Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_10_2_283_RHl8Pw.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.34 T-atoms per nm^3
Material density = 1.930 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6209 Angstrom
T1  -- O2  = 1.6209 Angstrom
T1  -- O3  = 1.6163 Angstrom
T1  -- O4  = 1.6155 Angstrom
      mean = 1.6184 Angstrom
        t1 = 0.005537  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001411  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6155 Angstrom
T2  -- O5  = 1.6193 Angstrom
T2  -- O6  = 1.6215 Angstrom
T2  -- O7  = 1.6215 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006611  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002901  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6155 A <--> 1.6215 A
          Mean   = 1.6189 A
          StdDev = 0.0026 A

       t1 Range  = 0.0055 <-- 0.0061 --> 0.0066
       t2 Range  = 0.0014 <-- 0.0022 --> 0.0029

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.189 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.259 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.833 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.289 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.946 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.309 deg; O3  -- O4  = 3 A
       109.189 deg <-- 109.471 deg --> 109.946 deg

O4  -- T2  -- O5  = 108.985 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.011 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.592 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.129 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.540 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.568 deg; O6  -- O7  = 3 A
       108.985 deg <-- 109.471 deg --> 110.129 deg

        O-T-O SUMMARY
          Range  = 108.9845 deg <--> 110.1286 deg
          Mean   = 109.4624 deg
          StdDev = 0.3621 deg

        O--O SUMMARY
          Range  = 2.6332 A <--> 2.6568 A
          Mean   = 2.6429 A
          StdDev = 0.0069 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 116.446 deg; T2  -- T1  = 5.1862 A
T2  - O1  - T1  - O3  - T1  = 112.605 deg; T2  -- T1  = 5.0741 A
T2  - O1  - T1  - O4  - T1  = 115.427 deg; T2  -- T1  = 5.3434 A
T1  - O2  - T1  - O3  - T1  = 125.265 deg; T1  -- T1  = 5.2846 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3678 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3664 A

T1  - O4  - T2  - O5  - T2  = 122.770 deg; T1  -- T2  = 5.5104 A
T1  - O4  - T2  - O6  - T2  = 115.427 deg; T1  -- T2  = 5.1916 A
T1  - O4  - T2  - O7  - T2  = 118.144 deg; T1  -- T2  = 5.4525 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3643 A
T2  - O5  - T2  - O7  - T2  = 111.694 deg; T2  -- T2  = 5.2846 A
T2  - O6  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.4215 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 125.2651 deg
          Mean   = 108.3081 deg
          StdDev = 13.5421 deg

        T--T SUMMARY
          Range  = 4.3643 A <--> 5.5104 A
          Mean   = 5.0044 A
          StdDev = 0.4649 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 133.303 deg ; T1  -- T1   2.9763 A

T1  -- O2  -- T1  = 133.119 deg ; T1  -- T1   2.9743 A

T1  -- O3  -- T1  = 162.939 deg ; T1  -- T1   3.1968 A

T1  -- O4  -- T2  = 150.390 deg ; T1  -- T2   3.1237 A

T2  -- O5  -- T2  = 172.825 deg ; T2  -- T2   3.2322 A

T2  -- O6  -- T2  = 153.006 deg ; T2  -- T2   3.1535 A

T2  -- O7  -- T2  = 136.979 deg ; T2  -- T2   3.0171 A


        T-O-T SUMMARY
          Range  = 133.1192° <--> 172.8247 deg
          Mean   = 148.9373 deg
          StdDev = 14.5194 deg

        T--T SUMMARY
          Range  = 2.9743 A <--> 3.2322 A
          Mean   = 3.0963 A
          StdDev = 0.1005 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000