Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_486_bKvnY5.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 18.07 T-atoms per nm^3
Material density = 1.802 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6215 Angstrom
T1  -- O2  = 1.6157 Angstrom
T1  -- O3  = 1.6196 Angstrom
T1  -- O4  = 1.6101 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.004627  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001949  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6100 Angstrom
T2  -- O5  = 1.6202 Angstrom
T2  -- O6  = 1.6154 Angstrom
T2  -- O7  = 1.6221 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.004880  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002756  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6100 A <--> 1.6221 A
          Mean   = 1.6168 A
          StdDev = 0.0046 A

       t1 Range  = 0.0046 <-- 0.0048 --> 0.0049
       t2 Range  = 0.0019 <-- 0.0024 --> 0.0028

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.466 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.472 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.544 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.660 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.529 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.156 deg; O3  -- O4  = 3 A
       109.156 deg <-- 109.471 deg --> 109.660 deg

O4  -- T2  -- O5  = 109.291 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.298 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.699 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.422 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.594 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.521 deg; O6  -- O7  = 3 A
       109.291 deg <-- 109.471 deg --> 109.699 deg

        O-T-O SUMMARY
          Range  = 109.1559 deg <--> 109.6992 deg
          Mean   = 109.4540 deg
          StdDev = 0.1682 deg

        O--O SUMMARY
          Range  = 2.6307 A <--> 2.6493 A
          Mean   = 2.6387 A
          StdDev = 0.0058 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 124.382 deg; T1  -- T2  = 5.5091 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3061 A
T1  - O1  - T1  - O4  - T1  = 112.135 deg; T1  -- T1  = 5.1778 A
T2  - O2  - T1  - O3  - T1  = 124.826 deg; T2  -- T1  = 5.5803 A
T2  - O2  - T1  - O4  - T1  = 109.822 deg; T2  -- T1  = 5.2738 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4611 A

T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.4198 A
T2  - O4  - T2  - O6  - T1  = 110.639 deg; T2  -- T1  = 5.3021 A
T2  - O4  - T2  - O7  - T2  = 110.664 deg; T2  -- T2  = 5.1778 A
T2  - O5  - T2  - O6  - T1  = 124.826 deg; T2  -- T1  = 5.5251 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.2992 A
T1  - O6  - T2  - O7  - T2  = 124.700 deg; T1  -- T2  = 5.5638 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 124.8255 deg
          Mean   = 106.9586 deg
          StdDev = 13.3243 deg

        T--T SUMMARY
          Range  = 4.2992 A <--> 5.5803 A
          Mean   = 5.0227 A
          StdDev = 0.4700 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.355 deg ; T1  -- T1   3.0106 A

T1  -- O2  -- T1  = 175.003 deg ; T1  -- T1   3.2283 A

T1  -- O3  -- T1  = 143.789 deg ; T1  -- T1   3.0788 A

T1  -- O4  -- T2  = 174.847 deg ; T1  -- T2   3.2169 A

T2  -- O5  -- T2  = 141.995 deg ; T2  -- T2   3.0637 A

T2  -- O6  -- T2  = 179.598 deg ; T2  -- T2   3.2307 A

T2  -- O7  -- T2  = 136.779 deg ; T2  -- T2   3.0161 A


        T-O-T SUMMARY
          Range  = 136.3555° <--> 179.5981 deg
          Mean   = 155.4810 deg
          StdDev = 18.7453 deg

        T--T SUMMARY
          Range  = 3.0106 A <--> 3.2307 A
          Mean   = 3.1207 A
          StdDev = 0.0950 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000