Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_107_2_6_k6ORAs.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 15.88 T-atoms per nm^3
Material density = 1.584 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6195 Angstrom
T1  -- O1  = 1.6189 Angstrom
T1  -- O2  = 1.6250 Angstrom
T1  -- O3  = 1.6375 Angstrom
      mean = 1.6252 Angstrom
        t1 = 0.012045  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009943  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6283 Angstrom
T2  -- O4  = 1.6228 Angstrom
T2  -- O4  = 1.6305 Angstrom
T2  -- O5  = 1.6347 Angstrom
      mean = 1.6291 Angstrom
        t1 = 0.020012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010796  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6189 A <--> 1.6375 A
          Mean   = 1.6271 A
          StdDev = 0.0064 A

       t1 Range  = 0.0120 <-- 0.0160 --> 0.0200
       t2 Range  = 0.0099 <-- 0.0104 --> 0.0108

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O1  = 110.009 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 107.537 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 110.935 deg; O2  -- O3  = 3 A
O1  -- T1  -- O2  = 109.403 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.804 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.107 deg; O2  -- O3  = 3 A
       107.537 deg <-- 109.466 deg --> 110.935 deg

O3  -- T2  -- O4  = 105.274 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 110.298 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 113.538 deg; O3  -- O5  = 3 A
O4  -- T2  -- O4  = 110.106 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 108.670 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 108.878 deg; O4  -- O5  = 3 A
       105.274 deg <-- 109.461 deg --> 113.538 deg

        O-T-O SUMMARY
          Range  = 105.2736 deg <--> 113.5383 deg
          Mean   = 109.4633 deg
          StdDev = 1.8904 deg

        O--O SUMMARY
          Range  = 2.5840 A <--> 2.7295 A
          Mean   = 2.6567 A
          StdDev = 0.0337 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O1  - T1  = 114.656 deg; T1  -- T1  = 5.1321 A
T1  - O2  - T1  - O2  - T1  = 114.656 deg; T1  -- T1  = 5.1321 A
T1  - O2  - T1  - O3  - T2  = 133.531 deg; T1  -- T2  = 5.5019 A
T1  - O1  - T1  - O2  - T1  = 107.689 deg; T1  -- T1  = 4.8279 A
T1  - O1  - T1  - O3  - T2  = 102.582 deg; T1  -- T2  = 4.5810 A
T1  - O2  - T1  - O3  - T2  =  76.433 deg; T1  -- T2  = 3.6323 A

T1  - O3  - T2  - O4  - T2  =  77.188 deg; T1  -- T2  = 3.6323 A
T1  - O3  - T2  - O4  - T2  = 163.708 deg; T1  -- T2  = 5.5831 A
T1  - O3  - T2  - O5  - T2  = 103.767 deg; T1  -- T2  = 4.5810 A
T2  - O4  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.0340 A
T2  - O4  - T2  - O5  - T2  = 110.261 deg; T2  -- T2  = 4.8279 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.0340 A

        T-T-T SUMMARY
          Range  = 76.4326 deg <--> 163.7083 deg
          Mean   = 107.0394 deg
          StdDev = 23.2971 deg

        T--T SUMMARY
          Range  = 3.6323 A <--> 5.5831 A
          Mean   = 4.6250 A
          StdDev = 0.6444 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.262 deg ; T1  -- T1   3.1065 A

T1  -- O2  -- T1  = 134.288 deg ; T1  -- T1   2.9897 A

T1  -- O3  -- T2  = 123.750 deg ; T1  -- T2   2.8802 A

T2  -- O4  -- T2  = 129.479 deg ; T2  -- T2   2.9422 A

T2  -- O5  -- T2  = 115.150 deg ; T2  -- T2   2.7598 A


        T-O-T SUMMARY
          Range  = 115.1497° <--> 147.2619 deg
          Mean   = 129.9857 deg
          StdDev = 10.8030 deg

        T--T SUMMARY
          Range  = 2.7598 A <--> 3.1065 A
          Mean   = 2.9357 A
          StdDev = 0.1158 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7598 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 28 38 53 74 100 126 149 174 209 253 296 335 372
TD10 = 602
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.16
Weight = 29

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 14 25 39 52 66 87 117 152 184 207 232 276 334 389
TD10 = 565
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.16.20_{2}
Weight = 49

<TD10> = 583.500
Average ring size = 5.8427