Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_311_0NoiYi.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.76 T-atoms per nm^3
Material density = 1.972 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6220 Angstrom
T1  -- O2  = 1.6216 Angstrom
T1  -- O3  = 1.6168 Angstrom
T1  -- O4  = 1.6172 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006454  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002118  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6220 Angstrom
T2  -- O7  = 1.6225 Angstrom
T2  -- O4  = 1.6176 Angstrom
T2  -- O6  = 1.6197 Angstrom
      mean = 1.6204 Angstrom
        t1 = 0.007277  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002959  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6168 A <--> 1.6225 A
          Mean   = 1.6199 A
          StdDev = 0.0023 A

       t1 Range  = 0.0065 <-- 0.0069 --> 0.0073
       t2 Range  = 0.0021 <-- 0.0025 --> 0.0030

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.374 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.157 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.132 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.162 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.870 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.126 deg; O3  -- O4  = 3 A
       109.126 deg <-- 109.470 deg --> 110.132 deg

O5  -- T2  -- O7  = 109.501 deg; O5  -- O7  = 3 A
O5  -- T2  -- O4  = 109.002 deg; O5  -- O4  = 3 A
O5  -- T2  -- O6  = 110.243 deg; O5  -- O6  = 3 A
O7  -- T2  -- O4  = 109.831 deg; O7  -- O4  = 3 A
O7  -- T2  -- O6  = 109.401 deg; O7  -- O6  = 3 A
O4  -- T2  -- O6  = 108.848 deg; O4  -- O6  = 3 A
       108.848 deg <-- 109.471 deg --> 110.243 deg

        O-T-O SUMMARY
          Range  = 108.8485 deg <--> 110.2433 deg
          Mean   = 109.4698 deg
          StdDev = 0.4605 deg

        O--O SUMMARY
          Range  = 2.6330 A <--> 2.6594 A
          Mean   = 2.6448 A
          StdDev = 0.0085 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 127.300 deg; T1  -- T1  = 5.2936 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3355 A
T1  - O1  - T1  - O4  - T2  = 111.788 deg; T1  -- T2  = 5.0045 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3358 A
T1  - O2  - T1  - O4  - T2  = 115.577 deg; T1  -- T2  = 5.1140 A
T1  - O3  - T1  - O4  - T2  = 115.165 deg; T1  -- T2  = 5.2878 A

T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3542 A
T2  - O5  - T2  - O4  - T1  = 122.862 deg; T2  -- T1  = 5.5007 A
T2  - O5  - T2  - O6  - T2  = 111.371 deg; T2  -- T2  = 5.2936 A
T2  - O7  - T2  - O4  - T1  = 115.165 deg; T2  -- T1  = 5.1255 A
T2  - O7  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3998 A
T1  - O4  - T2  - O6  - T2  = 118.480 deg; T1  -- T2  = 5.4360 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 127.2996 deg
          Mean   = 110.9302 deg
          StdDev = 12.0370 deg

        T--T SUMMARY
          Range  = 4.3355 A <--> 5.5007 A
          Mean   = 5.0527 A
          StdDev = 0.4062 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.138 deg ; T1  -- T1   2.9535 A

T1  -- O2  -- T1  = 131.228 deg ; T1  -- T1   2.9539 A

T1  -- O3  -- T1  = 157.921 deg ; T1  -- T1   3.1739 A

T1  -- O4  -- T2  = 145.566 deg ; T1  -- T2   3.0898 A

T2  -- O5  -- T2  = 156.041 deg ; T2  -- T2   3.1733 A

T2  -- O6  -- T2  = 174.449 deg ; T2  -- T2   3.2356 A

T2  -- O7  -- T2  = 133.510 deg ; T2  -- T2   2.9815 A


        T-O-T SUMMARY
          Range  = 131.1378° <--> 174.4488 deg
          Mean   = 147.1218 deg
          StdDev = 15.5814 deg

        T--T SUMMARY
          Range  = 2.9535 A <--> 3.2356 A
          Mean   = 3.0802 A
          StdDev = 0.1112 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000