Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_286_IE5apJ.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.25 T-atoms per nm^3
Material density = 1.921 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6207 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6163 Angstrom
T1  -- O4  = 1.6155 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.005477  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001293  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6152 Angstrom
T2  -- O5  = 1.6190 Angstrom
T2  -- O7  = 1.6216 Angstrom
T2  -- O6  = 1.6214 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.006539  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001940  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6152 A <--> 1.6216 A
          Mean   = 1.6188 A
          StdDev = 0.0026 A

       t1 Range  = 0.0055 <-- 0.0060 --> 0.0065
       t2 Range  = 0.0013 <-- 0.0016 --> 0.0019

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.131 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.300 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.813 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.340 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.940 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.301 deg; O3  -- O4  = 3 A
       109.131 deg <-- 109.471 deg --> 109.940 deg

O4  -- T2  -- O5  = 108.984 deg; O4  -- O5  = 3 A
O4  -- T2  -- O7  = 109.615 deg; O4  -- O7  = 3 A
O4  -- T2  -- O6  = 109.028 deg; O4  -- O6  = 3 A
O5  -- T2  -- O7  = 109.520 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 110.127 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 109.552 deg; O7  -- O6  = 3 A
       108.984 deg <-- 109.471 deg --> 110.127 deg

        O-T-O SUMMARY
          Range  = 108.9837 deg <--> 110.1272 deg
          Mean   = 109.4627 deg
          StdDev = 0.3579 deg

        O--O SUMMARY
          Range  = 2.6328 A <--> 2.6564 A
          Mean   = 2.6427 A
          StdDev = 0.0069 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 116.636 deg; T2  -- T1  = 5.1983 A
T2  - O1  - T1  - O3  - T1  = 112.664 deg; T2  -- T1  = 5.0825 A
T2  - O1  - T1  - O4  - T1  = 115.871 deg; T2  -- T1  = 5.3633 A
T1  - O2  - T1  - O3  - T1  = 124.758 deg; T1  -- T1  = 5.2821 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3755 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3742 A

T1  - O4  - T2  - O5  - T2  = 117.989 deg; T1  -- T2  = 5.4507 A
T1  - O4  - T2  - O7  - T2  = 115.871 deg; T1  -- T2  = 5.2021 A
T1  - O4  - T2  - O6  - T2  = 122.747 deg; T1  -- T2  = 5.5119 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.4183 A
T2  - O5  - T2  - O6  - T2  = 111.608 deg; T2  -- T2  = 5.2821 A
T2  - O7  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3605 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 124.7584 deg
          Mean   = 108.3679 deg
          StdDev = 13.5522 deg

        T--T SUMMARY
          Range  = 4.3605 A <--> 5.5119 A
          Mean   = 5.0099 A
          StdDev = 0.4654 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 133.824 deg ; T1  -- T1   2.9817 A

T1  -- O2  -- T1  = 133.635 deg ; T1  -- T1   2.9798 A

T1  -- O3  -- T1  = 164.264 deg ; T1  -- T1   3.2022 A

T1  -- O4  -- T2  = 150.778 deg ; T1  -- T2   3.1263 A

T2  -- O5  -- T2  = 173.420 deg ; T2  -- T2   3.2327 A

T2  -- O6  -- T2  = 153.011 deg ; T2  -- T2   3.1532 A

T2  -- O7  -- T2  = 136.443 deg ; T2  -- T2   3.0118 A


        T-O-T SUMMARY
          Range  = 133.6351° <--> 173.4203 deg
          Mean   = 149.3395 deg
          StdDev = 14.7665 deg

        T--T SUMMARY
          Range  = 2.9798 A <--> 3.2327 A
          Mean   = 3.0982 A
          StdDev = 0.1002 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000