109.918 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.584 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.125 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.750 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 108.697 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.749 deg; O6  -- O4  = 3 A
       108.697 deg <-- 109.471 deg --> 109.918 deg

        O-T-O SUMMARY
          Range  = 108.6969 deg <--> 109.9177 deg
          Mean   = 109.4560 deg
          StdDev = 0.3416 deg

        O--O SUMMARY
          Range  = 2.6369 A <--> 2.6545 A
          Mean   = 2.6486 A
          StdDev = 0.0051 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  95.942 deg; T2  -- T1  = 4.4735 A
T2  - O1  - T1  - O3  - T1  = 108.701 deg; T2  -- T1  = 4.9077 A
T2  - O1  - T1  - O4  - T2  = 102.782 deg; T2  -- T2  = 4.6766 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3019 A
T1  - O2  - T1  - O4  - T2  = 147.242 deg; T1  -- T2  = 5.7845 A
T1  - O3  - T1  - O4  - T2  = 108.657 deg; T1  -- T2  = 4.9119 A

T1  - O3  - T2  - O5  - T2  = 108.701 deg; T1  -- T2  = 4.9095 A
T1  - O3  - T2  - O6  - T1  = 102.782 deg; T1  -- T1  = 4.6766 A
T1  - O3  - T2  - O4  - T2  = 147.801 deg; T1  -- T2  = 5.7851 A
T2  - O5  - T2  - O6  - T1  = 108.657 deg; T2  -- T1  = 4.9137 A
T2  - O5  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.3028 A
T1  - O6  - T2  - O4  - T2  =  95.257 deg; T1  -- T2  = 4.4536 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 147.8007 deg
          Mean   = 109.4749 deg
          StdDev = 19.3843 deg

        T--T SUMMARY
          Range  = 4.3019 A <--> 5.7851 A
          Mean   = 4.8549 A
          StdDev = 0.4963 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.500 deg ; T1  -- T1   3.0334 A

T1  -- O2  -- T1  = 140.531 deg ; T1  -- T1   3.0504 A

T1  -- O3  -- T2  = 134.218 deg ; T1  -- T2   2.9889 A

T1  -- O4  -- T2  = 134.632 deg ; T1  -- T2   2.9958 A

T2  -- O5  -- T2  = 138.540 deg ; T2  -- T2   3.0323 A

T2  -- O6  -- T2  = 140.594 deg ; T2  -- T2   3.0527 A


        T-O-T SUMMARY
          Range  = 134.2180° <--> 140.5940 deg
          Mean   = 137.8359 deg
          StdDev = 2.6098 deg

        T--T SUMMARY
          Range  = 2.9889 A <--> 3.0527 A
          Mean   = 3.0256 A
          StdDev = 0.0253 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 959.000
Average ring size = 5.6000