Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_300_7vV7yt.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.49 T-atoms per nm^3
Material density = 1.944 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6212 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O3  = 1.6164 Angstrom
T1  -- O4  = 1.6169 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.006137  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001949  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6170 Angstrom
T2  -- O5  = 1.6214 Angstrom
T2  -- O7  = 1.6231 Angstrom
T2  -- O6  = 1.6195 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.007155  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002887  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6164 A <--> 1.6231 A
          Mean   = 1.6196 A
          StdDev = 0.0024 A

       t1 Range  = 0.0061 <-- 0.0066 --> 0.0072
       t2 Range  = 0.0019 <-- 0.0024 --> 0.0029

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.196 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.230 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.046 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.242 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.002 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.106 deg; O3  -- O4  = 3 A
       109.106 deg <-- 109.470 deg --> 110.046 deg

O4  -- T2  -- O5  = 108.986 deg; O4  -- O5  = 3 A
O4  -- T2  -- O7  = 110.010 deg; O4  -- O7  = 3 A
O4  -- T2  -- O6  = 108.896 deg; O4  -- O6  = 3 A
O5  -- T2  -- O7  = 109.499 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 110.086 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 109.351 deg; O7  -- O6  = 3 A
       108.896 deg <-- 109.471 deg --> 110.086 deg

        O-T-O SUMMARY
          Range  = 108.8955 deg <--> 110.0863 deg
          Mean   = 109.4832 deg
          StdDev = 0.4648 deg

        O--O SUMMARY
          Range  = 2.6331 A <--> 2.6562 A
          Mean   = 2.6445 A
          StdDev = 0.0086 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 125.726 deg; T1  -- T1  = 5.2858 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3606 A
T1  - O1  - T1  - O4  - T2  = 112.016 deg; T1  -- T2  = 5.0308 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3581 A
T1  - O2  - T1  - O4  - T2  = 116.116 deg; T1  -- T2  = 5.1458 A
T1  - O3  - T1  - O4  - T2  = 116.593 deg; T1  -- T2  = 5.3489 A

T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.3443 A
T2  - O4  - T2  - O7  - T1  = 122.730 deg; T2  -- T1  = 5.5055 A
T2  - O4  - T2  - O6  - T2  = 110.995 deg; T2  -- T2  = 5.2858 A
T2  - O5  - T2  - O7  - T1  = 116.593 deg; T2  -- T1  = 5.1548 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3881 A
T1  - O7  - T2  - O6  - T2  = 118.114 deg; T1  -- T2  = 5.4315 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 125.7256 deg
          Mean   = 109.2962 deg
          StdDev = 12.7473 deg

        T--T SUMMARY
          Range  = 4.3443 A <--> 5.5055 A
          Mean   = 5.0167 A
          StdDev = 0.4345 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.839 deg ; T1  -- T1   2.9716 A

T1  -- O2  -- T1  = 132.516 deg ; T1  -- T1   2.9680 A

T1  -- O3  -- T1  = 161.622 deg ; T1  -- T1   3.1913 A

T1  -- O4  -- T2  = 146.357 deg ; T1  -- T2   3.0955 A

T2  -- O5  -- T2  = 156.889 deg ; T2  -- T2   3.1771 A

T2  -- O6  -- T2  = 175.793 deg ; T2  -- T2   3.2367 A

T2  -- O7  -- T2  = 131.774 deg ; T2  -- T2   2.9629 A


        T-O-T SUMMARY
          Range  = 131.7739° <--> 175.7928 deg
          Mean   = 148.2557 deg
          StdDev = 16.2031 deg

        T--T SUMMARY
          Range  = 2.9629 A <--> 3.2367 A
          Mean   = 3.0862 A
          StdDev = 0.1118 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 254 296 334 364 395 422
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 254 296 334 364 395 422
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000