Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_109_2_17_rWIv_n.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 17.63 T-atoms per nm^3
Material density = 1.759 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6276 Angstrom
T1  -- O2  = 1.6470 Angstrom
T1  -- O3  = 1.6319 Angstrom
T1  -- O1  = 1.6275 Angstrom
      mean = 1.6335 Angstrom
        t1 = 0.021096  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015848  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6259 Angstrom
T2  -- O4  = 1.6326 Angstrom
T2  -- O5  = 1.6135 Angstrom
T2  -- O3  = 1.6395 Angstrom
      mean = 1.6279 Angstrom
        t1 = 0.016410  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009296  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6135 A <--> 1.6470 A
          Mean   = 1.6307 A
          StdDev = 0.0093 A

       t1 Range  = 0.0164 <-- 0.0188 --> 0.0211
       t2 Range  = 0.0093 <-- 0.0126 --> 0.0158

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.761 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.608 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 111.158 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 108.276 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.183 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 114.530 deg; O3  -- O1  = 3 A
       106.608 deg <-- 109.419 deg --> 114.530 deg

O2  -- T2  -- O4  = 113.062 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 108.904 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 106.349 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.463 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.269 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.723 deg; O5  -- O3  = 3 A
       106.349 deg <-- 109.462 deg --> 113.062 deg

        O-T-O SUMMARY
          Range  = 106.3493 deg <--> 114.5296 deg
          Mean   = 109.4395 deg
          StdDev = 2.4480 deg

        O--O SUMMARY
          Range  = 2.6136 A <--> 2.7418 A
          Mean   = 2.6623 A
          StdDev = 0.0382 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 111.351 deg; T1  -- T2  = 4.6939 A
T1  - O1  - T1  - O3  - T2  =  63.260 deg; T1  -- T2  = 2.9380 A
T1  - O1  - T1  - O1  - T1  = 128.362 deg; T1  -- T1  = 4.9406 A
T2  - O2  - T1  - O3  - T2  = 110.484 deg; T2  -- T2  = 4.7596 A
T2  - O2  - T1  - O1  - T1  =  60.211 deg; T2  -- T1  = 2.8551 A
T2  - O3  - T1  - O1  - T1  = 166.212 deg; T2  -- T1  = 5.5588 A

T1  - O2  - T2  - O4  - T2  = 109.124 deg; T1  -- T2  = 5.0079 A
T1  - O2  - T2  - O5  - T2  = 160.876 deg; T1  -- T2  = 5.6680 A
T1  - O2  - T2  - O3  - T1  =  56.529 deg; T1  -- T1  = 2.7442 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.2628 A
T2  - O4  - T2  - O3  - T1  = 120.751 deg; T2  -- T1  = 5.2713 A
T2  - O5  - T2  - O3  - T1  = 113.981 deg; T2  -- T1  = 4.7506 A

        T-T-T SUMMARY
          Range  = 56.5291 deg <--> 166.2115 deg
          Mean   = 108.3601 deg
          StdDev = 34.8754 deg

        T--T SUMMARY
          Range  = 2.7442 A <--> 5.6680 A
          Mean   = 4.4625 A
          StdDev = 1.0218 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.925 deg ; T1  -- T1   2.7442 A

T1  -- O2  -- T2  = 127.702 deg ; T1  -- T2   2.9380 A

T1  -- O3  -- T2  = 121.556 deg ; T1  -- T2   2.8551 A

T2  -- O4  -- T2  = 118.757 deg ; T2  -- T2   2.8099 A

T2  -- O5  -- T2  = 166.786 deg ; T2  -- T2   3.2056 A


        T-O-T SUMMARY
          Range  = 114.9249° <--> 166.7861 deg
          Mean   = 129.9451 deg
          StdDev = 19.0054 deg

        T--T SUMMARY
          Range  = 2.7442 A <--> 3.2056 A
          Mean   = 2.9105 A
          StdDev = 0.1615 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7442 Angstrom
T1  -- T1  = 2.7442 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 17 28 45 66 88 114 141 182 213 252 300 348 399 450
TD10 = 694
Circuit symbol = 3.3.6.8.7.7
Weight = 8
Vertex symbol  = 3.3.6.10.10.10
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 16 28 48 66 84 115 150 178 206 255 312 346 384 452
TD10 = 699
Circuit symbol = 3.4.6.6.7.7
Weight = 12
Vertex symbol  = 3.4.6.6.10.10
Weight = 26

<TD10> = 696.500
Average ring size = 5.3333