Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_108_2_735_VFa5gZ.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 15.09 T-atoms per nm^3
Material density = 1.505 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6073 Angstrom
T1  -- O2  = 1.6264 Angstrom
T1  -- O3  = 1.6286 Angstrom
T1  -- O1  = 1.6072 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.008371  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004577  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O4  = 1.6276 Angstrom
T2  -- O4  = 1.6236 Angstrom
      mean = 1.6237 Angstrom
        t1 = 0.012241  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005689  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6072 A <--> 1.6286 A
          Mean   = 1.6195 A
          StdDev = 0.0090 A

       t1 Range  = 0.0084 <-- 0.0103 --> 0.0122
       t2 Range  = 0.0046 <-- 0.0051 --> 0.0057

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.505 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.110 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 108.223 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.208 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 110.515 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.251 deg; O3  -- O1  = 3 A
       108.223 deg <-- 109.469 deg --> 110.515 deg

O3  -- T2  -- O3  = 107.311 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 109.122 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.640 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.122 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.640 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 111.893 deg; O4  -- O4  = 3 A
       107.311 deg <-- 109.455 deg --> 111.893 deg

        O-T-O SUMMARY
          Range  = 107.3115 deg <--> 111.8931 deg
          Mean   = 109.3560 deg
          StdDev = 1.0119 deg

        O--O SUMMARY
          Range  = 2.6042 A <--> 2.6937 A
          Mean   = 2.6440 A
          StdDev = 0.0198 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  60.108 deg; T1  -- T2  = 2.9556 A
T1  - O1  - T1  - O3  - T1  = 113.745 deg; T1  -- T1  = 5.1216 A
T1  - O1  - T1  - O1  - T1  = 113.745 deg; T1  -- T1  = 5.1216 A
T2  - O2  - T1  - O3  - T1  = 127.958 deg; T2  -- T1  = 5.5037 A
T2  - O2  - T1  - O1  - T1  = 118.775 deg; T2  -- T1  = 5.2713 A
T1  - O3  - T1  - O1  - T1  = 110.577 deg; T1  -- T1  = 5.2084 A

T1  - O3  - T2  - O3  - T1  =  59.784 deg; T1  -- T1  = 2.9460 A
T1  - O3  - T2  - O4  - T2  = 123.401 deg; T1  -- T2  = 5.3700 A
T1  - O3  - T2  - O4  - T2  = 114.564 deg; T1  -- T2  = 5.1316 A
T1  - O3  - T2  - O4  - T2  = 123.401 deg; T1  -- T2  = 5.3700 A
T1  - O3  - T2  - O4  - T2  = 114.564 deg; T1  -- T2  = 5.1316 A
T2  - O4  - T2  - O4  - T2  = 111.931 deg; T2  -- T2  = 5.2084 A

        T-T-T SUMMARY
          Range  = 59.7841 deg <--> 127.9575 deg
          Mean   = 107.5291 deg
          StdDev = 22.4629 deg

        T--T SUMMARY
          Range  = 2.9460 A <--> 5.5037 A
          Mean   = 4.8466 A
          StdDev = 0.8801 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 160.504 deg ; T1  -- T1   3.1680 A

T1  -- O2  -- T1  = 129.834 deg ; T1  -- T1   2.9460 A

T1  -- O3  -- T2  = 130.824 deg ; T1  -- T2   2.9556 A

T2  -- O4  -- T2  = 150.281 deg ; T2  -- T2   3.1425 A


        T-O-T SUMMARY
          Range  = 129.8337° <--> 160.5042 deg
          Mean   = 141.8006 deg
          StdDev = 13.7456 deg

        T--T SUMMARY
          Range  = 2.9460 A <--> 3.1680 A
          Mean   = 3.0403 A
          StdDev = 0.1046 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 31 48 72 102 133 164 190 236 293 345 408 453 489
TD10 = 775
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 34 49 66 101 136 164 202 238 276 344 406 452 514
TD10 = 787
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

<TD10> = 779.000
Average ring size = 5.2500