Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_106_2_9091_xBgVH1.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.78 T-atoms per nm^3
Material density = 2.273 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6136 Angstrom
T1  -- O2  = 1.6306 Angstrom
T1  -- O3  = 1.6729 Angstrom
T1  -- O1  = 1.6143 Angstrom
      mean = 1.6329 Angstrom
        t1 = 0.044407  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027612  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6658 Angstrom
T2  -- O3  = 1.6722 Angstrom
T2  -- O4  = 1.6192 Angstrom
T2  -- O4  = 1.6187 Angstrom
      mean = 1.6440 Angstrom
        t1 = 0.047711  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033028  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6136 A <--> 1.6729 A
          Mean   = 1.6384 A
          StdDev = 0.0254 A

       t1 Range  = 0.0444 <-- 0.0461 --> 0.0477
       t2 Range  = 0.0276 <-- 0.0303 --> 0.0330

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 104.365 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.332 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 113.553 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 122.063 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 104.458 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 106.373 deg; O3  -- O1  = 3 A
       104.365 deg <-- 109.524 deg --> 122.063 deg

O2  -- T2  -- O3  = 122.390 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 104.646 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 104.574 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 106.225 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 106.214 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 113.015 deg; O4  -- O4  = 3 A
       104.574 deg <-- 109.511 deg --> 122.390 deg

        O-T-O SUMMARY
          Range  = 104.3650 deg <--> 122.3902 deg
          Mean   = 109.5174 deg
          StdDev = 6.4479 deg

        O--O SUMMARY
          Range  = 2.5628 A <--> 2.9250 A
          Mean   = 2.6725 A
          StdDev = 0.1137 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  80.426 deg; T1  -- T2  = 4.0604 A
T1  - O1  - T1  - O3  - T2  = 105.194 deg; T1  -- T2  = 4.6287 A
T1  - O1  - T1  - O1  - T1  = 125.168 deg; T1  -- T1  = 5.4006 A
T2  - O2  - T1  - O3  - T2  = 166.274 deg; T2  -- T2  = 5.9812 A
T2  - O2  - T1  - O1  - T1  =  80.503 deg; T2  -- T1  = 4.0636 A
T2  - O3  - T1  - O1  - T1  = 105.286 deg; T2  -- T1  = 4.6316 A

T1  - O2  - T2  - O3  - T2  =  83.296 deg; T1  -- T2  = 4.0636 A
T1  - O2  - T2  - O4  - T1  = 145.899 deg; T1  -- T1  = 5.7609 A
T1  - O2  - T2  - O4  - T2  =  83.214 deg; T1  -- T2  = 4.0604 A
T2  - O3  - T2  - O4  - T1  = 105.596 deg; T2  -- T1  = 4.4912 A
T2  - O3  - T2  - O4  - T2  = 141.892 deg; T2  -- T2  = 5.4006 A
T1  - O4  - T2  - O4  - T2  = 105.498 deg; T1  -- T2  = 4.4883 A

        T-T-T SUMMARY
          Range  = 80.4256 deg <--> 166.2743 deg
          Mean   = 110.6872 deg
          StdDev = 27.4646 deg

        T--T SUMMARY
          Range  = 4.0604 A <--> 5.9812 A
          Mean   = 4.7526 A
          StdDev = 0.6769 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.910 deg ; T1  -- T1   3.0420 A

T1  -- O2  -- T2  = 159.281 deg ; T1  -- T2   3.2426 A

T1  -- O3  -- T2  = 112.503 deg ; T1  -- T2   2.7814 A

T2  -- O4  -- T2  = 123.843 deg ; T2  -- T2   2.8568 A


        T-O-T SUMMARY
          Range  = 112.5031° <--> 159.2805 deg
          Mean   = 134.1341 deg
          StdDev = 17.9755 deg

        T--T SUMMARY
          Range  = 2.7814 A <--> 3.2426 A
          Mean   = 2.9807 A
          StdDev = 0.1813 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7814 Angstrom
T2  -- T1  = 2.7814 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 60 89 121 157 199 247 299 355 417 485 557 633
TD10 = 946
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{48}
Weight = 39

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 60 89 121 157 199 247 299 355 417 485 557 633
TD10 = 946
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{48}
Weight = 39

<TD10> = 946.000
Average ring size = 10.6000